A Comparison of Residual Tensile Properties of GFRP Reinforcing Bar at High Temperature and after Exposure to High Temperature

고온과 고온노출 후 GFRP 보강근의 잔존인장성능 비교

  • Received : 2014.10.06
  • Accepted : 2014.12.14
  • Published : 2015.02.01
Download PDF
⟨ Previous Next ⟩

Abstract

Tensile tests were conducted on the GFRP reinforcement exposed to high temperature. The exposure condition for this study was below $200^{\circ}C$ for about 3 minutes. This conditioning is minor compared with that presented in experimental program conducted by other researchers. The residual tensile strength and elastic modulus of GFRP reinforcing bars at high temperature and after exposure to high temperature were compared. In results, tensile properties were decreased at high temperatures, but those after exposure to high temperature were recovered to pre-heating level almost completely. These results could be valuable for evaluating GFRP reinforced structure damaged by fire accident.

고온에 노출된 GFRP 보강근의 인장실험을 수행하였다. 본 실험을 위한 고온노출조건은 $200^{\circ}C$ 이하의 온도에 3분간 노출하는 것으로 하였다. 이러한 조건은 다른 연구자들의 시험에서 적용한 고온노출조건과 비교하여 경미한 고온노출조건이다. 고온에서와 고온노출 후 GFRP 보강근의 인장강도와 탄성계수를 비교하였다. 실험결과, 고온에서 GFRP 보강근의 인장성능이 감소하는 것으로 나타났으나, 고온노출 후 보강근의 인장성능은 거의 고온노출전의 수준으로 회복되는 것으로 나타났다. 이와 같은 결과는 화재로 손상 받은 GFRP 보강 콘크리트 구조물의 평가를 위하여 중요한 자료가 된다.

Keywords

References

  1. Abbasi, A. and Hogg, P. J. (2005). "Temperature and environmental effects on glass fibre rebat : Modulus, Strength and Interfacial Bond Strength with Concrete." Compos : Part B., Vol. 36, pp. 394-404. https://doi.org/10.1016/j.compositesb.2005.01.006
  2. Alsayed, S., Al-Salloum, Y., Almusallam, T., El-Gamal, S. and Aqel, M. (2012). "Performance of glass fiber reinforced polymer bars under elevated temperatures." Compos : Part B., Vol. 43, pp. 2265-2271. https://doi.org/10.1016/j.compositesb.2012.01.034
  3. AL-ZAHRANI, M., AL-DULAIJAN, S. U., AL-IDI, S. H. and AL-METHEL, M. H. (2007). "High temperature effect on tensile strength of GFRP bars and flexural behavior of GFRP reinforced concrete beams." FRPRCS-8, University of Patras. Patras. Greece.
  4. Bisby, L. A., Green, M. F. and Kodur, V. K. R. (2005). "Response to fire of concrete structures that incorporate FRP." Prog. Struct. Engng Mater., Vol. 7, pp. 136-149. https://doi.org/10.1002/pse.198
  5. Bosze, E. J., Alawar, A., Bertschger, O., Tasai, Y. I. and Nutt, S. R. (2006). "High-temperature strength and storage modulus in unidirectional hybrid composites." Compos. Sci. Tech., Vol. 66, pp. 1963-1969. https://doi.org/10.1016/j.compscitech.2006.01.020
  6. Correia, J. R., Gomes, M. M., Pires, J. M. and Branco, F. A. (2013). "Mechanical behaviour of pultruded glass fibre reinforced polymer composites at elevated temperature : Experiments and Model Assessment." Compos. Struct., Vol. 98 pp. 303-313. https://doi.org/10.1016/j.compstruct.2012.10.051
  7. Foster, S. K. and Bisby, L. A. (2005). "High temperature residual properties of externally-bonded FRP systerms." Am. Concr. Inst., Vol. ACI-SP230, No. 7, pp. 1235-1252.
  8. Fu, Y. N., Zhao, J. and Li, Y. L. (2011). "Research on tensile mechanical properties of GFRP rebar after high temperature." Adv. Mater. Research., Vol. 181-182, pp. 349-354. https://doi.org/10.4028/www.scientific.net/AMR.181-182.349
  9. Kashwani, G. A. and Al-Tamimi, A. K. (2014). "Evaluation of FRP bars performance under high temperature." Phys. Procedia., Vol. 55, pp. 296-300. https://doi.org/10.1016/j.phpro.2014.07.043
  10. Kumahara, S., Masuda, Y., Tanano, H. and Shimizu, A. (1993). "Tensile strength of continuous fiber bar under high temperature." Spec. Publ., Vol. 138, pp. 731-742.
  11. Robert, M. and Benmokrane, B. (2010). "Behavior of GFRP reinforcing bars subjected to extreme temperatures." J. Compos. Constr., Asce., pp. 353-360.
  12. Saafi, M. (2002). "Effect of fire on FRP reinforced concrete members." Compos. Struct., Vol. 58, pp. 11-20. https://doi.org/10.1016/S0263-8223(02)00045-4
  13. Wang, Y. C. and Kodur, V. (2005). "Variation of strength and stiffness of fibre reinforced polymer reinforcing bars with temperature." Cem. Concr. Compos., Vol. 27, pp. 864-874. https://doi.org/10.1016/j.cemconcomp.2005.03.012
  14. Weber, A. (2008). "Fire-resistance tests on composite rebars." 4th Int. Conf. FRP Compos. Civ. Eng. (CICE 2008), Zurich, Switzerland.