Abstract
Dielectric layer of phosphate glass for plasma display panel (PDP) device made by silk screen printing on soda-lime glass. For regulate thermal expansion coefficient (CTE) of between substrate glass and dielectric layer use addition of $Al_2O_3$ and $TiO_2$. The crystallization process of glass-ceramics for dielectric layer have been examined by DTA, XRD some of optical, electrical properties of the dielectric layer were evaluated by UV-spectrometer, dilatometer, impedance analyser. The principal crystalline phase was identified as zinc metaphosphate [$Zn(PO_3)_2$] and zinc pyrophosphate [$Zn_2P_2O_7$]. Reflectance and dielectric constance increased with the addition of $TiO_2$ filler, dielectric constant lower the out side reflectance unchanging of the adding of $Al_2O_3$ filler. Besides CTE was at about $62{\times}10^{-7}/^{\circ}C$.
인산염계 유리를 사용하여 PDP 소자의 하판유전체 후막을 제작하였다. 유전체 후막의 제조는 soda-lime glass위에 silk screen printing 법을 사용하였다. 기판과 유전체후막의 열팽창계수를 맞추기 위하여 $TiO_2$와 $Al_2O_3$를 충진제로 사용하였다. 유전체의 결정화 거동은 DTA, XRD를 사용하였으며 광학적 열적 전기적인 특성을 알아보기 위하여 UV-spectrometer, Dilatometer, Impedance Analyser를 사용하였다. 실험결과 주 결정상은 메타인산아연과 피로인산아연으로 나타났다. $TiO_2$의 첨가로 인하여 반사율은 높아졌으나 상대적으로 유전상수는 높아졌다. 또한 $Al_2O_3$를 첨가한 경우 반사율은 크게 변화가 없었으나 유전상수 값은 낮아졌다. 또한 열팽창 계수는 약 $62{\times}10^{-7}/^{\circ}C$ 정도였다.