Wear Behavior of C/B filled NR Compounds using a Blade-type Abrader

칼날형 마모시험기를 이용한 C/B충전 NR 배합고무의 마모거동

  • Youn, J.H. (Department of Advanced Chemicals and Engineering, Chonnam National University) ;
  • Kaang, Shinyoung (School of Applied Chemical Engineering, Chonnam National University)
  • 윤재훈 (전남대학교 신화학소재공학과) ;
  • 강신영 (전남대학교 응용화학공학부)
  • Received : 2014.02.19
  • Accepted : 2014.03.06
  • Published : 2014.03.31

Abstract

Friction and wear behaviors of natural rubber(NR) compounds were investigated using a blade-type abrader. The effects of temperature, normal load, and rotation speed on wear rate were studied, and wear behaviors of deteriorated compounds were also evaluated. As the rotation speed of specimen and the normal load to specimen increased, the wear rate increased. However, as the experimental temperature increased, the frictional coefficient decreased and the wear rate decreased accordingly. It was found from the wear studies that a power-law relation works between the frictional work input and the wear rate. It was observed that the wear rate dramatically increased by the degradation of the rubber specimen. The wear pattern was developed and the bigger ridge space of the pattern was observed usually in the higher normal load applied. In determining the wear rate of rubber compound, the continuous measurements of wear distance using the blade-type abrader could be successfully used instead of intermittent measurements of wear-loss weight.

칼날형 마모 마찰 시험기를 이용하여 NR배합고무의 마모 거동을 조사하였다. 온도, 하중, 그리고 회전속도를 변화시켜 마모속도에 미치는 영향과 열화된 배합고무의 마모 현상에 대해 평가하였다. 시편의 회전속도와 수직 하중이 증가할수록 마모속도가 증가하였다. 실험온도가 증가할수록 마찰계수가 감소하였고, 마모속도도 감소하였다. 마찰에너지와 마모속도 사이에 Power-Law 관계를 나타냈으며 마모속도는 열화에 의해 급격히 증가하였다. 시편의 마모패턴은 마모조건에 의해 영향을 받았으며 특히 수직 하중을 변화시켰을 때 마모융기(ridge)간격에 큰 변화를 보였다. 배합고무의 마모속도를 결정하는데 간헐적 마모손실 무게측정 대신 칼날형 마모시험기를 이용한 연속적인 마모이동거리측정으로 대체할 수 있음을 확인하였다.

Keywords

References

  1. G.J. Lake and A.G. Thomas, "Natural Rubber Science and Technology" ed. by A.D. Roberts, Chap. 15, p.731, Oxford University Press, New York, 1988.
  2. K.P. Jones, P.M. Lewis, P.McL. Swift, and I.R. Wallace, "Natural Rubber Science and Technology" ed. by A.D. Roberts, Chap. 8, p.283, Oxford University Press, New York, 1988.
  3. A. Schallamach, "Abrasion of rubber by a needle", J. Polym. Sci., 9, 385 (1952). https://doi.org/10.1002/pol.1952.120090501
  4. A. Schallamach, "Friction and abrasion of rubber", Wear, 1, 384 (1958). https://doi.org/10.1016/0043-1648(58)90113-3
  5. A. Schallamach, "Recent advances in knowledge of rubber friction and tire wear", Rubber Chem. Technol., 41, 209 (1968). https://doi.org/10.5254/1.3539171
  6. K. A. Grosch, "The relation between the friction and visco- elastic properties of rubber", Proc. Roy. Soc., A274, 21 (1963).
  7. G. M. Bartenev and V. V. Lavrentiv, "Friction and Wear of Polymers", Chap. 4, p.111, Elsevier North-Holland, Amsterdam, 1981.
  8. A.N. Gent and C.T.R. Pulford, "Mechanisms of rubber abrasion", J. Appl. Polym. Sci., 28, 943 (1983). https://doi.org/10.1002/app.1983.070280304
  9. A.N. Gent and C.T.R. Pulford, "Wear of steel by rubber", J. Wear, 49, 135 (1978). https://doi.org/10.1016/0043-1648(78)90028-5
  10. A.N. Gent and C.T.R. Pulford, "Wear of metal by rubber", J. Materials Sci., 14, 1301 (1979). https://doi.org/10.1007/BF00549301
  11. A.N. Gent and C. Nah, "Abrasion of rubber by a blade abrader: effect of blade sharpness and test temperature for selected compounds", Rubber Chem. Technol., 69, 819 (1996). https://doi.org/10.5254/1.3538405
  12. C. Nah, J. Cho, and S. Kaang, "An improved test method of abrasion of rubber in a blade abrader". Poly. Test., 17, 11 (1998). https://doi.org/10.1016/S0142-9418(97)00025-1
  13. S. Kaang, J. Cho, S. Kim, C. Nah, and C.T. Cho, "Friction and wear of rubber compounds containing powdered polynorbornene vulcanizate", J. Polym. Eng., 18(1-2), 83 (1998).

Cited by

  1. An experimental study of the friction and wear on counterpart roughness of silica particle reinforced nano composites vol.50, pp.2, 2014, https://doi.org/10.3796/KSFT.2014.50.2.162