Abstract
Steel structures have a higher probability of being damaged by fatigue than by other causes of deterioration. As such, their maintenance to prevent fatigue damage is essential to sustain their safety and performance during their service period. In their maintenance, the current state of their fatigue cracks must be assessed to determine appropriate reinforcement methods and the suitable time intervals of periodic inspections when fatigue cracks are detected. Determining the crack growth rate is a successful method of predicting fractures, but it requires technical knowledge on fracture mechanics and experience in numerical methods and software for finite element analysis. In this study, a fatigue crack growth test on through-thickness cracked steel plates was conducted to assess the crack growth rate without superior technical knowledge and experience. The relationship between the Crack Opening Displacement (COD) and the crack growth rate was found in relatively long fatigue cracks.
강구조물의 점검시 피로균열이 발견되는 경우에는 보수 보강 시행의 결정과 구조물의 점검주기 결정을 위한 균열의 현재 상태평가와 앞으로의 균열진행 정도에 대한 정량적인 예측이 요구된다. 피로균열에 대한 손상도 평가는 파괴역학 파라미터를 이용한 균열진전속도와 취성파단의 여부 결정이 대표적인 방법으로 파괴역학에 관한 전문적인 지식과 함께 수치해석 프로그램의 활용능력이 필요하다. 이에, 본 연구에서는 피로손상도 평가 방법에 관한 다양성을 확보하고, 파괴역학에 대한 전문적인 지식이 없는 기술자가 피로균열에 의한 강구조물의 손상도를 간편하게 평가 할 수 있는 방법을 개발하기 위한 첫 단계로, 관통균열 시험편을 이용한 균열진전시험을 실시하였다. 그리고 피로균열 표면으로부터 측정된 COD(Crack Opening Displacement)의 크기와 측정위치를 이용하여, 균열진전속도를 추정하기 위한 파라미터를 도출하고, 그 타당성을 분석하였다. 그리고 관통균열이 있는 시험편의 형상, 응력범위, 그리고 응력비에 상관없이 COD를 이용하여 피로균열진전속도를 추정할 수 있는 방법을 제시하였다.