Life Time Prediction Using Accelerated Ageing Test for a CR/CB Rubber Composite

  • Ahn, WonSool (Department of Chemical Engineering, Keimyung University) ;
  • Lee, Hyung Seok (Technology Center, Sanyang Rubber Co., LTD)
  • Received : 2017.09.26
  • Accepted : 2017.11.01
  • Published : 2017.12.31
Download PDF
⟨ Previous Next ⟩

Abstract

The tensile strength (TS) and elongation-at-break (EB) loss of a CR/CB rubber composite sample prepared for the automotive parts were measured after accelerated thermal ageing at temperatures of 100, 120, 140, and $150^{\circ}C$. The change in TS was observed to be linear from the master curve prepared using the time-temperature superposition-principle (TTSP). An Arrhenius type of shift factor, $a_T$ was used to predict the life time of the sample, and a plot of ln $a_T$ vs. 1/T was also shown to be linear. The activation energy ($E_a$) of the sample was calculated as 70.30 kJ/mole from the Arrhenius plot. The expected life time of the sample was predicted at the given operating conditions by applying Arrhenius analysis. Assuming the $E_a$ value was constant at lower operating condition, life time of the sample was calculated as 2.3 years when the life limit was set as time to reach the 20% decrease of the initial TS value at operating temperature of $40^{\circ}C$.

Keywords

References

  1. B. Adhikari and D. de Maiti, "Reclamation and Recycling of Waste Rubber", Progress in Polymer Science, 25, 909 (2000). https://doi.org/10.1016/S0079-6700(00)00020-4
  2. S. R. Scagliusi, S. G. Arajo, L. Landini, and A. B. Lugao, "Study of Properties of Chloroprene Rubber Devulcanizate by Radiaion in Micrwave", 2009 International Nuclear Atlantic Conference-INAC 2009.
  3. D. J. Toop, "Theory of Life Testing and Use of Thermogravimetric Analysis to Predict the Thermal Life of Wire Enamels", IEEE Trans. Elec. Insul., E1-6, 2 (1971).
  4. R. P. Brown, "Practical Guide to the Assessment of the Useful life of Rubbers", pp. 117-124, Rapra Technology, 2001.
  5. J. Wise, K. T. Gillen, and R. L. Clough, "An ultra sensitive technique for testing the Arrhenius extrapolation assumption for thermally aged elastomers", Polym. Degrd. Stab., 49, 403 (1995). https://doi.org/10.1016/0141-3910(95)00137-B
  6. A. L. Stokoe, "Heat Ageing of Rubbers", Technical Report No. 91, Explosives Research and Development Establishment in Ministry of Defence, England, 1972.
  7. C. S. Woo and H. S. Park, "Useful lifetime prediction of rubber component", Engineering Failure Analysis, 18, 1645 (2011). https://doi.org/10.1016/j.engfailanal.2011.01.003
  8. W. Ahn and K. H. Park, "A Study on Thermal Life-Time Expectation of NR Rubber Material using Isothermal TGA and TMA", Elast. Compos., 44, 269 (2009).
  9. W. D. Kim, W. S. Kim, C. S. Woo, and S. J. Cho, "Prediction of Useful Life by Heat Ageing of Motor Fan Isolating Rubber", Elastomer(Korea), 37, 107 (2002).
  10. K. T. Gillen, R, Bernstein, and D. K Derzon, "Evidence of non-Arrhenius behavior from laboratory ageing and 24-year field adeing of polychloroprene rubber materials", Polym. Degrd. Stab., 87, 57 (2005). https://doi.org/10.1016/j.polymdegradstab.2004.06.010
  11. W. Ahn and H. S. Lee, "A Study on Creep Behavior of ACM Rubber using TMA Thermal Analysis", Elast. Compos., 48, 156 (2013). https://doi.org/10.7473/EC.2013.48.2.156