Durability of Alkali-Activated Slag-Red Mud Cement Mortar Using Polymer

폴리머 혼입 알칼리활성화 슬래그-레드머드 시멘트모르타르의 내구특성

  • Received : 2016.09.12
  • Accepted : 2016.12.22
  • Published : 2017.01.30

Abstract

The alkali-slag-red mud (ASRC) cement belongs to clinker free cementitious material, which is made from alkali activator, blast-furnace slag (BFS) and red mud in designed proportion. This study is to investigate durability such as accelerated carbonation test, chloride ion penetration test and freezing and thawing resistance of alkali-activated slag-red mud cement according to the red mud content. The results showed that the durability such as accelerated carbonation resistance, chloride ion penetration resistance and freezing and thawing resistance of alkali-activated slag cement decreased as the red mud content increased. but the chloride ion penetration resistance of alkali-activated slag cement was increased compared with that of ordinary portland cement, regardless of the red mud content. In terms of the effects of pore structure, generally, a larger mean pore radius and/or higher total porosity will cause durability decreased. Comparing alkali-activated slag cement and ordinary portland cement, the addition of red mud increase the pore size less than 100nm and the pore size distribution seems very similar. The overall porosity becomes important factor in affecting the durability, as can be seen in the foamed samples.

Keywords

Acknowledgement

Supported by : 국토교통부

References

  1. Hakkinen, T. (1986). Properties of alkali-activated slag concrete, VTT Research Notes, Technical Research Centre of Finland(VTT), No. 540.
  2. Hyung, W. (2006). Properties of Polymer-Modified Mortars Using Acrylic Latexes According to Glass Transition Temperature, Journal of the Architectural Institute of Korea Structure & Construction, 22(6), 103-109
  3. Kang, S. (2013). Strength Properties of Alkali-activated Cementless Binder Mortar Using Polymer. Journal of the Construction and Environment Research Institute. 8(1), 112-119.
  4. Kim, J., Lee, J., & Hyung, W. (2014). Properties of Alkali-Activated Cement Mortar by Curing Method, Jourmal of the Korea Concrete Institute, 26(2), 117-124 https://doi.org/10.4334/JKCI.2014.26.2.117
  5. Krivenko, P. (1994). Theory, Chemistry, Structure and Properties of Alkaline Cementitious Systems, First International Conference on Alkaline Cements and Concretes, Kiev, Ukraine, Vol. 1, 12-29
  6. Kumar, S., Kumar, R., & Mehrotra, S. (2010). Influence of granulated blast furnace slag on the reaction, structure and properties of fly ash based geopolymer, J Mater Sci, 45, 607-615 https://doi.org/10.1007/s10853-009-3934-5
  7. Moon, K. (2004). Properties of non-sintered cement and concrete recycled with industrial waste, Chonbuk National University, Ph.D thesis, 61-172
  8. Narender Reddy, A., Anitha, D., & Venkata Tilak, U. (2014). Performance of Alkali Activated Slag and Alkali Activated Slag + Fly Ash with various Alkali Activators, International Journal of Engineering and Technical Research, Vol. 2, Issue 1, 73-78
  9. Pontikes, Y., & Angelopoulos, G. (2013). Bauxite residue in cement and cementitious applications : Current status and a possible way forward, Resources, Conservation and Recycling, 73, 53-63 https://doi.org/10.1016/j.resconrec.2013.01.005
  10. Pan, Z., Li, D., Yu, J., & Yang, N. (2003). Properties and Microstructure of the Hardened Alkali-Activated Red Mud-Slag Cementitious Material, Cement and Concrete Research, 33, 1437-1441 https://doi.org/10.1016/S0008-8846(03)00093-0
  11. Park, P. (2008). A Study on the Influence of VAE Polymers on the Cement Hydration. Ph.D. Dissertation. M yongji University, 112-123.
  12. Takameto, K., & Unikawa, H. (1980). 7th International Congress on Chemistry of Cement, I, IV-2/1-2.29.