Abstract
The computer simulation was performed to confirm distribution of current and power density according to inner diameter of graphite mold of SPS(Spark Plasma Sintering). When the inner diameters of a graphite mold are varied $10mm{\Phi}$, $20mm{\Phi}$, $30mm{\Phi}$ and $40mm{\Phi}$, the more the inner diameter of graphite mold is decreased, the more the current density of punch section is increased. Because the electrical resistivity of the SiC-$ZrB_2$ specimen section($7.77{\times}10^{-4}{\Omega}{\cdot}cm$) was lower than the electrical resistivity($6.00{\times}10^{-3}{\Omega}{\cdot}cm$) of graphite section, the current density and power density of specimen section was higher than those of graphite section. It is considered that a SiC-$ZrB_2$ composite is sintered by more Joule heat of specimen section than that of mold and punch section. The current and power density distribution of a SiC-$ZrB_2$ composite can be predicted through computer simulation when SPS is conducted, and an electrical resistivity of the SiC-$ZrB_2$ composite is main element of SPS.