Abstract
Although the interest in NBR has been increasing due to the recent developments of the aerospace sector, there are few reports on HNBR's aeronautical oil, particularly evaluations of the accelerated life of harsh factors. In this study, the tensile strength was adopted as a performance evaluation factor to evaluate the accelerated life of HNBR used in the aviation field. The accelerated stress factor affecting the performance-aging characteristics was defined as temperature. The acceleration stress factor was determined to be temperature, and the result of measuring the tensile strength change over time. The sample for the acceleration condition was taken out of the oven for a certain period and left at room temperature for 24 hours. The dumbbell type 3 specimens were manufactured according to the standard specified in KS M 6518 and were measured the tensile strength, a factor in accelerated life evaluations. The activation energy was 0.895, and the shape parameter was 1.152 using the Arrhenius model. The characteristic life obtained from the tensile strength of the HNBR specimen immersed in aviation oil at 20℃ was 272,256 hours; the average life was 258,965 hours, and the B10 life was 38,624 hours.
최근 우주 항공 분야 발전으로 인해 NBR에 대한 관심이 높아지고 있으나, HNBR의 항공용 윤활유 관련 연구는 많지 않고, 특히 가혹인자들에 대한 가속수명 평가는 그렇게 많이 보고되지 않고 있다. 본 연구에서는 항공분야에 사용되는 HNBR(Hydrogenated Acrylonitrile Butadiene Rubber) 제품의 가속수명을 평가하기 위해 성능평가 인자로 인장강도를 채택하고, 성능 노화특성에 영향을 미치는 가속 스트레스 인자를 온도로 정의했다. 가속 스트레스 인자는 온도(60 ℃, 80 ℃, 100 ℃)로 정하여 시간(0 ~ 720시간)에 따른 인장강도 변화를 측정한 결과값으로 결정했다. 가속 조건은 일정 기간 동안 노화된 시편을 오븐에서 꺼내어 24시간 상온에서 방치한 후, 시험편을 KS M 6518에 명시된 기준에 따라 아령형 3호 시편을 제작하여 가속수명 평가의 한 요소인 인장강도를 측정하였다. 아레니우스 모델을 이용하여 얻어진 활성화 에너지 값은 0.895임을 알 수 있고, 형상모수는 1.152이었으며, 20℃에서 항공용 오일에 침지한 HNBR 시편의 인장강도로부터 얻어진 특성수명은 272,256시간, 평균수명(MTTF)는 258,965시간, B10 수명은 38,624시간이었다.