Fracture toughness of high performance concrete subjected to elevated temperatures Part 2 The effects of heating rate, exposure time and cooling rate

  • Zhang, Binsheng (School of Engineering and Built Environment, Glasgow Caledonian University) ;
  • Cullen, Martin (School of Engineering and Built Environment, Glasgow Caledonian University) ;
  • Kilpatrick, Tony (School of Engineering and Built Environment, Glasgow Caledonian University)
  • 투고 : 2017.07.24
  • 심사 : 2017.09.19
  • 발행 : 2017.10.25

초록

In this study, the fracture toughness $K_{IC}$ of high performance concrete (HPC) was investigated by conducting three-point bending tests on a total of 240 notched beams of $500mm{\times}100mm{\times}100mm$ subjected to heating temperatures up to $450^{\circ}C$ with exposure times up to 16 hours and various heating and cooling rates. For a heating rate of $3^{\circ}C/min$, $K_{IC}$ for the hot concrete sustained a monotonic decrease trend with the increasing heating temperature and exposure time, from $1.389MN/m^{1.5}$ at room temperature to $0.942MN/m^{1.5}$ at $450^{\circ}C$ for 4-hour exposure time, $0.906MN/m^{1.5}$ for 8-hour exposure time and $0.866MN/m^{1.5}$ for 16-hour exposure time. For the cold concrete, $K_{IC}$ sustained a two-stage decrease trend, dropping slowly with the heating temperature up to $150^{\circ}C$ and then rapidly down to $0.869MN/m^{1.5}$ at $450^{\circ}C$ for 4-hour exposure time, $0.812MN/m^{1.5}$ for 8-hour exposure time and $0.771MN/m^{1.5}$ for 16-hour exposure time. In general, the $K_{IC}$ values for the hot concrete up to $200^{\circ}C$ were larger than those for the cold concrete, and an inverse trend was observed thereafter. The increase in heating rate slightly decreased $K_{IC}$, and at $450^{\circ}C$ $K_{IC}$ decreased from $0.893MN/m^{1.5}$ for $1^{\circ}C/min$ to $0.839MN/m^{1.5}$ for $10^{\circ}C/min$ for the hot concrete and from $0.792MN/m^{1.5}$ for $1^{\circ}C/min$ to $0.743MN/m^{1.5}$ for $10^{\circ}C/min$ for the cold concrete after an exposure time of 16 hours. The increase in cooling rate also slightly decreased $K_{IC}$, and at $450^{\circ}C$ $K_{IC}$ decreased from $0.771MN/m^{1.5}$ for slow cooling to $0.739MN/m^{1.5}$ for fast cooling after an exposure time of 16 hours. The fracture energy-based fracture toughness $K_{IC}$' was also assessed, and similar decrease trends with the heating temperature and exposure time existed for both hot and cold concretes. The relationships of two fracture toughness parameters with the weight loss and the modulus of rapture were also evaluated.

키워드

참고문헌

  1. Bazant, Z.P. (1984), "Size effect in blunt fracture: Concrete rock and metal", ASCE J. Eng. Mech., 110(4), 518-535. https://doi.org/10.1061/(ASCE)0733-9399(1984)110:4(518)
  2. Bazant, Z.P. and Oh, B.H. (1983), "Crack band theory for fracture of concrete", RILEM Mater. Struct., 16(93), 155-177.
  3. Bazant, Z.P., Kim, J.K. and Pfeiffer, P.A. (1986), "Nonlinear fracture properties from size effect tests", ASCE J. Struct. Eng., 112(2), 289-307. https://doi.org/10.1061/(ASCE)0733-9445(1986)112:2(289)
  4. Dong, W., Wu, Z. and Zhou, X. (2013), "On fracture process zone and crack extension resistance of concrete based on initial fracture toughness", Constr. Build. Mater., 49(12), 352-363. https://doi.org/10.1016/j.conbuildmat.2013.08.041
  5. Dong, W., Wu, Z., Zhou, X. and Wang, C. (2016), "A comparative study on two stress intensity factor-based criteria for prediction of mode-I crack propagation in concrete", Eng. Fract. Mech., 158, 39-58. https://doi.org/10.1016/j.engfracmech.2016.02.051
  6. Gettu, R., Bazant, Z.P. and Karr, M.E. (1990), "Fracture properties and brittleness of high-strength concrete", ACI Mater. J., 87(6), 608-618.
  7. Hamoush, S.A., Abdel-Fattah, H. and McGinley, M.W. (1998), "Residual fracture toughness of concrete exposed to elevated temperature", ACI Mater. J., 95(6), 689-694.
  8. Hillerborg, A., Modeer, M. and Petersson, P.E. (1976), "Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements", Cement Concrete Res., 6(6), 773-782. https://doi.org/10.1016/0008-8846(76)90007-7
  9. Ince, R. (2010), "Determination of concrete fracture parameters based on two-parameter and size effect models using split-tension cubes", Eng. Fract. Mech., 77, 2233-2250. https://doi.org/10.1016/j.engfracmech.2010.05.007
  10. Kaplan, M.F. (1961), "Crack propagation and the fracture of concrete", ACI J., 58(5), 591-610.
  11. Karihaloo, B.L. and Nallathambi, P. (1989), "An improved effective crack model for the determination of fracture toughness of concrete", Cement Concrete Res., 19, 603-610. https://doi.org/10.1016/0008-8846(89)90012-4
  12. Nallathambi, P., Karihaloo, B.L. and Heaton, B.S. (1984), "Effect of specimen and crack sizes, water/cement ratio and coarse aggregate texture upon fracture toughness of concrete", M. Concrete Res., 36(129), 227-236. https://doi.org/10.1680/macr.1984.36.129.227
  13. Phillips, D.V. and Zhang, B. (1993), "Direct tension tests on notched and un-notched plain concrete specimens", M. Concrete Res., 45, 25-35. https://doi.org/10.1680/macr.1993.45.162.25
  14. Prokoski, G. (1995), "Fracture toughness of concrete at high temperature", J. Mater. Sci., 30, 1609-1612. https://doi.org/10.1007/BF00375272
  15. RILEM Technical Committee 89 FME (1990a), "Draft recommendation: Determination of fracture parameters ($K^{5}_{IC}$ and $CTOD_c$) of plain concrete using three-point bend tests", RILEM Mater. Struct., 23, 457-460. https://doi.org/10.1007/BF02472029
  16. RILEM Technical Committee 89 FME (1990b), "Draft recommendation: Size-effect method for determining fracture energy and process zone size of concrete", RILEM Mater. Struct., 23, 461-465. https://doi.org/10.1007/BF02472030
  17. Shah, S.P. (1990), "Experimental methods for determining fracture process zone and fracture parameters", Eng. Fract. Mech., 35(1/2/3), 3-14. https://doi.org/10.1016/0013-7944(90)90178-J
  18. Wu, Z., Rong, H., Zheng, J. and Dong, W. (2013), "A numerical method for mixed I-II crack propagation in concrete", ASCE J. Eng. Mech., 139(11), 1530-1538. https://doi.org/10.1061/(ASCE)EM.1943-7889.0000594
  19. Wu, Z., Rong, H., Zheng, J., Xu, F. and Dong, W. (2011), "An experimental investigation on the FPZ properties in concrete using digital image correlation technique", Eng. Fract. Mech., 78(17), 2978-2990. https://doi.org/10.1016/j.engfracmech.2011.08.016
  20. Xu, S. and Reinhardt, H.W. (1999a), "Determination of double-K criterion for crack propagation in quasibrittle materials. Part I: Experimental investigation of crack propagation", J. Fract., 98, 111-149. https://doi.org/10.1023/A:1018668929989
  21. Xu, S. and Reinhardt, H.W. (1999b), "Determination of double-K criterion for crack propagation in quasibrittle materials. Part II: Analytical evaluating and practical measuring methods for three-point bending notched beams", J. Fract., 98, 151-177. https://doi.org/10.1023/A:1018740728458
  22. Xu, S. and Reinhardt, H.W. (1999c), "Determination of double-K criterion for crack propagation in quasibrittle materials. Part III: Compact tension specimens and wedge splitting specimens", J. Fract., 98, 179-193. https://doi.org/10.1023/A:1018788611620
  23. Xu, S. and Reinhardt, H.W. (2000), "A simplified method for determining double-K fracture parameters for three-point bending tests", J. Fract., 104, 181-209. https://doi.org/10.1023/A:1007676716549
  24. Yu, K. and Lu, Z. (2014), "Determining residual double-K fracture toughness of post-fire concrete using analytical and weight function method", Mater. Struct., 47(5), 839-852. https://doi.org/10.1617/s11527-013-0097-2
  25. Zhang, B. (2011), "Effects of moisture evaporation (weight loss) on fracture properties of high performance concrete subjected to high temperatures", Fire Safety J., 46, 543-549. https://doi.org/10.1016/j.firesaf.2011.07.010
  26. Zhang, B. and Bicanic, N. (2002) "Residual fracture toughness of normal- and high-strength gravel concrete after heating to $600^{\circ}C$", ACI Mater. J., 99(3), 217-226.
  27. Zhang, B., Bicanic, N., Pearce, C.J. and Balabanic, G. (2000), "Residual fracture properties of normal- and high-strength concrete subject to elevated temperatures", M. Concrete Res., 52(2), 123-136. https://doi.org/10.1680/macr.2000.52.2.123
  28. Zhang, B., Bicanic, N., Pearce, C.J. and Phillips, D.V. (2002) "Relationship between brittleness and moisture loss of concrete exposed to high temperatures", Cement Concrete Res., 32, 363-371. https://doi.org/10.1016/S0008-8846(01)00684-6
  29. Zhang, B., Cullen, M. and Kilpatrick, T. (2014) "Fracture toughness of high performance concrete subjected to elevated temperatures Part 1 The effects of heating temperatures and testing conditions (hot and cold)", Adv. Concrete Constr., 2(2), 145-162. https://doi.org/10.12989/acc.2014.2.2.145
  30. Zhang, B., Cullen, M. and Kilpatrick, T. (2016), "Spalling of heated high performance concrete due to thermal and hygric gradients", Adv. Concrete Constr., 4(1), 1-14. https://doi.org/10.12989/acc.2016.4.1.001