Emulsion Grafting of Glycidyl Methacrylate onto Plasma-treated Polypropylene Surface

플라즈마 처리된 폴리프로필렌 표면 위에 글리시딜메타크릴레이트의 에멀젼 그래프팅

  • Ji, Han-Sol (Department of Chemical Engineering, Chungnam National University) ;
  • Liu, Xuyan (Department of Chemical Engineering, Chungnam National University) ;
  • Choi, Ho-Suk (Department of Chemical Engineering, Chungnam National University) ;
  • Kim, Jae-Ha (Bioneer Co.) ;
  • Park, Han-Oh (Bioneer Co.)
  • 지한솔 (충남대학교 공과대학 화학공학과) ;
  • 류욱연 (충남대학교 공과대학 화학공학과) ;
  • 최호석 (충남대학교 공과대학 화학공학과) ;
  • 김재하 ((주)바이오니아) ;
  • 박한오 ((주)바이오니아)
  • Received : 2011.06.22
  • Accepted : 2011.08.10
  • Published : 2012.01.25
Download PDF
⟨ Previous Next ⟩

Abstract

Glycidyl methacrylate (GMA) was used to introduce epoxy groups on the surface of polypropylene (PP) plate, used as a substrate, through plasma-induced graft copolymerization. Emulsion polymerization was applied for graft copolymerization of GMA and was compared with conventional solution polymerization to confirm its effect. Plasma treatment conditions under one atmospheric pressure were fixed as follows; the RF power of 200 W, the treatment time of 30 sec, the Ar gas flow rate of 6 LPM, and the exposure time of treated PP samples in air of 5 min. For graft-copolymerization, GMA concentration, reaction temperature, and reaction time was optimized to maximize the grafting degree of GMA. The maximum grafting degree of GMA was obtained at the condition of 12%-GMA concentration, $90^{\circ}C$ reaction temperature, and 5 hr-reaction time. Analysis results supported that the emulsion polymerization was more effective than the solution polymerization for grafting more GMAs on the surface of PP plate under the same reaction conditions.

글리시딜메타크릴레이트(GMA)의 플라즈마 유도 그래프트 공중합을 통해 기재로 사용한 평판형 폴리프로필렌 위에 에폭시 그룹을 도입하였다. 그래프트 공중합은 에멀젼 공중합법을 적용하였고, 기존의 용액 공중합과 비교하여 그 효과를 확인하고자 하였다. 대기압 플라즈마 처리 조건은 RF power 200 W, 처리시간 30초, Ar 기체 유속 6 LPM으로 고정하였고, 처리 후의 대기 중 노출시간 역시 5분으로 고정하였다. 중합반응에서는 GMA의 농도, 반응온도, 반응시간에 따라 표면 그래프트도의 변화를 최적화하였다. 그 결과, GMA 농도 12%, 반응온도 $90^{\circ}C$, 반응시간 5시간으로 중합하였을 때 가장 높은 그래프트도를 나타내었다. 분석 결과, 같은 반응조건 하에서 에멀젼 중합이 용액 중합에 비하여 더 많은 에폭시 그롭 도입에 효과적임을 확인하였다.

Keywords

Acknowledgement

Supported by : (주)바이오니아

References

  1. M. Zeniewicz, J. Adhes. Sci. Technol., 15, 1769 (2001). https://doi.org/10.1163/15685610152715773
  2. G. Xu and S. Lin, Macromol. Sci. Rev. Macromol. Chem. Phys., 34, 555 (1994). https://doi.org/10.1080/15321799408014167
  3. C. M. Chen, Reac. Func. Polym., 68, 1307 (2008). https://doi.org/10.1016/j.reactfunctpolym.2008.06.008
  4. C. Tyagi, L. Kumar, and H. Singh, J. Appl. Polym., 111, 1381 (2009). https://doi.org/10.1002/app.28933
  5. N. Seko, N. T. Y. Ninh, and M. Tamada, Radiat. Phys. Chem., 79, 22 (2010). https://doi.org/10.1016/j.radphyschem.2009.08.014
  6. T. Hirotsu, Thin Solid Films, 506, 173 (2006). https://doi.org/10.1016/j.tsf.2005.08.209
  7. K. J. Kitching, P. Vicky, and B. D. Ratner, Plasma Polymer Films, Imperial College Press, Singapore, 2004.
  8. P. Favia, L. D. Tomaso, E. Sardella, F. Palumbo, V. Colaprico, and R.d'Agostino, Proceedings of Vol. VI, ISPC-15, VI, p. 2367.
  9. N. Gomathi and S. Neogi, Appl. Surf. Sci., 255, 7590 (2009). https://doi.org/10.1016/j.apsusc.2009.04.034
  10. J. S. Jung, S. W. Myung, and H. S. Choi, Korean J. Chem. Eng., 25, 1190 (2008). https://doi.org/10.1007/s11814-008-0196-x
  11. V. A. Titov, T. G. Shikova, V. V. Rybkin, D. S. Smirnov, T. A. Ageeva, and H. S. Choi, High Temp. Mat. Pr., 10, 467 (2006). https://doi.org/10.1615/HighTempMatProc.v10.i3.100
  12. H. S. Choi, V. V. Rybkin, V. A. Titov, T. G. Shikova, and T. A. Ageeva, Surf. Coat. Tech., 200, 4479 (2006). https://doi.org/10.1016/j.surfcoat.2005.03.037
  13. O. J. Kwon, S. Tang, S. W. Myung, N. Lu, and H. S. Choi, Surf. Coat. Tech., 192, 1 (2005). https://doi.org/10.1016/j.surfcoat.2004.09.018
  14. P. le Thuaut, B. Martel, G. Crini, U. Maschke, X. Coqueret, and M. Morcellet, J. Appl. Polym. Sci., 77, 2118 (2000). https://doi.org/10.1002/1097-4628(20000906)77:10<2118::AID-APP4>3.0.CO;2-Y
  15. T. Hirotsu, Thin Solid Films, 506, 173 (2006). https://doi.org/10.1016/j.tsf.2005.08.209
  16. N. Seko, L. T. Bang, and M. Tamada, Materials and Atoms, 265, 146 (2007).
  17. V. N. Kudrysvtsev, V. Y. Kabanov, N. A. Yanul, and S. A. Kedik, High. Energ. Chem., 37, 382 (2003). https://doi.org/10.1023/B:HIEC.0000003396.56980.1d
  18. M. Zeniewicz, J. Adhes. Sci. Technol., 15, 1769 (2001). https://doi.org/10.1163/15685610152715773
  19. N. V. Bhat, D. J. Upadhyay, R. R. Deshmukh, and S. K. Gupta, J. Phys. Chem. B, 107, 4550 (2003). https://doi.org/10.1021/jp021729s
  20. K. Nakanishi, Infrared Absorption Spectroscopy, Holden-Day, San Francisco, 1962.

Cited by

  1. 오일스네어에 대한 오일 흡착기준 정립 및 고시방향 연구 vol.34, pp.6, 2012, https://doi.org/10.14346/jkosos.2019.34.6.22