Effects of relining materials on the flexural strength of relined thermoplastic denture base resins

  • Sun, Yunhan (Department of Medicine, Graduate School, Korea University) ;
  • Song, So-Yeon (Department of Biomedical Sciences, Graduate School, Korea University) ;
  • Lee, Ki-Sun (Department of Prosthodontics, Korea University Guro Hospital) ;
  • Park, Jin-Hong (Department of Prosthodontics, Korea University Guro Hospital) ;
  • Ryu, Jae-Jun (Department of Prosthodontics, Korea University Guro Hospital) ;
  • Lee, Jeong-Yol (Department of Prosthodontics, Korea University Guro Hospital)
  • Received : 2017.12.28
  • Accepted : 2018.08.22
  • Published : 2018.10.31

Abstract

PURPOSE. The aim of this study was to evaluate the effects of relining materials on the flexural strength of relined thermoplastic denture base resins (TDBRs). MATERIALS AND METHODS. For shear bond strength testing, 120 specimens were fabricated using four TDBRs (EstheShot-Bright, Acrytone, Valplast, Weldenz) that were bonded with three autopolymerizing denture relining resins (ADRRs: Vertex Self-Curing, Tokuyama Rebase, Ufi Gel Hard) with a bond area of 6.0 mm in diameter and were assigned to each group (n=10). For flexural strength testing, 120 specimens measuring $64.0{\times}10.0{\times}3.3mm$ (ISO-1567:1999) were fabricated using four TDBRs and three ADRRs and were assigned to each group (n=10). The thickness of the specimens measured 2.0 mm of TDBR and 1.3 mm of ADRR. Forty specimens using four TDBRs and 30 specimens using ADRRs served as the control. All specimens were tested on a universal testing machine. For statistical analysis, Analysis of variance (ANOVA) with Tukey's test as post hoc and Spearman's correlation coefficient analysis (P=.05) were performed. RESULTS. Acry-Tone showed the highest shear bond strength, while Weldenz demonstrated the lowest bond strength between TDBR and ADRRs compared to other groups. EstheShot-Bright exhibited the highest flexural strength, while Weldenz showed the lowest flexural strength. Relined EstheShot-Bright demonstrated the highest flexural strength and relined Weldenz exhibited the lowest flexural strength (P<.05). Flexural strength of TDBRs (P=.001) and shear bond strength (P=.013) exhibited a positive correlation with the flexural strength of relined TDBRs. CONCLUSION. The flexural strength of relined TDBRs was affected by the flexural strength of the original denture base resins and bond strength between denture base resins and relining materials.

Keywords

References

  1. Takabayashi Y. Characteristics of denture thermoplastic resins for non-metal clasp dentures. Dent Mater J 2010;29:353-61. https://doi.org/10.4012/dmj.2009-114
  2. Goiato MC, Santos DM, Haddad MF, Pesqueira AA. Effect of accelerated aging on the microhardness and color stability of flexible resins for dentures. Braz Oral Res 2010;24:114-9. https://doi.org/10.1590/S1806-83242010000100019
  3. Yunus N, Rashid AA, Azmi LL, Abu-Hassan MI. Some flexural properties of a nylon denture base polymer. J Oral Rehabil 2005;32:65-71. https://doi.org/10.1111/j.1365-2842.2004.01370.x
  4. Katsumata Y, Hojo S, Hamano N, Watanabe T, Yamaguchi H, Okada S, Teranaka T, Ino S. Bonding strength of autopolymerizing resin to nylon denture base polymer. Dent Mater J 2009;28:409-18. https://doi.org/10.4012/dmj.28.409
  5. Kasumata Y, Hojo S, Ino S, Hamano N, Watanabe T, Suzuki Y, Ikeya H, Morino T, Toyoda M. Mechanical characterization of a flexible nylon denture base material. Bull Kanagawa Dent Coll 2007;35:177-82.
  6. Takahashi Y, Hamanaka I, Shimizu H. Effect of thermal shock on mechanical properties of injection-molded thermoplastic denture base resins. Acta Odontol Scand 2012;70:297-302. https://doi.org/10.3109/00016357.2011.600719
  7. Fueki K, Ohkubo C, Yatabe M, Arakawa I, Arita M, Ino S, Kanamori T, Kawai Y, Kawara M, Komiyama O, Suzuki T, Nagata K, Hosoki M, Masumi S, Yamauchi M, Aita H, Ono T, Kondo H, Tamaki K, Matsuka Y, Tsukasaki H, Fujisawa M, Baba K, Koyano K, Yatani H. Clinical application of removable partial dentures using thermoplastic resin-part I: definition and indication of non-metal clasp dentures. J Prosthodont Res 2014;58:3-10. https://doi.org/10.1016/j.jpor.2013.12.002
  8. Fueki K, Ohkubo C, Yatabe M, Arakawa I, Arita M, Ino S, Kanamori T, Kawai Y, Kawara M, Komiyama O, Suzuki T, Nagata K, Hosoki M, Masumi S, Yamauchi M, Aita H, Ono T, Kondo H, Tamaki K, Matsuka Y, Tsukasaki H, Fujisawa M, Baba K, Koyano K, Yatani H. Clinical application of removable partial dentures using thermoplastic resin. Part II: Material properties and clinical features of non-metal clasp dentures. J Prosthodont Res 2014;58:71-84. https://doi.org/10.1016/j.jpor.2014.03.002
  9. Takahashi H, Kawada E, Tamaki Y, Teraoka F, Hosoi T, Yoshida T. Basic properties of thermoplastic resins for denture base material referred to non-clasp denture. J Jpn Dent Mater 2009;28:161-7.
  10. Hamanaka I, Takahashi Y, Shimizu H. Mechanical properties of injection-molded thermoplastic denture base resins. Acta Odontol Scand 2011;69:75-9. https://doi.org/10.3109/00016357.2010.517557
  11. Arena CA, Evans DB, Hilton TJ. A comparison of bond strengths among chairside hard reline materials. J Prosthet Dent 1993;70:126-31. https://doi.org/10.1016/0022-3913(93)90006-A
  12. Takahashi Y, Chai J. Shear bond strength of denture reline polymers to denture base polymers. Int J Prosthodont 2001; 14:271-5.
  13. Chai J, Takahashi Y, Kawaguchi M. The flexural strengths of denture base acrylic resins after relining with a visible-light-activated material. Int J Prosthodont 1998;11:121-4.
  14. Arima T, Murata H, Hamada T. Analysis of composition and structure of hard autopolymerizing reline resins. J Oral Rehabil 1996;23:346-52. https://doi.org/10.1111/j.1365-2842.1996.tb00863.x
  15. Hamanaka I, Shimizu H, Takahashi Y. Shear bond strength of an autopolymerizing repair resin to injection-molded thermoplastic denture base resins. Acta Odontol Scand 2013;71: 1250-4. https://doi.org/10.3109/00016357.2012.757645
  16. Hamanaka I, Shimizu H, Takahashi Y. Bond strength of a chairside autopolymerizing reline resin to injection-molded thermoplastic denture base resins. J Prosthodont Res 2017;61: 67-72. https://doi.org/10.1016/j.jpor.2016.04.006
  17. da Cruz Perez LE, Machado AL, Canevarolo SV, Vergani CE, Giampaolo ET, Pavarina AC. Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin. Gerodontology 2010;27:62-9. https://doi.org/10.1111/j.1741-2358.2009.00292.x
  18. Takahashi Y, Kawaguchi M, Chai J. Flexural strength at the proportional limit of a denture base material relined with four different denture reline materials. Int J Prosthodont 1997;10:508-12.
  19. Archadian N, Kawano F, Ohguri T, Ichikawa T, Matsumoto N. Flexural strength of rebased denture polymers. J Oral Rehabil 2000;27:690-6. https://doi.org/10.1046/j.1365-2842.2000.00552.x
  20. Seo RS, Murata H, Hong G, Vergani CE, Hamada T. Influence of thermal and mechanical stresses on the strength of intact and relined denture bases. J Prosthet Dent 2006;96: 59-67. https://doi.org/10.1016/j.prosdent.2006.05.007
  21. Reis JM, Vergani CE, Pavarina AC, Giampaolo ET, Machado AL. Effect of relining, water storage and cyclic loading on the flexural strength of a denture base acrylic resin. J Dent 2006; 34:420-6. https://doi.org/10.1016/j.jdent.2005.10.001

Cited by

  1. Flexural strength of polymethyl methacrylate copolymers as a denture base resin vol.38, pp.4, 2018, https://doi.org/10.4012/dmj.2018-393