Influence of Initial States of Test Sheets on Adhesion of NR/NR, BR/BR, and NR/BR

시험편의 초기 상태가 NR/NR, BR/BR, 그리고 NR/BR 접착에 미치는 영향

  • Published : 2007.06.30

Abstract

Adhesion of NR and BR composites with different initial states of precured or uncured conditions was studied. Adhesion between the NR and BR sheets as well as adhesion between the same rubber sheets was investigated. Adhesion forces of the uncured/uncured specimens were larger than those of the cured/uncured and cured/cured ones. The cured/cured samples and uncured NR/cured BR specimen were fully peeled out by the peel test. When one sheet was broken during the peel test, the sheet having the higher crosslink density was broken irrespective of the rubber types. Adhesion forces of the same rubber sheets were higher than those of the different ones and adhesion force of the cured NR/uncured BR sample was higher than that of the uncured NR/cured BR one. The experimental results were explained with the crosslink density and interdiffusion of rubber chains.

초기 상태를 선가황 혹은 미가황으로 다르게 한 NR과 BR 복합체 간의 접착에 대해 연구하였다. 동일한 고무인 NR/NR과 BR/BR 간의 접착뿐 아니라 이종 고무 간의 접착인 NR/BR의 접착도 조사하였다. 미가황 시트 간의 접착력이 선가황/미가황 시험편과 선가황/선가황 시험 편보다 우수하였다. 선가황/선가황 시험편과 미가황 NR/선가황 BR시험편은 완전 박리가 일어났다. 박리 시험 중 파단이 일어난 경우, 고무의 종류에 상관없이 두 개의 시트 중에 가교밀도가 높은 곳에서 끊어졌다. 이종 고무 간의 접착력보다는 동종 간의 접착력이 더 우수하였으며, 선가황 NR/미가황 BR의 접착력이 미가황 NR/선가황 BR의 경우보다 더 컸다. 실험 결과는 가교밀도와 고무 사슬의 계면간 확산으로 설명하였다.

Keywords

References

  1. F. Ruch, M. O. David, and M. F. Vallat, 'Adhesion in EPDM joints: Role of the interdiffusion mechanism on interfacial co-crosslinking', J. Polym. Sci. B: Polym. Phys., 38, 3189 (2000) https://doi.org/10.1002/1099-0488(20001201)38:23<3189::AID-POLB190>3.0.CO;2-5
  2. A. L. G. Saad and S. El-Sabbagh, 'Compatibility studies on some polymer blend systems by electrical and mechanical techniques', J. Appl. Polym. Sci., 79, 60 (2001) https://doi.org/10.1002/1097-4628(20010103)79:1<60::AID-APP70>3.0.CO;2-L
  3. A. N. Gent, 'The role of chemical bonding in the adhesion of elastomers', Int. J. Adhesion Adhesives, 1, 145 (1980)
  4. N. J. Morrison and M. Porter, 'Temperature effects on the stability of intermediates and crosslinks in sulfur vulcanization', Rubber Chem. Technol., 57, 63 (1984) https://doi.org/10.5254/1.3536002
  5. S.-S. Choi, 'Cure characteristics of carbon blackfilled rubber compounds composed of NR, SBR, and BR', Elastomer, 35, 215 (2000)