Abstract
The purpose of this study was to evaluate the material characteristics of SHN400 steel, which is suitable as a steel material for building structures, using the experimental approach. For this purpose, the chemical composition test, tensile test, macro test, micro test, and charpy notch impact test were conducted with specimens taken from the highest, thickest, and commonly used H-beams for girder or beam members. Each test was conducted under the Korean Standard(KS) test conditions. All the test results satisfied the requirements of KS (KS D 3866) and the steel material for seismic design. The carbon equivalent value (Ceq), which is related to weldability, and the yield ratio, which is related to inelastic behavior, showed especially good results. Thus, SHN400 is definitely suitable as the steel material for building structures.
본 연구의 목적은 시험적 방법을 통해 SHN400 강재의 소재 특성이 건축구조용 강재로 적합한지를 평가하는 것이다. 이를 위해 국내에서 생산되는 열간 압연 H형강 중 최대 춤 및 최대 플랜지 두께의 H형강과 SHN400 강종의 주요 사용처가 될 보부재로 수요가 많은 H형강 규격을 대상으로 화학성분 평가, 인장강도, 매크로, 미크로 및 샤르피 충격 시험을 실시하였다. 각 시험은 관련 KS 규격에서 요구하는 시험 조건하에서 수행되었으며, 시험 결과 화학성분 및 기계적 특성과 관련된 모든 시험에서 SHN400 강종은 KS 규격(KS D 3866)의 요구 조건과 내진설계시 강재에 요구되는 조건들을 만족하는 것으로 나타났다. 특히 용접성과 관련된 탄소당량(Ceq)과 비탄성 변형능력과 관련된 항복비의 경우 KS 규격을 상회하는 결과를 나타내었다. 따라서 SHN400 강재는 소재 특성 측면에서 건축구조용 강재에 적합한 것으로 판단된다.