Surface Fracture Behaviors of Unidirectional and Cross Ply Glass Fiber/Epoxy Lamina-Coated Glass Plates under a Small-Diameter Steel Ball Impact

일방향 및 직교형 유리섬유/에폭시 복합재로 피막된 판유리의 미소강구 충격에 의한 표면파괴거동

  • Published : 2009.08.31

Abstract

Fiber orientation effects on the impact surface fracture of the glass plates coated with the glass fiber/epoxy lamina layer were investigated using a small-diameter steel-ball impact experiment. Four kinds of materials were used: soda-lime glass plates, unidirectional glass fiber/epoxy layer(one ply, two plies)-coated, crossed glass tiber/epoxy layer (two plies)-coated glass plates. The maximum stress and absorbed fracture energy were measured on the back surface of glass plates during the impact. With increasing impact velocity, various surface cracks such as ring, cone, radial and lateral cracks appeared near the impacted site of glass plates. Cracks in the plate drastically diminished by glass fiber coating. The tiber orientation guided the directions of delamination and plastic deformation zones between the tiber layer and the glass plate. Impact surface-fracture indices expressed in terms of the maximum stress and absorbed energy could be used as an effective evaluation parameter of the surface resistance.

유리섬유/에폭시 복합재료로 피막한 판유리의 표변파괴거동에 대한 섬유방향효과를 미소강구 충격실험을 통해 연구했다. 본 연구에서는 단순소다유리판(soda-lime glass plates), 일방향 유리섬유/에폭시박막 (glass/epoxy lamina ply)을 1층 및 2층 접착, 직교형 유리섬유/에폭시 박막 (2층)을 접착한 4종류의 시편을 사용하였다. 유리판 배면에 스트레인게이지를 부착하여 충격중의 최대 응력과 흡수파괴에너지를 측정하였다. 피막없는 판유리의 경우 충격속도 증가에 따라 링균열, 콘균열, 레이디얼 균열이 충격표면부에서 발생하였다. 복합재료 박막으로 피막한 결과, 소다유리판의 균열은 현저히 감소하였으며 섬유층과 판유리사이의 박리 및 소성변형영역의 방향은 섬유방향으로 진행했다. 최대응력과 흡수파괴에너지를 이용하여 구한 충격 표면파괴지수는 표면저항의 효과적인 평가지수로서 사용될 수 있었다.

Keywords

References

  1. C.G. Knight, M.Y. Swain, M. M Chaudhri, Joumal of Materials Science, Vol. 12, 1977, pp. 1573-1580 https://doi.org/10.1007/BF00542808
  2. B.A. latella, Brain H. O'Conor, "Hertzian Contact Damage in Porous Alumina Ceramics," J Am. Ceram. Soc. , Vol. 80 [4], 1997, pp. 1027-1031 https://doi.org/10.1111/j.1151-2916.1997.tb02940.x
  3. J. Persson, K. Breder, D.J. Rowciffe, "Loading Rate Effects during Indentation and Impact on Glass with Small Spheres," Journal of Materials Science, Vol. 23,1993, pp. 6484-6489 https://doi.org/10.1007/BF01352218
  4. S.M. Wiederhom, B.R. Lawn, "Strenght Degradation of Resulting from Impact with Spheres," Journal of Ceramic Society, Vol. 60, No. 9-10, 1977, pp. 451-458 https://doi.org/10.1111/j.1151-2916.1977.tb15531.x
  5. S.M. Wiederhom, B.J. Hockey, "Effect of Material Parameters on the Erosion Resistance of Brittle Materials," Journal of Materials Science, Vol. 18. 1983, pp. 766-80 https://doi.org/10.1007/BF00745575
  6. M.M. Chaudhri, Patrica A. Brophy, "Single Particle Impact Damage of Fused Silica," Journal of Materials Science, Vol. 15, 1980, pp. 345-352 https://doi.org/10.1007/BF02396782
  7. M.M. Chaudhri, C.R. Kurkjian, "Impact of Small Steel Spheres on the Surfaces of Nonnal and Anomalous Glasses," J. Am. Ceram. Soc. , Vol. 69, 1986, pp. 404-410 https://doi.org/10.1111/j.1151-2916.1986.tb04769.x
  8. J.T. Hagan, "Micromechanics of Crack Nucleation during Indentations," Journal of Materials Science, Vol. 14, 1979, pp. 2975-2980 https://doi.org/10.1007/BF00611482
  9. J.T. Hagan, "Cone Cracks around Vickers Indentations in Fused Silica Glass," Journal of Materials Science, Vol. 14, 1979, pp. 462-466 https://doi.org/10.1007/BF00589840
  10. J. T. Hagan, 'Shear Defonnation under Pyramidal Indentations in Soda-Lime Glass," Journal of Materials Science, Vol. 15, 1980, pp. 1417-1424 https://doi.org/10.1007/BF00752121
  11. D.A. Shockey, D.C. Elich, K C. Dao, "Particle Impact DAmage in Silicon Nitride at 1400 $^{\circ}C$," Journal of Materials Science, Vol. 16, 1981 , pp. 477-482 https://doi.org/10.1007/BF00738639
  12. K. Zeng, K. Breder, D.J. Rowcliffe, C. Herrstorm, "Elastic Modulus Determined by Hertzian Indentation," Journal of Materials Science, Vol. 27, 1992, pp. 3789-3792 https://doi.org/10.1007/BF00545457
  13. M. Munawar, Chaudbri, Chen Hen Liangyi, "The Orientation of the Hertzian Cone Crack in Soda-Lime Glass Formed by Oblique Dynamic and Quasi-Static Loading with a Hard Sphere," Journal of Material Science, Vol. 24, 1989, pp. 3441-3448 https://doi.org/10.1007/BF02385722
  14. R.F. Cook, G.M. Pharr, "Direct Observation and Analysis of Indentation Cracking in Glasses and Ceramics," J. Am. Ceram. Soc. , Vol. 73 [4], 1990, pp. 787-817 https://doi.org/10.1111/j.1151-2916.1990.tb05119.x
  15. B.R. Lawn, F. Guiberteau, N.P. Padture, "Effect of Grain Size on Hertzian Contact Damage in Alumina," J. Am Ceram. Soc., Vol. 77, 1994, pp. 1825-31 https://doi.org/10.1111/j.1151-2916.1994.tb07057.x
  16. 서창민, 이문환, 김성호, "$Cr_2O_3$ 용사 코팅된 유리에 저속 입자 충격에너지에 따른 손상거동," 대한기계학회 1998년도 추계학술대회논문집 A, 1998, pp. 126-131
  17. 서창민, 이문환, 김성호, 이동화, "입자충격에 따른 $Al_2O_3$ - $TiO_2$ 플라스마 코팅유리의 손상체적 변화에 관한 연구," 대한기계학회 '99년도 제 2차 재료 및 파괴부문 학술대회 논문집, 1999, pp. 98-104
  18. 서창민, 신형섭, 정성묵, 황병원, "입자 충격에 의한 유리의 손상기구에 관한 실험적 연구," 대한기계학회논문집 (A), 제 20권 제 6호, 1996, pp. 1903-1912
  19. F.W. Flocker, L.R. Dharani, "Modeling Fracture in Laminated Architectural Glass subject to Low Velocity Impact," Journal of Materials Science, Vol. 32, 1997, pp. 2587-2594 https://doi.org/10.1023/A:1018698900942
  20. 김형구, 최낙삼, "직물형 유리섬유/에폭시 복합재료로 피막된 판유리의 미소강구 충격에 의한 표면 파괴거동," 한국 복합재료학회지, 제13 권 4호, 2000, pp. 75-82
  21. H.G. Kim, N.S. Choi, N.Cho, "Evaluation of the impactivesurface- fracture behavior of giass plates using a back-surface strain measurement," Journal of Materials Research, Vol. 16 (11), 2001, pp. 3042-3045 https://doi.org/10.1557/JMR.2001.0419
  22. R. Olsson, "Mass criterion for wave controlled impact response of composite plates," Composites, Part A 32, 2000, pp. 879-887 https://doi.org/10.1016/S1359-835X(00)00020-8