Abstract
It is said that polymer modified asphalt using polyethylene as modifier would show phase separation due to density difference and incompatibility between asphalt and polyethylene. In this study, to prevent coalescence of polyethylene in asphalt, we employed peroxides as phase separation inhibitor. On microscope, peroxides (dicumyl peroxide, lauroyl peroxide) with waste vinyl (comprising low density polyethylene) did not show phase separation, however, rheometer test showed phase separation at molecular level, i.e., polyethylene and asphalt are immiscible ultimately. Mechanical properties (tensile strength, Marshall stability, dynamic stability) showed waste vinyl-modified asphalts are highly resistant to plastic deformation and these properties are even better than those of Superphalt.
아스팔트 개질재로 쓰이고 있는 폴리에틸렌은 아스팔트와의 비중차와 비상용성으로 인하여 상분리가 일어난다고 알려지고 있다. 본 연구에서는 상분리를 억제하기 위하여 폴리에틸렌을 가교시킬 수 있는 것으로 알려지고 있는 과산화물을 사용하여 상분리 억제를 시도하였다. 폴리에틸렌 수지로는 폐비닐을 사용하였으며, 과산화물로는 디큐밀퍼옥사이드와 로로일퍼옥사이드를 사용하였다. 현미경상으로는 과산화물이 첨가되어 상분리가 억제되었다. 그러나 유변물성을 측정한 결과는 아스팔트와 폴리에틸렌은(비록 폴리에틸렌이 가교된다 하더라도) 분자단위에서는 서로 섞일 수 없음을 보여주고 있다. 기계적 시험(인장강도, 마샬안정도, 동적안정도)에서는 매우 우수한 물성을 보여주어 소성변형에 대한 저항성이 크게 향상된 것으로 나타났고, 이는 기존의 슈퍼팔트보다 우수한 것으로 나타났다.