• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.11
• /
• pp.925-928
• /
• 2011

Perovskite niobates and tantalates have been placed on a short list of functional materials for future technologies. This article was investigated ferroelectric materials $Ag(Ta,Nb)O_3$ thick film. In this study, we have fabricated the $Ag(Ta,Nb)O_3$ thick film on the $Al_2O_3$ substrates by screen printing method. The $Ag(Ta,Nb)O_3$ thick film were fabricated by the mixed oxide method. The sintering temperature and time were 1,150$^{\circ}C$, 2 hr. The electrical properties of $Ag(Ta,Nb)O_3$ thick film were investigated at 30~100$^{\circ}C$.

• Journal of Sensor Science and Technology
• /
• v.24 no.1
• /
• pp.41-46
• /
• 2015

In this work, pure hierarchical ZnO structure was prepared using a simple hydrothermal method, and Ag nanoparticles doped hierarchical ZnO structure was synthesized uniformly through photochemical route. The reduced graphene oxide (rGO) has been synthesized by typical Hummer's method and reduced by hydrazine. Prepared Ag/ZnO nanostructures are uniformly dispersed on the surface of rGO sheets using ultrasonication process. The synthesized samples were characterized by SEM, TEM, EDS, XRD and PL spectra. The average size of prepared ZnO microspheres was around $2{\sim}3{\mu}m$ and showed highly uniform. The average size of doped-Ag nanoparticles was 50 nm and decorated into ZnO/rGO network. The $C_2H_2$ gas sensing properties of as-prepared products were investigated using resistivity-type gas sensor. Ag/ZnO-rGO based sensors exhibited good performances for $C_2H_2$ gas in comparison with the Ag/ZnO. The $C_2H_2$ sensor based on Ag/ZnO-rGO had linear response property from 3~1000 ppm of $C_2H_2$ concentration at working temperature of $200^{\circ}C$. The response values with 100 ppm $C_2H_2$ at $200^{\circ}C$ were 22% and 78% for Ag/ZnO and Ag/ZnO-rGO, respectively. In additions, the sensor still shows high sensitivity and quick response/recovery to $C_2H_2$ under high relative humidity conditions. Moreover, the device shows excellent selectivity towards to $C_2H_2$ gas at optimal working temperature of $200^{\circ}C$.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.84-89
• /
• 2014

In this work, Ag-$TiO_2$ nanocomposites were prepared via the sonochemical deposition of Ag nanometals on $TiO_2$ nanoparticles. The size of deposited Ag nanometals was ranged in 1~3 nm and the number of Ag nanometals deposited on $TiO_2$ increased in proportion to the dosage amounts of Ag precursors. As-prepared Ag-$TiO_2$ was loaded on the sterilized agar plate together with an aliquot volume of diluted E-coli, followed by 30 min irradiation of the solar simulated light ($600{\sim}1800{\mu}w/cm^2$). Finally, the agar plate was incubated for 24 h at $37^{\circ}C$ and the number of survived colonies were counted. It was experimentally confirmed that Ag-$TiO_2$ exhibited the higher antimicrobial activity than that of pure $TiO_2$, based on measuring the colony number of control sample. The survived colony numbers on the agar plate decreased with the increase of dosage amounts of Ag-$TiO_2$ and the irradiated intensity of solar simulated light for 30 min before incubating. The increase of Ag nanometal doposition induced the progressive enhancement of antimicrobial activity, but rather reduced the photocatalytic activity of Ag-$TiO_2$ probably due to the excessive presence of Ag nanometals on $TiO_2$ matrix.

• Composites Research
• /
• v.24 no.3
• /
• pp.17-24
• /
• 2011

The EAM simulation of nanoindentation was performed to investigate misfit dislocation slip in the Ag/Cu. The film layer, whose thickness in the range of 2-5nm, was indented by a spherical indenter with the N$\'{o}$se-Hoover thermostat condition. The simulation shows that the indentation position relative to misfit dislocation (MFD) has the effect on the dislocation, glide up or cross slip, for Ag film layer thickness less than 4 nm. Elastic energy variation during MFDs slip was revealed to be a key factor for the softening of Ag/Cu. The critical film layer thickness was evaluated for each case of Ag/Cu according to the spline extrapolation technique.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.3
• /
• pp.200-207
• /
• 2011

Abstract: The effect of lead free glass frit compositions on the properties of thick film conductor and resistor pastes were investigated. Two types lead free frits, HBF-A(without $Bi_2O_3$) and HBF-B(with $Bi_2O_3$) were made from $SiO_2$, $B_2O_3$, $Al_2O_3$, CaO, MgO, $Na_2O$, $K_2O$, ZnO, MnO, $ZrO_2$, $Bi_2O_3$. And Ag based conductor pastes and $RuO_2$ based resistor paste were prepared by mixed with these frits and functional phase(Ag and $RuO_2$), and organic vehicle. The properties of thick film conductor and resistor sintered at $850^{\circ}C$ were studied after printing on $Al_2O_3$ substrate. The morphology of the sintered films surface were SEM and EDS were carried out to analysis the chemical composition on resistor surface and state of Ru atom in frit matrix.

• Journal of the Microelectronics and Packaging Society
• /
• v.24 no.2
• /
• pp.69-74
• /
• 2017

Effect of post-annealing treatment times at $200^{\circ}C$ on the peel strength of screen-printed Ag film/polyimide substrate were systematically investigated by $180^{\circ}$ peel test for thermal reliability assessment of printed interconnect. Initial peel strength around 16.7 gf/mm increased up to 29.4 gf/mm after annealing for 24hours, and then sharply decreased to 22.3, 3.6, 0.6, and 0.1 gf/mm after 48, 100, 250, and 500 hours, respectively. Ag-O-C chemical bonding as well as binder organic bridges formations seemed to be responsible for interfacial adhesion improvement after the initial annealing treatment, while excessive Cu oxide formation at Cu/Ag interface seems to be closely related to sharp decrease in peel strength for longer annealing times.

• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1104-1109
• /
• 2001

Samples with the nominal composition, B $i_{1.84}$P $b_{0.34}$S $r_{1.91}$C $a_{2.03}$C $u_{3.06}$ $O_{10+}$$\delta$/ high $T_{c}$ superconductors containing As as an additive were fabricated by a solid-state reaction method. Samples with Ag of 10wt%, 30 wt% and 50 wt% each were sintered at 86$0^{\circ}C$~875$^{\circ}C$ for 24 hours. The structural characteristics, critical temperature and grain size with respect to Ag contents were analyzed by XRD(X-ray Diffraction) and SEM(Scanning Electron Microscope), respectively. As Ag contents increased, XRD peaks of g in Bi-2223 phase superconductors intensified and the proportion of the phase transition from Bi-2223 to Bi-2212 was increased.increased.

• Journal of the Korean Ceramic Society
• /
• v.39 no.9
• /
• pp.846-850
• /
• 2002

A PMN-PT-BT/Ag composite was prepared by surface modification with MgO sol with hoping to suppress silver's migration during sintering. The mixture of PbO, $N_2O_5,\;TiO_2\;with\;Mg(NO_3)_2$ instead of MgO was ball milled, the solvent was removed and then the dried powders were calcined at 950$^{\circ}C$/1h. The calcined powder were treated with 3.0 mol% $Ag_2O$ and 1.0 wt% MgO sol and calcined at 550$^{\circ}C$/1h. The dielectrics sintered at 1000$^{\circ}C$/4h under a flowing oxygen showed the density of 7.84g/$cm^3$, the room temperature dielectric constant of 18400, the dielectric loss of 2.4%, the specific resistivity of $0.24{\times}10^{12}{\Omega}{\cdot}cm$. It also showed the bending strength of $120.7{\pm}11.26$ MPa and the fracture toughness of $0.87{\pm}0.002\;MPam^{1/2}$ which were comparable to commercial PZT. The microstructure sonsisted of grains of ∼4${\mu}m$. SEM and SIMS analysis showed that Ag grew as ∼1${\mu}m$ and excess MgO as ∼0.5${\mu}m$.

• Journal of the Korean Ceramic Society
• /
• v.22 no.3
• /
• pp.19-24
• /
• 1985

The phtoelectrochemical porperties of $Nb_2O_5$, $Sb_2O_3$ and $V_2O_5$ doped and pure $SrTiO_3$ ceramic electodes were investigated. Shapes of I-V and I-λ characteristics of the pure $SrTiO_3$ ceramic electrode are similar to those of SrTiO3 single crystal electorde ; the anodic current strats at -0.9V (vs. Ag/AgCI) in 1 N-NaOH aqueous solution and the photoresponse appears at a wavelength of about 390nm and the quantum efficiency is about 3.5% at wavelength of 390nm under 0.5V vs. Ag/AgCl. Photocurrents of $Nb_2O_5$, $Sb_2O_3$ and $V_2O_5$ doped electrodes and $V_2O_5$ doped ceramic electrode appears at wavelength of 390nm and 500nm respectively.

• Journal of the Korean Society for Heat Treatment
• /
• v.28 no.3
• /
• pp.134-138
• /
• 2015

Ag intermediated $TiO_2$ films were deposited by RF and DC magnetron sputtering and then vacuum annealed at 100, 200 and $300^{\circ}C$ for 30 minutes to investigate the effect of annealing temperature on the structural and optical properties of the films. For all depositions, the thickness of the $TiO_2$ and Ag films were kept constant at 24 and 15 nm by controlling the deposition time. As-deposited $TiO_2/Ag/TiO_2$ trilayer films have a weak crystalline and an optical reflectance in a near infrared wavelength region of 77.8%, while the films annealed at $300^{\circ}C$ show the polycrystalline structure and an increased mean optical reflectance of 80.4%. From the experimental results, it can be concluded that increasing the annealing temperature enhanced the structural and optical properties of the $TiO_2/Ag/TiO_2$ films.