Effect of Titanium Surface Treatments Bond Strength and Cytotoxicity in Titanium-Porcelain System

  • Chung, In-Sung (Department of Dental Lab. Science, College of Health Sciences, Catholic University of Pusan) ;
  • Kim, Chi-Young (Department of Dental Lab. Science, College of Health Sciences, Catholic University of Pusan) ;
  • Choi, Sung-Min (Department of Dental Lab. Science, College of Health Sciences, Catholic University of Pusan)
  • 정인성 (부산가톨릭대학교 치기공학과) ;
  • ;
  • Published : 2008.06.30

Abstract

The objective of this study was to evaluate the influence of surface modifications on the bonding characteristics and cytotoxicity of specific titanium porcelain bonded to milling titanium and cast titanium. Milling titanium and cast titanium samples were divided into 8 test groups. These groups are as follow: i) sandblasted with particles of different size of $220{\mu}m\;and\;50{\mu}m$, ii) different sequences of sandblasting treatment and etching treatment, iii) etched with different etching solutions, and iv) preheated or not. The surface characteristics of specimens were characterized by the test of mean roughness of surface and SEM. The bond strength of titanium-ceramic systems was measured by using three-point bending test and SEM. The results show that the mean roughness of surface of sample sandblasted with $220{\mu}m$ aluminum oxide increased and bond strength were higher than sample sandblasted with $50{\mu}m$ aluminum oxide. The mean roughness of surface decreased, but the bond strength increased when the samples sandblasted with $220{\mu}m$ aluminum oxide were preheated. The sample sandblasted with $220{\mu}m$ aluminum oxide after oxidized with occupational corrosive agent I (50% NaOH, 10% $CuSO_4{\cdot}5H_2O$) and II (35% $HNO_3$, 5% HF) showed higher bond strength than sample oxidized with 30% $HNO_3$ after sandblasted with $220{\mu}m$ aluminum oxide. Group NaCuNF220SP (milling Ti: 35.3985 MPa, casting Ti: 37.2306 MPa) which was treated with occupational corrosive agent I (50% NaOH, 10% $CuSO_4{\cdot}5H_2O$) and II (35% $HNO_3$, 5% HF), followed by sandblasting with $220{\mu}m$ aluminum oxide and preheating at $750^{\circ}C$ for 1 hour showed the highest bond strength and significant differences (P<0.05). The method for modifying surface of titanium showed excellent stability of cells.

Keywords