Abstract
On adsorbing carbon monoxide (CO) on the silica supported ruthenium/iron alloy ($Ru/Fe-SiO_2$) samples above mole ratio 9/1 of Ru/Fe five bands ($2138.7{\sim}2142.5cm^{-1}$, $2067.3{\sim}2073.1cm^{-1}$, $1976.7{\sim}2017.2cm^{-1}$, $1737.9{\sim}1799.3cm^{-1}$, $1625.7cm^{-1}$) were observed, and in $Ru/Fe-SiO_2$ samples below mole ratio 8/2 of Ru/Fe two bands ($1934.0{\sim}1990.2cm^{-1}$, $1625.7cm^{-1}$) were observed. The $2138.7{\sim}2142.5cm^{-1}$ bands, the $2067.3{\sim}2073.1cm^{-1}$ bands, and the $1988.3{\sim}2030.7cm^{-1}$ bands may be ascribed to stretching vibrations of CO molecules lineally bonded to the Ru atoms on supported Ru/Fe cluster surface, the $1737.9{\sim}1799.3cm^{-1}$ bands to stretching vibrations of CO molecules bridge bonded to the Ru atoms on supported Ru/Fe cluster surface or to stretching vibrations of CO molecules bonded to the Ru atoms on high Miller index planes, and the $1934.0{\sim}1990.2cm^{-1}$ bands to stretching vibrations of CO molecules lineally bonded to the Fe atoms on supported Ru/Fe cluster surface. The absorbances of the $1934.0{\sim}1990.2cm^{-1}$ bands in $Ru/Fe-SiO_2$ samples gradually increased with the increases of Ru/Fe mole ratio below the ratio of 8/2. This phenomena may be ascribed to the increases of Fe concentration of surface compared with the one of the sample and to the increases of surface area of supported Ru/Fe cluster according as increase of Ru/Fe mole ratio below the ratio of 8/2 compared with the $Fe-SiO_2$ sample.
실리카 지지 루테늄과 철의 합금($Ru/Fe-SiO_2$) 시료에 일산화탄소(CO)를 흡착시켰을 때 Ru/Fe의 몰비 9/1 이상에서 다섯 적외선 흡수띠($2138.7{\sim}2142.5cm^{-1}$, $2067.3{\sim}2073.1cm^{-1}$, $1976.7{\sim}2017.2cm^{-1}$, $1737.9{\sim}1799.3cm^{-1}$, $1625.7cm^{-1}$)를 관찰했고, Ru/Fe의 몰비 8/2 이하에서 두 적외선 흡수띠($1934.0{\sim}1990.2cm^{-1}$, $1625.7cm^{-1}$)를 관찰했다. $2138.7{\sim}2142.5cm^{-1}$ 흡수띠, $2067.3{\sim}2073.1cm^{-1}$ 흡수띠, $1976.7{\sim}2017.2cm^{-1}$흡수띠는 Ru/Fe 뭉치 표면의 Ru 원자에 선형결합한 CO의 신축진동에 의한 것으로, $1774.2{\sim}1799.3cm^{-1}$ 흡수띠는 Ru/Fe 뭉치 표면의 Ru 원자와 다리결합하거나 높은 지수 평면에 있는 Ru 원자에 결합한 CO의 신축진동에 의한 것으로, $1934.0{\sim}1990.2cm^{-1}$ 흡수띠는 Ru/Fe 뭉치 표면의 Fe 원자에 선형결합한 CO의 신축진동에 의한 것으로 제시할 수 있다. $Ru/Fe-SiO_2$에서 CO를 흡착시켰을 때 Ru/Fe 몰비가 8/2 이하에서 증가할 때 CO가 Fe에 선형결합하여 생긴 $1934.0{\sim}1990.2cm^{-1}$ 흡수띠의 흡광도가 증가하였는데, 이 현상은 Ru/Fe 몰비가 8/2 이하에서 증가할 때 Ru/Fe 뭉치 표면에서 시료의 함량과 비교하여 Fe 농도가 증가했고 $Fe-SiO_2$ 시료와 비교하여 표면적이 Ru/Fe 몰비의 증가에 따라 점차 증가했기 때문으로 설명할 수 있다.