Journal of Adhesion and Interface (접착 및 계면)

The Society of Adhesion and Interface, Korea (한국접착및계면학회)
권호 표지

Thermal Stability of Glass Powder and Rubber-Filled Phenolic Resins and Dynamic Mechanical Properties of Glass Braid/Phenolic Composites

유리분말 및 고무 충진 페놀수지의 열안정성 및 Glass Braid/페놀수지 복합재료의 동역학적 열특성

  • Yoon, Sung Bong (Department of Polymer Science and Engineering, Kumoh National Institute of Technology) ;
  • Cho, Donghwan (Department of Polymer Science and Engineering, Kumoh National Institute of Technology) ;
  • Lee, Geon-Woong (Korea Electrotechnology Research Institute)
  • 윤성봉 (금오공과대학교 고분자공학과) ;
  • 조동환 (금오공과대학교 고분자공학과) ;
  • 이건웅 (한국전기연구원)
  • Received : 2007.12.05
  • Accepted : 2007.12.12
  • Published : 2007.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

In the present study, the effect of milled glass powder and liquid-type nitrile rubber (NBR) on the thermal stability of phenolic resin and the dynamic mechanical properties of glass braid/phenolic composites has been investigated by means of thermogravimetric analysis and dynamical mechanical analysis. It was found that both milled glass power and NBR filled in the waterborne phenolic resin significantly influenced the thermal stability of phenolic resins and the storage modulus and tan delta of the composites. The presence of glass powder increased the thermal stability of the phenolic resin, whereas the presence of NBR resulted in the weight loss in the specific temperature range. The thermal stability of the phenolic resins without and with the fillers was dependent not only on the cure temperature but also on the cure time. The variation of the storage modulus and tan ${\delta}$ of strip-type glass braid/phenolic composites was also influenced with the introduction of glass powder and NBR to the phenolic matrix as well as by the cure conditions given.

본 연구에서는 페놀수지의 열안정성 그리고 glass braid/페놀수지 복합재료의 동역학적 열특성에 미치는 유리분말 및 액상 니트릴고무(NBR)의 영향을 열중량분석기와 동역학적 열분석기를 이용하여 조사하였다. 수용성 페놀수지에 충진된 유리분말과 NBR은 페놀수지의 열안정성과 복합재료의 저장탄성률 그리고 tan ${\delta}$ 변화에 중요한 영향을 미쳤다. 유리분말의 충진은 페놀수지의 열안정성을 향상시키는 반면, NBR의 존재는 특정 온도영역에서 페놀수지의 중량감소를 초래하였다. 충진제의 유 무에 따른 페놀수지의 열안정성은 경화온도뿐만 아니라 경화시간에도 의존하였다. 스트립형태의 glass braid/페놀수지 복합재료의 저장탄성률과 tan ${\delta}$의 변화는 유리분말과 NBR이 혼합된 매트릭스의 도입과 경화조건에 의해 크게 영향을 받았다.

Keywords