Properties of Silk-Sericin Films Modified by Isocyanate Compounds

화학 개질된 실크세리신 필름의 특성

  • Published : 2008.04.27

Abstract

Polar amino groups of the waste SS(silk-sericin) were modified by two isocyanate compounds of MOI[2-(methacryloyloxy)ethyl isocyanate] and AOI [2-(acryloyloxy)ethyl isocyanate]. When the MOISS (MOI-modified silk sericin) or AOISS(AOI-modified silk sericin) was pressed hot, vinyl groups in the MOI or AOI were polymerized and then the flexible and transparent films were obtained. Tensile moduli and strengths of the MOISS films were significantly improved as the MOI contents increased. By the addition of the isocyanate compounds, silk sericin films exhibited lower solubility to the distilled water($80^{\circ}C$) and also lower swell ratio to the distilled water(room temperature). In the effect of tensile properties and restraining the water swelling, MOI was better than AOI. BOD(biochemical oxygen demand)/TOD(theoretical oxygen demand) of the pure sericin film was almost 100% perfect level after 10 days immersion into the activated sludge. With increasing isocyanate content reacted with polar amino groups, BOD/TOD decreased. When more than 50 mol% of polar amino groups remained unreacted, sericin films could retain more biodegradability. Comparing with MOI from the viewpoint of biodegradability, AOI was more effective.

Keywords

References

  1. 野村正和, 岩佐陽一,新家英正, 特許公開平 07-292241(1995)
  2. 畠山兵衛, 廣瀨重雄, 中村邦雄, 特許公開平 08-012738(1995)
  3. 浜岡容子, 小林 哲, 淺田 淰, 山崎正夫, 早川 潔, 特許公開平 11-131318(1999)
  4. 野村正和, 山田英幸, 不破順淸, セリシンの再発 見と纎維への應用, 日本纎維學會誌(纎維と工業), 57, 279-283(2001)
  5. 中川百樹, 特許公開 2002-69848(2002)
  6. 野形明廣, 山田英幸, 野村正和, 特許公開 2003- 239174(2003)
  7. Kongdee, A., Bechtold, T. and Teufel, L., Modification of Cellulose Fiber with Silk Sericin, J. Appl. Polym. Sci., 96, 1421-1428(2005) https://doi.org/10.1002/app.21576
  8. Miyake, H., Wakisaka, H. and Nagura, M., Structures and Physical Properties of Poly (vinyl alcohol)/Sericin Blended Plastic, J. Insect Biotechnol. Sericol., 71, 85-89(2002)
  9. 永田謙二, 竹內孝行, 伊藤美和, 高橋淸久, 尹興 洙, セルロ一ス/キトサンおよびセ リシン/キトサン系複合化フィルムの力學特性, 接着, 47, 257-264(2003)
  10. Nagura, M., Onishi, R., Gotoh, Y. and Ohkoshi, Y., Structures and Physical Properties of Cross- Linked Sericin Membranes, J. Insect Biotechnol. Sericol., 70, 149-153(2001)
  11. 大津晉三, 三宅肇, 脇坂博之, 特許公開 2002- 265498, 265499(2002)
  12. Miyake, H., Wakisaka, H., Yamashita, H. and Nagura, M., Moisture Characteristic and Structure of High Molecular Weight Sericin Film, Polym. J., 35, 683-687(2003) https://doi.org/10.1295/polymj.35.683
  13. Miyake H., Yamashita S., Wakisaka H., Shimizu Y., and Nagura M., Fiber Processing by High Molecular Weight Sericin and its Basic Properties, SEN'I GAKKAISHI, 60, 271-275 (2004) https://doi.org/10.2115/fiber.60.271
  14. Teramoto, H. and Miyazawa, M., Molecular Orientatio Behavior of Silk Sericin Film as Revealed by ATR Infrared Spectroscopy, Biomacromolecules, 6, 2049-2057(2005) https://doi.org/10.1021/bm0500547
  15. 栗原福次, 大石不二夫, "活用ガイド高分子材 料", オ-ム社, p.188, 1978