Abstract
Carbon fiber-reinforced composite materials have been widely used in various industrial fields, but there are limits to increasing their strength and stiffness, because of the short-length fibers that are impregnated in them. In this study, a lab-scale small extruder system was developed with the capability to perform the carbon fiber impregnation and extrusion process in order to evaluate the properties of long-length carbon fiber reinforced thermoplastic composite materials molded by the LFT-D method. Specimens were made with the small extruder to press-mold long-length carbon fiber composite materials and evaluate their material properties. As a result, it was found that the carbon fiber length, press load and carbon fiber contents have a considerable influence on the strength and stiffness. Additional studies on such factors as the mixing screw design and coating of the carbon fiber are needed in order to improve the mechanical properties of carbon fiber composite materials.
탄소섬유강화 복합재는 기계적 물성이 우수하여 다양한 산업분야에서 활용되고 있으나 섬유길이가 짧은 단섬유 형태로 함침 되고 있어 강도와 강성을 증대시키는데 한계가 있다. 이를 보완하기 위한 LFT-D성형은 탄소 또는 유리섬유를 열가소성 수지와 혼합하여 압출 후 프레스 성형하여 제품을 만드는 공법으로 연속공정이 가능하고 사출성형에 비해 생산성이 높아 자동차 구조용 부품을 제작하는데 사용할 수 있다. 본 연구에서는 LFT-D공법으로 성형된 탄소 장섬유강화 열가소성 복합소재의 기계적 특성을 파악하기 위하여 탄소 장섬유의 함침과 압출공정을 수행할 수 있는 Lab scale의 소형 압출기 시스템을 제작하였다. Lab scale의 소형 압출기를 사용하여 제작된 탄소 장섬유 복합소재를 프레스 성형하여 시편을 제작하고 재료의 기계적 특성을 평가한 결과, 탄소섬유길이, 프레스 가압압력 및 탄소섬유 함유량이 복합소재의 강도 및 강성의 증가에 영향을 미침을 알 수 있었다. 향후 탄소 장섬유 복합소재의 기계적 성질 향상을 위해서 혼합 스크류 설계, 탄소 섬유코팅 등에 대한 추가적인 연구가 필요하다.