Fabrication of La2O3-TiO2-SiO2 System Glass Derived from a Sol-Gel Process

  • Published : 2007.03.31
Download PDF
⟨ Previous Next ⟩

Abstract

$La_{2}O_{3}-TiO_{2}-SiO_{2}$ glass, a type that could not obtained so far by the conventional melting method, was prepared successfully using a sol gel process. Glass derived with the sol-gel process has compositions of $5La_{2}O_{3}-5TiO_{2}-90SiO_{2},\;5La_{2}O_{3}-10TiO_{2}-85SiO_{2}$, and $5La_{2}O_{3}-20TiO_{2}75SiO_{2}$. The UV-visible absorption edge of all glass compositions was below 400 nm. The measured density is in the range of 2.55-2.89, and was nearly identical to the calculated density and the refractive index of the glasses derived from the sol-gel ranges from 1.545 to 1.645. The molar additive coefficient of $TiO_{2}$ measured in this ternary system is lower than the calculated value, while the value of $La_{2}O_{3}$ is higher.

Keywords

References

  1. I. Yasui and H. Kawazoe eds, 'High Performance Glasses,' Materials Technology 14; University of Tokyo Press, 1985
  2. S.-I. Hirota and T. Izumitani, 'Influence of Oscillator Strength on the Refractive Index,' J. Ceram. Soc. Jpn., 84 435-38 (1974)
  3. M. Iwasaki, S. Shibata, and M. Yamane, Ceramic Transactions, 30 327 (1993)
  4. S. Sakka ed., Science and Technology of Sol-Gel Process; Agune-Shofusha, 1988
  5. S. Sakka, The Chemical Society of Japan, 88 243-52 (1988)
  6. H. Dislich, 'New Routes to Multicomponent Oxide Glasses,' Angew. Chem. Int. Ed. Engl., 10 363-70 (1971) https://doi.org/10.1002/anie.197103631
  7. S. Akahoshi and K. Kimura eds, Encyclopedia of Chemical Experiments; Kodansha, p. 938 (1973)
  8. S. Sakka et al. eds, Glass Handbook; p. 617, Asakura Shoten, 1975
  9. A. A. Apen, The Chemistry of Glass; Nisso-Tsushinsha, Wakayama, 1974
  10. Y. Yamamoto, K. Kamiya, and S. Sakka, 'Study on the Properties of Coating Films Prepared from Metal Alkoxides,' J. Ceram. Soc. Jpn., 90 328-33 (1982)
  11. M. Yamane and S. Okano, 'Low Temperature Synthesis of a Monolithic Silica Glass,' J. Ceram. Soc. Jpn., 87 434-38 (1979) https://doi.org/10.2109/jcersj1950.87.1008_434
  12. S. Satoh, K. Susa, and I. Matsuyama, 'Sol-Gel-Derived Binary Silica Glasses with High Refractive Index,' J. Noncryst. Solids, 146 121-28 (1992) https://doi.org/10.1016/S0022-3093(05)80483-1