Abstract
A study to apply phase change material(PCM) to rapid hardening cement paste forming semi-rigid pavement was carried out. The characteristics fresh and hardened paste were evaluated through the experiment for a total of 6 mixtures according to the cement type and the substitution of phase change material for acrylate. The fluidity by substituting phase change material for acrylate satisfied the target flow time of 10 to 13 seconds. In case of setting time, it was possible to secure the performance of rapid hardening cement by substituting phase change material, and if the substitution ratio over 60%, the initial set occurred 1 to 2 minutes faster than other mixtures. In case of compressive strength and bond strength, it showed similar strength characteristics with the plain mixture, and it satisfied both the target compressive and bonding strength of 36MPa and 2MPa. The mixture substituting phase change material showed higher resistance to chloride ion penetration than the mixture only using acrylate and the OPC level was insufficient. From the results of physical and mechanical performances of semi-rigid pavement cement paste, the phase change material substitution rate of 20% was effective in the range of this study.
본 연구에서는 상변화물질(PCM)을 반강성 포장체를 구성하는 초속경시멘트 페이스트 주입재에 적용하기 위한 연구를 수행하였다. 반강성포장용 주입재의 아크릴레이트를 PCM으로 치환에 따른 총 6종류의 주입재 배합에 대하여 경화 전 후 특성을 실험을 통해 평가하였다. 아크릴레이트를 PCM으로 치환하여 유동성을 평가한 결과 본 연구에서 목표로한 유하시간 10~13초를 모두 만족시킬 수 있는 것으로 나타났다. 응결시간의 경우 PCM으로 치환하더라도 초속경 시멘트의 성능을 확보할 수 있는 것으로 나타났고, PCM 치환 60%이상의 경우 초결시간이 다른 배합에 비해 1~2분 빨리 발생되었다. 압축강도 및 부착강도의 경우 Plain 배합과 유사한 강도특성을 나타내었고, 본 연구에서 목표로 하는 압축강도 36MPa, 부착강도 2MPa를 모두 만족시켰다. PCM으로 치환한 배합은 아크릴레이트만을 사용한 배합에 비해 우수한 염소이온침투저항성을 나타내었으나, OPC수준에는 미흡하였다. 반강성포장용 주입재에 대한 물리 역학적 성능평가 결과, 이 연구의 범위내에서는 PCM 대체율 20% 수준이 효과적인 것으로 판단된다.