Abstract
Solid hydrated by hydro-thermal synthesis reaction is cured two times, the first curing is the steam curing at atmospheric pressure and the second one is a high-pressure steam curing, that is autoclaving. Steam curing is to acquire the proper strength for the resistance of treatment in the first curing process, it was not evaluated properly so far. Because of ignorance about curing, some engineers even think that the dry curing is better than the steam curing. The relation between compressive strength of solid hydrated by hydrothermal synthesis reaction and curing condition are presented in this paper. In order to investigate the effect of curing on the strength properties of specimen, the hydration behavior of solid hydrated by hydro-thermal synthesis reaction has been studied over curing condition using XRD, DT-TGA and porosimeter, SEM analysis technique. The results show that the specimens which are cured with blended method of dry and steam curing appear to have better strength properties than that of dry curing and steam curing. Also, there are significant difference of hydration behavior among curing condition in the solid hydrated by hydro-thermal synthesis reaction.
프리캐스트 제품은 소요의 강도를 단기간에 얻기 위하여 일반적으로 상압 증기양생을 실시하며, 칼슘-실리케이트의 수열합성반응을 이용할 경우 1차 양생 이후에 오토클레이브 양생이라는 2차 양생도 실시하고 있다. 여기에서 제품의 강도발현에 커다란 영향을 미치는 양생 방법의 경우, 2차 양생 방법에 대한 연구는 각종 연구로 부터 수열반응에 적합한 조건이 구명되는 등 많은 연구가 수행되었으나, 1차 양생 방법에 대한 검토는 아직 미비한 실정이며 생산업체별로 양생 방식을 달리하여 제품을 생산하고 있어 제품의 소요강도 획득에 문제점을 가지고 있다. 이에 본 연구에서는 수열합성 경화체에 있어서 보다 높은 강도를 얻기 위한 1차 양생 방법에 대한 자료를 얻고자 실험적 연구를 수행하였다. 즉 수열합성 경화체에 있어서 1차 양생 방법을 건식과 건/습식 그리고 습식으로 실시한 후에 각각의 시험체에 대하여 수화특성을 알아보기 위하여 SEM, XRD, DT-TGA 및 porosimeter 시험을 실시하였으며, 강도 특성을 알아보기 위하여 압축강도 시험을 실시하였다. 측정 결과, 1차, 2차 양생 후 각 양생조건에 따른 시험체의 압축강도는 건/습식 양생조건이 강도발현에 유리한 것으로 나타났으며, 그 차이는 크지 않은 것을 알 수 있었다. 수화도 분석을 위한 SEM, XRD 및 DT-TGA의 측정 결과, 건/습식 양생조건의 경우가 건식과 습식 양생조건에 비해 가장 많이 수화가 진행된 것을 알 수 있었고, porosimeter의 측정 결과에 있어서도 건/습식 양생조건이 강도특성에 유리한 공극특성을 갖는 것으로 나타났다.