Thermal Dissipation Property of Acrylic Composite Films Containing Graphite and Carbon Nanotube

흑연과 탄소나노튜브 함유 아크릴 복합체 박막의 방열 특성

  • Kim, Junyeong (Department of Advanced Materials Engineering, Korea Polytechnic University) ;
  • Kang, Chan Hyoung (Department of Advanced Materials Engineering, Korea Polytechnic University)
  • 김준영 (한국산업기술대학교 신소재공학과) ;
  • 강찬형 (한국산업기술대학교 신소재공학과)
  • Received : 2017.04.14
  • Accepted : 2017.05.15
  • Published : 2017.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

Thermal dissipation was investigated for poly methyl methacrylate (PMMA) composite films containing graphite and multi wall carbon nanotube(CNT) powders as filler materials. After mixing PMMA with fillers, solvent, and dispersant, the pastes were prepared by passing through a three roll mill for three times. The prepared pastes were coated $15{\sim}40{\mu}m$ thick on a side of 0.4 mm thick aluminium alloy plate and dried for 30 min at $150^{\circ}C$ in an oven. The content of fillers in dried films was varied as 1, 2, and 5 weight % maintaining the ratio of graphite and CNT as 1:1. Raman spectra from three different samples exhibited D, G and 2D peaks, as commonly observed in graphite and multi wall CNT. Among those peaks, D peak was prominent, which manifested the presence of defects in carbon materials. Thermal emissivity values of three samples were measured as 0.916, 0.934, and 0.930 with increasing filler content, which were the highest ever reported for the similar composite films. The thermal conductivities of three films were measured as 0.461, 0.523, and $0.852W/m{\cdot}K$, respectively. After placing bare Al plate and film coated samples over an opening of a polystyrene box maintained for 1 h at $92^{\circ}C$, the temperatures inside and outside of the box were measured. Outside temperatures were lower by $5.4^{\circ}C$ in the case of film coated plates than the bare one, and inside temperatures of the former were lower by $3.6^{\circ}C$ than the latter. It can be interpreted that the PMMA composite film coated Al plates dissipate heat quicker than the bare Al plate.

Keywords

References

  1. S. Garimella, A. S. Fleischer, J. Y. Murphy, A. Keshavarzi, R. Prasher, C. Patel, S. H. Bhavnani, R. Venkatasubramanian, R. Mahajan, Y. Joshi, B. Sammakia, B. A. Myers, L. Chorosinski, M. Baelmans, P. Sathyamurthy, Thermal challenges in next-generation electronic systems, IEEE Trans. Comp. Pack. Tech., 31 (2008) 801-813. https://doi.org/10.1109/TCAPT.2008.2001197
  2. A. Castellazzi, T. Funaki, T. Kimoto, T. Hikihara, Thermal instability effects in SiC power MOSFETs, Microelectron. Reliab., 52 (2012) 2414-2419. https://doi.org/10.1016/j.microrel.2012.06.096
  3. D. A. Jaworske, Optical and calorimetric evaluation of Z-93-P and other thermal control coatings, Thin Solid Films, 290-291 (1996) 278-282. https://doi.org/10.1016/S0040-6090(96)08969-9
  4. H. Yu, G. Xu, X. Shen, X. Yan, C. Shao, C. Hu, Effects of size, shape and floatage of Cu particles on the low infrared emissivity coatings, Progr. Org. Coating., 66 (2009) 161-166. https://doi.org/10.1016/j.porgcoat.2009.07.002
  5. J.-S. Roh, J.-S. Ahn, B.-J. Kim, H.-Y. Jeon, S.-K. Seo, S. H. Kim, S.-W. Lee, Thermal emissivity changes as a function of degree of flakes alignment on the graphite surfaces, J. Kor. Inst. Surf. Eng., 42 (2009) 95-101. https://doi.org/10.5695/JKISE.2009.42.2.095
  6. W.-Y. Eom, J.-S. Roh, S.-K. Seo, J.-S. Ahn, D.-S. Kang, S. H. Kim, Thermal emission effect of electronic parts using carbon materials, Kor. J. Mater. Res., 20 (2010) 204-209. https://doi.org/10.3740/MRSK.2010.20.4.204
  7. S.-M. Kim, S.-M. Lee, Preparation and characteristics of the excellent heat-releasing composites sheet containing AlN and graphite powder, J. Kor. Inst. Electric. Electronic Mater. Eng, 25 (2012) 462-466.
  8. J.-G. Kim, H.-S. Park, H. Kim, B.-D. Hahn, Y.-R. Cho, Evaluation of thermal conductivity for screen-printed AlN layer on Al substrate in thickness direction, J. Microelectron. Packag. Soc., 22 (2015) 65-70. https://doi.org/10.6117/kmeps.2015.22.4.065
  9. S. Yu, P. Hing, X. Hu, Thermal conductivity of polystyrene-aluminium nitride composite, Composites: Part A, 33 (2002) 289-292. https://doi.org/10.1016/S1359-835X(01)00107-5
  10. S.-H. Xie, B.-K. Zhu, J.-B. Li, X.-Z. Wei, Z.-K. Xu, Preparation and properties of polyimide/aluminium nitride composites, Polymer Testing, 23 (2004) 797-801. https://doi.org/10.1016/j.polymertesting.2004.03.005
  11. B. Weidenfeller, M. Hofer, F. R. Schilling, Thermal conductivity, thermal diffusivity, and specific heat capacity of particle filled polypropylene, Composites: Part A, 35 (2004) 423-429. https://doi.org/10.1016/j.compositesa.2003.11.005
  12. G.-W. Lee, M. Park, J. Kim, J. I. Lee, H. G. Yoon, Enhanced thermal conductivity of polymer composites filled with hybrid filler, Composites: Part A, 37 (2006) 727-734. https://doi.org/10.1016/j.compositesa.2005.07.006
  13. W. Zhou, S. Qi, H. Li. S. Shao, Study on insulating thermal conductive BN/HDPE composites, Thermochim. Acta, 452 (2007) 36-42. https://doi.org/10.1016/j.tca.2006.10.018
  14. J. H. Lee, M.-H. Song, C. H. Kang, Characteristics of Thermal Radiation Pastes Containing Graphite and Carbon Nanotube, J. Kor. Inst. Surf. Eng., 49 (2016) 218-224. https://doi.org/10.5695/JKISE.2016.49.2.218
  15. American Society for Testing and Materials, ASTME 1933-99a, Standard test methods for measuring and compensating for emissivity using infrared imaging radiometers.
  16. Korean Agency for Technology and Standards, KS L 1604 : 2002, Fine ceramics - Determination of thermal diffusivity, specific heat capacity, and thermal conductivity of monolithic ceramics by laser flash method.
  17. American Society for Testing and Materials, ASTME 1461-11, Standard test method for thermal diffusivity by the flash method.
  18. American Society for Testing and Materials, ASTME 1269-11, Standard test method for determining specific heat capacity by differential scanning calorimetry.
  19. S. Reich, C. Thomsen, Raman spectroscopy of graphite, Phil. Trans. R. Soc. Lond. A 362 (2004) 2271-2288. https://doi.org/10.1098/rsta.2004.1454
  20. L. Bokobza, J. Zhang, Raman spectroscopic characterization of multiwall carbon nanotubes and of composites, Polymer Letters 6 (2012) 601-608. https://doi.org/10.3144/expresspolymlett.2012.63
  21. A. Kushwara, I. Kumar, A. Khare, Laser induced breakdown of poly methyl methacrylate(PMMA) in air, J. Phys. Sci. Appl., 4 (2014) 426-429.