The Enhanced Off-Diagonal Magneto-Impedance Effect in Cu/Ni80Fe20 Core-Shell Composite Wires Fabricated by Electrodeposition under Torsional Strain

비틀림 스트레인 하에서 전기도금으로 만든 Cu 코어/Ni80Fe20 쉘 복합 와이어에서 비대각 자기임피던스(Off-diagonal Magneto-Impedance) 효과의 증대

  • Received : 2017.07.31
  • Accepted : 2017.08.08
  • Published : 2017.08.31

Abstract

The magneto-impedance effect (MI effect) has been investigated in metal core/soft magnetic shell composite wires fabricated by electrodeposition of $Ni_{80}Fe_{20}$ on Cu wire (diameter $190{\mu}m$). The diagonal impedances $Z_{zz}$ and $Z_{{\theta}{\theta}}$ in cylindrical coordinate showed strong MI effect for the magnetic field applied along z-axis, while the off-diagonal impedance $Z_{{\theta}z}$ showed very weak MI effect. We have tried to develop the Cu $core/Ni_{80}Fe_{20}$ shell composite wire having strong MI effect in off-diagonal impedance by electrodeposion under torsional strain. The core/shell composite wire electrodeposited under torsional angles above $270^{\circ}$ showed significantly enhanced MI effect in the off-diagonal impedance. The maximum MI effect was observed in the composite wire electrodeposited under torsional angle of $360^{\circ}$. The developed method to enhance off-diagonal MI effect is expected to increase the applicability of the core/shell composite wire to magnetic sensor material.

직경 $190{\mu}m$ Cu 와이어에 $Ni_{80}Fe_{20}$ 연자성 물질을 전기도금법으로 증착하여 금속 코어/연자성 쉘 구조의 복합 와이어를 제작하고 이 와이어에서 자기임피던스 효과(MI 효과)를 연구하였다. 원통 좌표계에서 복합 와이어의 임피던스 텐서의 두 대각 성분 $Z_{{\theta}{\theta}}$$Z_{zz}$는 z 방향으로 가한 자기장에 대해 큰 MI 효과를 나타낸 반면, 비대각 임피던스 $Z_{{\theta}z}$의 MI 효과는 매우 약하게 나타났다. 비대각 자기임피던스 효과가 큰 복합 와이어를 만들기 위해 비틀림 스트레인 하에서 전기도금하는 방법을 시도하였다. Cu 와이어의 한쪽 끝을 약 $270^{\circ}$ 이상 회전한 상태에서 전기도금 된 복합 와이어는 뚜렷하게 증대된 비대각 MI 효과를 보였으며 $360^{\circ}$ 회전한 상태에서 도금 된 와이어에서 최대의 비대각 MI 효과를 얻을 수 있었다. 본 연구를 통해 비대각 MI 효과가 큰 복합와이어를 제작하는 방법을 개발한 것은 금속 코어/자성 쉘 복합 와이어의 자기센서 소재로써의 응용가능성을 높일 것으로 기대된다.

Keywords

References

  1. T. Uchiyama, K. Mohri, Y. Honkura, and L. V. Panina, IEEE Trans. Magn. 48, 3833 (2012). https://doi.org/10.1109/TMAG.2012.2198627
  2. http://www.aichi-mi.com.
  3. http://www.rohm.co.kr/web/korea/news-detail?news-title=2015-07-02_ad_mi&defaultGroupId.
  4. P. Kollu, S. S. Yoon, G. W. Kim, C. S. Angani, and C. G. Kim, J. Magn. 15, 194 (2010). https://doi.org/10.4283/JMAG.2010.15.4.194
  5. A. F. Cobeno, A. Zhukov, J. M. Blanco, V. Larin, and J. Gonzalez, Sens. Act. A 91, 95 (2001). https://doi.org/10.1016/S0924-4247(01)00502-7
  6. M. H. Phan, H. X. Peng, M. T. Tung, N. V. Dung, and N. H. Nghi, J. Magn. Magn. Mater. 316, 244 (2007). https://doi.org/10.1016/j.jmmm.2007.02.111
  7. M. H. Phan and H. X. Peng, Prog. Mater. Sci. 53, 323 (2008). https://doi.org/10.1016/j.pmatsci.2007.05.003
  8. L. Chen, Y. Zhou, C. Lei, and Z. M. Zhou, Mater. Sci. Eng. B 172, 101 (2010). https://doi.org/10.1016/j.mseb.2010.04.026
  9. M. A. Correa, F. Bohn, V. M. Escobar, M. S. Marques, A. D. C. Viegas, L. F. Schelp, and R. L. Sommer, J. Appl. Phys. 110, 093914 (2011). https://doi.org/10.1063/1.3658262
  10. A. C. Mishra, T. Sahoo, V. Srinivas, and A. K. Thakur, Physica B: Condens. Matter. 406, 645 (2011). https://doi.org/10.1016/j.physb.2010.11.070
  11. D. L. Chen, X. Li, H. L. Pan, H. Y. Luan, and Z. J. Zhao, Nano-Micro Lett. 6, 227 (2014). https://doi.org/10.1007/BF03353786
  12. S. E. Cho, T. J. Goo, D. Y. Kim, S. S. Yoon, and S. H. Lee, J. Korean Magn. Soc. 25, 129 (2015). https://doi.org/10.4283/JKMS.2015.25.4.129
  13. S. E. Cho, Ph.D thesis, Andong National University, Korea (2015).