Preparation of High Purity α-Alumina from Aluminum Black Dross by Redox Reaction

알루미늄 블랙 드로스로부터 산화 환원반응을 이용한 고순도 알파 알루미나의 제조

  • 신의섭 (나고야대학대학원 공학연구과 결정재료공학전공) ;
  • 안응모 (한국지질자원연구원 광물자원연구본부) ;
  • 이수정 (한국지질자원연구원 광물자원연구본부) ;
  • 오오츠키 치카라 (나고야대학대학원 공학연구과 결정재료공학전공) ;
  • 김윤종 ((주)미네월드) ;
  • 조성백 (한국지질자원연구원 광물자원연구본부)
  • Received : 2012.06.19
  • Accepted : 2012.07.28
  • Published : 2012.09.27

Abstract

We investigate the effects of redox reaction on preparation of high purity ${\alpha}$-alumina from selectively ground aluminum dross. Preparation procedure of the ${\alpha}$-alumina from the aluminum dross has four steps: i) selective crushing and grinding, ii) leaching process, iii) redox reaction, and iv) precipitation reaction under controlled pH. Aluminum dross supplied from a smelter was ground to separate metallic aluminum. After the separation, the recovered particles were treated with hydrochloric acid(HCl) to leach aluminum as aluminum chloride solution. Then, the aluminum chloride solution was applied to a redox reaction with hydrogen peroxide($H_2O_2$). The pH value of the solution was controlled by addition of ammonia to obtain aluminum hydroxide and to remove other impurities. Then, the obtained aluminum hydroxide was dried at $60^{\circ}C$ and heat-treated at $1300^{\circ}C$ to form ${\alpha}$-alumina. Aluminum dross was found to contain a complex mixture of aluminum metal, aluminum oxide, aluminum nitride, and spinel compounds. Regardless of introduction of the redox reaction, both of the sintered products are composed mainly of ${\alpha}$-alumina. There were fewer impurities in the solution subject to the redox reaction than there were in the solution that was not subject to the redox reaction. The impurities were precipitated by pH control with ammonia solution, and then removed. We can obtain aluminum hydroxide with high purity through control of pH after the redox reaction. Thus, pH control brings a synthesis of ${\alpha}$-alumina with fewer impurities after the redox reaction. Consequently, high purity ${\alpha}$-alumina from aluminum dross can be fabricated through the process by redox reaction.

Keywords

References

  1. G. J. Kulic and J. C. Daley, in Proceeding of the Second International Symposium on Recycling of Metals and Engineered Materials (Williamsburg, VA, October 1990), p. 427.
  2. O. Manfredi, W. Wuth and I. Bohlinger, J. Miner. Met. Mater. Soc., 49(11), 48 (1997). https://doi.org/10.1007/s11837-997-0012-9
  3. B. J. Jody, E. J. Daniels, P. V. Bonsignore and D. E. Karvelas, J. Resource Manage. Tech., 20(1), 38 (1992).
  4. M. N. I. Castro, J. M. A. Robles, D. A. C. Hernández, J. C. E. Bocardo and J. T. Torres, Ceram. Int., 35, 921 (2009). https://doi.org/10.1016/j.ceramint.2008.03.006
  5. S. J. Yoo, D. H. Kwak, S. I. Lee, J. W. Lee, U. Y. Hwang, J. G. Kim, H. J. Jung, H. S. Yoon and H. D. Jang, Kor. J. Chem. Eng., 26, 281 (2009). https://doi.org/10.1007/s11814-009-0048-3
  6. H. N. Yoshimura, A. P. Abreu, A. L. Molisani, A. C. de Camargo, J. C. S. Portela and N. E. Narita, Ceram. Int., 34, 581 (2008). https://doi.org/10.1016/j.ceramint.2006.12.007
  7. N. Murayama, N. Okajima, S. Yamaoka, H. Yamamoto and J. Shibata, J. Eur. Ceram. Soc., 26, 459 (2006). https://doi.org/10.1016/j.jeurceramsoc.2005.06.022
  8. B. Dash, B. R. Das, B. C. Tripathy, I. N. Bhattacharya and S. C. Das, Hydrometallurgy, 92, 48 (2008). https://doi.org/10.1016/j.hydromet.2008.01.006
  9. B. Lucheva, Ts. Tsonev and R. Petkov, J. Univ. Chem. Technol. Metallurgy, 40(4), 335 (2005).
  10. M. Ueda, S. Tsukamoto, S. Konda and T. Ohtsuka, J. Appl. Electrochem., 35, 925 (2005). https://doi.org/10.1007/s10800-005-5289-1
  11. J. G. Speight, Lang's Handbook of Chemistry, 16th ed., p.1331, McGraw-Hill, NY, USA (2005).