Effect of PPG, MDI, 2-HEMA and butyl acrylate content on the properties of polyurethane adhesive

폴리우레탄 접착제의 물성에 미치는 PPG, MDI, 2-HEMA 및 butyl acrylate량의 영향

  • 박찬영 (부경대학교 공과대학 고분자공학과)
  • Received : 2014.08.20
  • Accepted : 2014.08.25
  • Published : 2014.09.30
Download PDF
⟨ Previous Next ⟩

Abstract

FT-IR measurement and the physical properties of polyurethane adhesive prepared from the polyol, isocyanate, 2-HEMA and other acrylate monomers were examined. The softening point, viscosity, adhesion strength and mechanical properties of the PU adhesives were reviewed by Ring and Ball method, Brookfield viscometer and universal test machine, respectively. Results revealed that increment of both PPG amount and butyl acrylate content decreased softening point, adhesion strength, tensile strength and 100% modulus. However as 2-HEMA and MDI content increased the mechanical properties including tensile strength, 100% modulus increased, and also the viscosity and NCO content increased.

폴리올, 이소시아네이트, 2-HEMA 및 기타 아크릴레이트 단량체들로부터 제조된 폴리우레탄 접착제의 FT-IR측정과 물성을 검토하였다. 폴리우레탄 접착제의 연화점, 점도, 접착강도 및 기계적 물성들이 각각 링과볼법, Brookfield 점도계 및 만능시험기를 이용하여 검토되었다. 실험 결과에 의하면 PPG 함량 및 부틸아크릴레이트 함량이 증가함에 따라 연화점, 접착강도, 인장강도 및 100% modulus 값 등은 감소하는 것을 보여준다. 하지만 2-HEMA 및 MDI량이 증가할수록 인장강도 및 100% modulus값 등은 증가하였으며 점도와 NCO함량 등도 또한 증가하였다.

Keywords

References

  1. D. D. Sandip, V .P. Jigar, K. S. Vijay, "Polyurethane adhesive system from biomaterial-based polyol for bonding wood", Int. J. Adhes. Adhes., 23, 393 (2003). https://doi.org/10.1016/S0143-7496(03)00070-8
  2. A. Pizzi, "Recent developments in eco-efficient bio-based adhesives for wood bonding: opportunities and issues", J. Adhes. Sci. Technol., 20, 829 (2006). https://doi.org/10.1163/156856106777638635
  3. M. Deepak, K. S. Vijay, "Eco-economical polyurethane wood adhesives from cellulosic waste: Synthesis, characterization and adhesion study", Int. J. Adhes. Adhes., 30, 47 (2010). https://doi.org/10.1016/j.ijadhadh.2009.08.003
  4. A. V. Pocius, Adhesion and Adhesives Technology, Hanser Publishers, New York (1997).
  5. J. F. Meier, Fundamentals of Plastics and Elastomers, C.A. Harper(Ed.), Handbook of Plastics, Elastomers, and Composites (3rd ed.), McGraw Hill, New York (1996).
  6. I. Skiest, J. Miron,, Handbook of Adhesives, (3rd ed.)Van Nostrand Reinhold Publishing, New York (1990).
  7. J. Tyczkowski, I. Krawczyk-K, S. Kuberski, P. Makowski, "Chemical nature of adhesion: Plasma modified styrene-butadiene elastomer and polyurethane adhesive joints", Eur. Polym. J., 46, 767 (2010). https://doi.org/10.1016/j.eurpolymj.2009.12.019
  8. D. Rakai, E. Charles, "Structure-property behavior of moisture-cure polyurethane wood adhesives: Influence of hard segment content", Int. J. Adhes. Adhes., 45, 1184 (2013).
  9. H. Yong, Z. Xinya, Z. Xinfang, H. Hong, C. Jie, C. Huanqin, "Structural investigations of toluene diisocyanate (TDI) and trimethylolpropane (TMP)-based polyurethane prepolymer", J. Ind. Eng. Chem., 18, 1620 (2012). https://doi.org/10.1016/j.jiec.2012.02.023
  10. M. Gauthier, Engineered Materials Handbook Vol. 3: Adhesives and Sealants., American Society for Materials (1990).
  11. R. Krech, J. Mueller, N. Pohlmann, P. Sellig, R. Steinberger, US Patent 6,538,075 B1 (2003).
  12. S. B. Clough, N. S. Schneider, "Structural studies on urethane elastomers", J. Mcromol. Sci. B: Phys., 2, 553 (1968). https://doi.org/10.1080/00222346808212458
  13. P. Carmen, N. S. Allen, E. F. Salvador, C. Teresa, C. Fernando, "Chemiluminescence and fluorescence for monitoring the photooxidation of an UV-cured aliphatic polyurethane-acrylate based adhesive", Polym. Degrad. Stab., 77, 523 (2002). https://doi.org/10.1016/S0141-3910(02)00111-8
  14. J. H. Saunders, K. C. Frisch, Polyurethanes: Chemistry and Technology: Part 1. Chemistry, Interscience Publishers, 368 (1962).
  15. H. A. Essawy, A. Moustafa, N. H. Elsayed, "Enhancing the properties of urea formaldehyde wood adhesive system using different generations of core-shell modifiers based on hydroxyl-terminated dendritic poly(amidoamine)", J. Appl. Polym. Sci., 115, 370 (2010). https://doi.org/10.1002/app.30572
  16. K. Alireza, R. Bernard, "Nano-aluminum oxide as a reinforcing material for thermoplastic adhesives", J. Ind. Eng. Chem., 18, 1076 (2012). https://doi.org/10.1016/j.jiec.2011.12.001
  17. S. Kirchmeyer, H. P. Muller, M. Ullrich,, U. Liesenfelder, US Patent 6,417,312 B1 (2002).
  18. S. Yamasaki, D. Nishiguchi, K. Kojio, M. Furukawa, "Effects of polymerization method on structure and properties of thermoplastic polyurethanes", J. Polym. Sci. B: Polym. Phys., 45, 800 (2007).
  19. H. B. Tsai, D. K. Lee, R. S. Tsai, P. Chen, Y. F. Yang, H. H. Wang, "Synthesis and properties of transparent thermoplastic segmented polyurethanes", Adv. Polym. Technol., 26, 33 (2007). https://doi.org/10.1002/adv.20086

Cited by

  1. Study of Dye Encapsulated Microcapsule Polymerization Using Polyurethane Prepolymer Synthesis and Textile Finishing vol.27, pp.3, 2015, https://doi.org/10.5764/TCF.2015.27.3.184