Abstract
Overlay welding affects the chemical components and weld hardness by dilution of the lamination layer thickness, which determines the surface properties. This study experimentally investigates different numbers of layers for overlay welding monel materials, which are anti-corrosion materials. The Fe content, weldability of the base metal and monel materials, hardness, and surface flatness were examined. Each evaluation was carried out after overlay welding with three layers on the base material and pipe base material of the plate. The Fe content was evaluated by analyzing the constituents of each layer. The Fe content was satisfactory in the three layers. The weldability of the laminate specimens was evaluated by a bending test. The hardness and bead flatness of the laminate specimens were evaluated by micro Vickers and 3D measurements. The hardness was highest in the heat-affected zone with one layer, and it decreased with increasing lamination. In the case of bead flatness, there is a sharp difference in the deviation with increasing numbers of laminations, which should be considered carefully.
오버레이 용접은 희석율에 의해 적층 두께에 따라 화학성분 함량과 용접부의 경도에 영향을 미치며 이는 파이프 제품의 표면성질을 결정한다. 이로 인해 오버레이 용접은 적층의 수를 고려하여야 한다. 본 연구에서는 탄소강 모재에 내부식성 소재인 모넬 소재를 오버레이 용접하여 적층수에 따른 Fe함량, 모재와 모넬 소재와의 용접성, 부위별 경도와 표면 평탄도를 실험적으로 연구하였다. 각각의 평가는 평판의 모재와 파이프 모재에 3개의 층으로 오버레이 용접 후 실시하였다. Fe함량은 각 층별 시료를 채취하여 성분 분석을 통해 평가하였으며, 3Layer에서 만족하는 함량을 나타내었다. 또한 적층별 시편을 밴딩 시험하여 용접성을 평가하였다. 적층별 경도와 비드 평탄도는 Micro Vickers와 3차원 측정을 통해 평가하였다. 경도는 1Layer에서 발생하는 HAZ부에 의해 가장 높은 경도 값을 보였으며, 적층이 증가할수록 경도가 감소하였다. 비드 평탄도의 경우 적층수 증가에 따라 편차가 급격한 차이가 발생하였으며, 이는 경도와 함께 사용 목적의 측면에서 주의 깊게 고려해야 한다. 이러한 실험적 결과는 목적에 따른 용접 파이프 적층수의 결정 방법을 나타내었다.