Synthesis and Characterization of Polyurethane Elastomer

Polyurethane Elastomer의 합성 및 특성

  • Received : 2009.08.17
  • Accepted : 2009.09.10
  • Published : 2009.12.30
Download PDF
⟨ Previous Next ⟩

Abstract

In this study, We were studied on the properties of polyurethane elastomer containing the polyol, chain extender and isocyanate in polyurethane elastomer. Polyurethane elastomer had the best properties with poly(tetramethylene) glycol for in-line skate wheel. With more incorporation of chain extender content in polyurethane elastomer, tensile strength and hardness increased and elongation decreased. And then properties of polyurethane elastomer with the bulky type isocyanate had better than the flexible type isocyanate.

본 연구에서는 폴리우레탄 엘라스토머 합성 시 사용되는 폴리올, 사슬 연장제, 이소시아네이트에 따른 물성 변화를 알아보았다. 폴리우레탄 엘라스토머 합성시 poly(tetramethylene) glycol을 사용하였을 경우가 인라인 스케이트 휠의 요구물성을 만족하였다. 사슬 연장제의 함량이 증가함에 따라 인장강도와 경도는 증가하였으나, 신율은 감소하는 경향을 나타내었다. 또한 방향족 이소시아네이트의 종류에 따른 평가 결과 bulky한 구조보다는 상대적으로 유연한 구조를 가지고 있는 이소시아네이트가 우수한 물성을 나타내었다.

Keywords

References

  1. Z. Wirpsza, Polyurethanes Chemistry Technology and Applications, Ellis Horwood, New York (1993).
  2. G. Oertel, Polyurethane Handbook, Hanser, Cincinnati (1994).
  3. J. Y. K. J. Seo, S. Y. Kwon, J. P. Wu, and H. S. Park, Polymer(Korea), 22, 756 (1998).
  4. C. Hepbum, Polyurethane Handbook, Elsevier Science Publishing Co., New York (1992).
  5. K. C. Frrish and S. L. Reegen, "Advances in Urethane Science and Technology" vol. 1-8, Technomic USA (1978).
  6. R. Bonart, Polymer, 20, 1389 (1979). https://doi.org/10.1016/0032-3861(79)90280-5
  7. M. J. Han, K. B. Choi, S. H. Kim, and S. H Lee, Polymer (Korea), 7(6) (1983).
  8. B. Y. Jeong, J. M. Cheon, J. S. Yoo, and J. H. Chun, Journal of Adhesion and Interface, 8(4) (2007).
  9. S. K. Kim, K. S. Kim, T. K. Kim, and G. J. Oh, Elastomer, 35, 281 (2000).
  10. A. W. McLennaghan and R. A. Petherick, Eur. Polym. J., 24 1063 (1988). https://doi.org/10.1016/0014-3057(88)90066-3
  11. Y. K. Yang, N. S. Kwak, and T. S. Hwang, Polymer (Korea), 29, 81 (2005).
  12. D. W. Kang, Y, M. Kim, and D. K. Kweon, Polymer (Korea), 22, 4 (1998).