A study on the luminescence characterization of red long persistent phosphors by the $B_2O_3$ addition

$B_2O_3$ 첨가에 의한 적색 축광성 형광체의 발광특성에 관한 연구

  • Hwang, Ku-Hyeon (Department of Gemological Engineering, Dongshin University) ;
  • Choi, Jong-Koen (Department of Gemological Engineering, Dongshin University)
  • 황구현 (동신대학교 보석공학과) ;
  • 최종건 (동신대학교 보석공학과)
  • Published : 2008.02.29
Download PDF
⟨ Previous Next ⟩

Abstract

Red long persistent phosphors of $CaZrO_3$ : Pr was synthesized by a solid reaction method. $CaCO_3\;and\;ZrO_2$ were used as hosting materials and Pr was doped as luminescence center element, and $B_2O_3$ was used as flux. The XRD pattern confirmed crystalline phase of the phosphor, and photoluminescence investigation showed emission spectrum at $480{\sim}570nm\;and\;590{\sim}700nm$. Phosphor samples were synthesized with $B_2O_3$ flux concentration of 1, 5, 10%, and luminescent peak of maximum intensity at 494 nm was obtained for 1% $B_2O_3$. Luminescent peak of red color at 620 nm was of highest intensity for 10% $B_2O_3$.

[ $CaCO_3$ ]와 $ZrO_2$를 모체결정으로 하고 Pr을 부활제로, 융제로 $B_2O_3$을 사용하였으며 고상반응법으로 합성하여 $CaZrO_3$ : Pr 적색 축광성 형광체를 제조하였다. XRD 분석을 통하여 시료의 결정상을 확인하였고, PL 검사를 통하여 $480{\sim}570nm$영역과 $590{\sim}700nm$ 영역의 발광 스펙트럼을 관찰하였다. 융제로서 $B_2O_3$을 각각 1%, 5%, 10%를 첨가하여 고상반응법으로 합성하였을 때, 494 nm 에서 발광은 $B_2O_3$의 농도가 1%일 때 가장 높은 강도를 나타냈다. 적색을 나타내는 620 nm에서의 Peak는 $B_2O_3$의 농도가 10%일 때 가장 높은 강도를 나타내었다.

Keywords

References

  1. Z. Liu, Y. Liu, J. Zhang, J. Rong, L. Huang, D.S. Yuan, "Long afterglow in $Pr^{3+}$ and $Li^{+}$ co-doped $CaZrO_3$", Science Optics Communications 251 (2005) 388 https://doi.org/10.1016/j.optcom.2005.03.011
  2. W. Hoogenstraaten, J. Philips Res. Rep. 13 (1958) 515
  3. J.G. Park, "Flux effect of alkali borates on $SrAl_2O_4$ phosphor ceramics", Kanggung National University 8-9
  4. Y.Y. Choi, "Synthesis and characterization of long phosphorescent oxide phosphors activated with rare earth elements", Department of Chemical Engineering Graduate School Chonbuk National University (2004) 7
  5. R.A. Davies, M.S. Islam, A.V. Chadwick and G.E. Rush, "Cation dopant sites in the $CaZrO_3$ proton conductor: a combined EXAFS and computer simulation study", Solid State Ionics 130 (2000) 115 https://doi.org/10.1016/S0167-2738(00)00573-7
  6. Z. Liu, Y. Liu, J. Zhang, J. Rong, L. Huang and D.S. Yuan, "Long afterglow in $Pr^{3+}$ and $Li^{+}$ co-doped $CaZrO_3$", Science Optics Communications 251 (2005) 390
  7. A.P. Vink, P. Dorenbors and J.t.m.de Hass, "Photon cascade emission in $SrAlF_5$ : $Pr^{3+}$", J. Phys. Condens. Matter. 14 (2002) 8889 https://doi.org/10.1088/0953-8984/14/38/312
  8. P.A. Rodnyi, P. Dorenbos and C.B. Stryganyuk, "Emission of $Pr^{3+}$ in $SrAl_{12}O_{19}$ under vacuum ultraviolet synchrotron excitation", J. Phys Condens. Matter. 15 (2003) 719 https://doi.org/10.1088/0953-8984/15/4/311
  9. Y.Y. Choi, "Synthesis and characterization of long phosphorescent oxide phosphors activated with rare earth elements", Department of Chemical Engineering Graduate School Chonbuk National University (2004) 161