• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.398-402
• /
• 2000

Three kinds of $Al_3Ti-Cr$ alloys, namely, $Al_{67}Ti_{25}Cr_8,\;Al_{66}Ti_{24}Cr_{10}\;and\;Al_{59}Ti_{26}Cr_{15}$, were prepared by induction melting followed by the thermomechanical treatment. The corrosion behavior in 3.5% NaCl solution and the high-temperature oxidation behavior at 1000, 1100 and $1200^{\circ}C$ for the prepared alloys were investigated. Electrochemical results indicated increased resistance to localized corrosion with increasing Cr content. Cr additions were found to prevent passive film from undergoing brittle fracture. XPS results revealed the passive films of $Al_3Ti-Cr$ alloys were composed mainly of $Al_2O_3$ that coexisted with $TiO_2$ and $Cr_2O_3$. The overall oxidation resistance of the prepared alloys were excellent. Specifically, the oxidation resistance increased in the order of $Al_{59}Ti_{26}Cr_{15},\;Al_{66}Ti_{24}Cr_{10}\;and\;Al_{67}Ti_{25}Cr_8$. As the Al content in the base alloys increased, the $Al_2O_3$ formation was facilitated leading to the increased oxidation resistance.

• The Journal of Korean Academy of Prosthodontics
• /
• v.47 no.1
• /
• pp.39-45
• /
• 2009

Statement of problem: Recently precalcification treatment has been studied to shorten the period of the implant. Purpose: This study was performed to evaluate the effect of precalcification treatment of $TiO_2$ Nanotube formed on Ti-6Al-4V Alloy. Material and methods: Specimens of $20{\times}10{\times}2\;mm$ in dimensions were polished sequentially from #220 to #1000 SiC paper, ultrasonically washed with acetone and distilled water for 5 min, and dried in an oven at $50^{\circ}C$ for 24 hours. The nanotubular layer was processed by electrochemical anodic oxidation in electrolytes containing 0.5 M $Na_2SO_4$ and 1.0 wt% NaF. Anodization was carried out using a regulated DC power supply (Kwangduck FA, Korea) at a potential of 20 V and current density of $30\;㎃/cm_2$ for 2 hours. Specimens were heat-treated at $600^{\circ}C$ for 2 hours to crystallize the amorphous $TiO_2$ nanotubes, and precalcified by soaking in $Na_2HPO_4$ solution for 24 hours and then in saturated $Ca(OH)_2$ solution for 5 hours. To evaluate the bioactivity of the precalcified $TiO_2$ nanotube layer, hydroxyapatite formation was investigated in a Hanks' balanced salts solution with pH 7.4 at $36.5^{\circ}C$ for 2 weeks. Results: Vertically oriented amorphous $TiO_2$ nanotubes of diameters 48.0 - 65.0 ㎚ were fabricated by anodizing treatment at 20 V for 2 hours in an 0.5 M $Na_2SO_4$ and 1.0 NaF solution. $TiO_2$ nanotubes were composed with strong anatase peak with presence of rutile peak after heat treatment at $600^{\circ}C$. The surface reactivity of $TiO_2$ nanotubes in SBF solution was enhanced by precalcification treatment in 0.5 M $Na_2HPO_4$ solution for 24 hours and then in saturated $Ca(OH)_2$ solution for 5 hours. The immersion in Hank's solution for 2 weeks showed that the intensity of $TiO_2$ rutile peak increased but the surface reactivity decreased by heat treatment at $600^{\circ}C$. Conclusion: This study shows that the precalcified treatment of $TiO_2$ Nanotube formed on Ti-6Al-4V Alloy enhances the surface reactivity.

• Korean Journal of Materials Research
• /
• v.2 no.5
• /
• pp.313-319
• /
• 1992

The mechanisms of fatigue crack growth (FCG) in a Ti$_3$Al-based (${\alpha}_2$) alloy, Ti-24Al-11Nb (a/o) with acicular microstructure were studied with particular attention focused on the fatigue crack path through the microstructure and on the effects of specimen orientation and crack closure. The results showed that the fatigue cracks of Ti-24Al-11Nb alloy grew much faster than conventional titanium alloys, with little difference in FCG rates for TL and TS orientations. The fatigue crack paths revealed crystallographic transgranular fracture with frequent serrations and branching. This is in agreement with the known effects of slip planarity and microstructure on the FCG behavior. The load-displacement hysteresis loops showed that the crack closure influenced the FCG behavior.

• Journal of the Korean Ceramic Society
• /
• v.34 no.6
• /
• pp.629-635
• /
• 1997

The effects of the annealing atmospheres(O2, N2) and sintering additives that Bi2O3 is a major composition on the microwave dielectric and sintering propertie of (1-x)CaTiO3-xLaAlO3 system were investigated. The annealing atmospheres and the increase of annealing time after sintering did not affect the relative dielectric constant($\varepsilon$r) and temperature coefficient of resonant frequency($\tau$f) of (1-x)CaTiO3-xLaAlO3 system. However, the Q.f0 values of (1-x)CaTiO3-xLaAlO3 were very sensitive to annealing atmospheres. As the annealing time increased under O2 atmosphere the Q.f0 values of (1-x)CaTiO3-xLaAlO3 enhanced untill 10 hrs in 0.3$\leq$x$\leq$0.6 region, but degraded over that time. The increasing rate of Q.f0 value increased wth increasing x. On the other hand, as the annealing time increased under N2 atmosphere the Q.f0 values were constant in x$\leq$0.6 region, increased gradually in x$\geq$0.7 region. When 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% as sintering additives were added to (Ca0.5La0.5) (Ti0.5Al0.5)O3 (x=0.5) the sintering temperature of 1$600^{\circ}C$ was lowered to 140$0^{\circ}C$, and the relative dielectric constant($\varepsilon$r) and temperature coefficient of resonant frequency($\tau$f) were not nearly changed. The addition of 0.97Bi2O3-0.03Al2O3 and 0.76Bi2O3-0.24NiO of 3wt% to (Ca0.5La0.5)(Ti0.5Al0.5)O3 made the Q.f0 values to be lower about 15% and 34%, respectively.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.660-664
• /
• 2000

Effect of various kinds of additive such as AlOOH, Al(OH)3, Al2Si2O5(OH)4, Nb2O5, TiO2 and MgO on the properties and microstructures of UO2 pellet has been examined. All the tested dopants had played a role to reduce sintered density and open porosity. It was revealed that the addition of TiO2 made pellet more stable thermally. UO2 pellet doped with 0.2wt% TiO2 was swelled rather than densified after annealing for 24 hrs at 1$700^{\circ}C$. It was attributed to large pore with spherical shape. Titinia and silicon coexisted with Al element were more effective to increase grain size than other additives. It could be also revealed that the formation of liquid phase was the main cause of grain growth.

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.4
• /
• pp.451-463
• /
• 2004

The performance of disk-type catalytic filters impregnated by TiO$_2$ or TiO$_2$-3Al$_2$O$_3$ㆍ 2SiO$_2$ supports and V$_2$O$_{5}$ catalyst was evaluated for selective catalytic reduction (SCR) of NO with ammonia as a reductant. XRD, FT -IR, BET and SEM were used to characterize the catalytic filters prepared in this work. Optimal V$_2$O$_{5}$ loading and reaction temperature for V$_2$O$_{5}$/TiO$_2$ catalytic filters were 3-6 wt.% and 350-40$0^{\circ}C$ at GHSV 14,300 $hr^{-1}$ in the presence of oxygen, respectively. With increasing the V$_2$O$_{5}$ loading from 0.5 to 6 wt%, NO conversion increased from 24 to 96% at 40$0^{\circ}C$ and 14.300$hr^{-1}$, and maintained at 80% over in the V$_2$O$_{5}$ loading range of 3-6 wt.% and then dropped at V$_2$O$_{5}$ loading of 7wt.% over. In comparing V$_2$O$_{5}$/ TiO$_2$ and V$_2$O$_{5}$/ TiO$_2$-3Al$_2$O$_3$ㆍ2SiO$_2$ catalytic fillers, which have same 3wt.% V$_2$O$_{5}$ loading, the V$_2$O$_{5}$/ TiO$_2$-3A1$_2$O$_3$ㆍ2SiO$_2$ catalytic filter showed higher activity than V$_2$O$_{5}$/ TiO$_2$ catalytic filter, but higher differential pressure drops owing to its low air permeability. low air permeability.

• Journal of the Korean Ceramic Society
• /
• v.22 no.2
• /
• pp.17-24
• /
• 1985

In the composition of $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ the effect of particle size on PbO vaporization were measured, . The initial step of discontinuous vaporization of unreated PbO during the calcining process was depended on the particle size. All additives $La_2O_3Nb_2O_5$ and $Al_2O_3$ inhibited the grain growth of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ +2wt% excess PbO. The dielectric and piezoelectric properties of the composition $Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$ were improved by the addition of 2wt% excess PbO and proper additive. The electromechanical planar coupling factor of 0.65 and mechnical quality factor of 390 could be obtained by adding 5wt% $Nb_2O_5$ to the composition 2wt% excess PbO+$Pb(Mg_{0.15} W_{0.15})Ti_{0.35}-Zr_{0.35}O_3$.

• Korean Journal of Materials Research
• /
• v.17 no.8
• /
• pp.447-451
• /
• 2007

We investigated the dependence of the various annealing conditions and thickness ($6\sim45nm$) of the Ti-doped $Al_2O_3$ coating on the electrochemical properties and the capacity fading of Ti-doped $Al_2O_3$ coated $LiCoO_2$ films. The Ti-doped-$Al_2O_3$-coating layer and the cathode films were deposited on $Al_2O_3$ plate substrates by RF-magnetron sputter. Microstructural and electrochemical properties of Ti-doped-$Al_2O_3$-coated $LiCoO_2$ films were investigated by transmission electron microscopy (TEM) and a dc four-point probe method, respectively. The cycling performance of Ti-doped $Al_2O_3$ coated $LiCoO_2$ film was improved at higher cut-off voltage. But it has different electrochemical properties with various annealing conditions. They were related on the microstructure, surface morphology and the interface condition. Suppression of Li-ion migration is dominant at the coating thickness >24.nm during charge/discharge processes. It is due to the electrochemically passive nature of the Ti-doped $Al_2O_3$ films. The sample be made up of Ti-doped $Al_2O_3$ coated on annealed $LiCoO_2$ film with additional annealing at $400^{\circ}C$ had good adhesion between coating layer and cathode films. This sample showed the best capacity retention of $\sim92%$ with a charge cut off of 4.5 V after 50 cycles. The Ti-doped $Al_2O_3$ film was an amorphous phase and it has a higher electrical conductivity than that of the $Al_2O_3$ film. Therefore, the Ti-doped $Al_2O_3$ coated improved the cycle performance and the capacity retention at high voltage (4.5 V) of $LiCoO_2$ films.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.50 no.5
• /
• pp.221-225
• /
• 2001

The effect of $Al_2O_3+Y_2O_3$ additives on fracture toughness of ${\beta}-SiC-TiB_2$ composites by hot-pressed sintering was investigated. The ${\beta}-SiC-TiB_2$ ceramic composites were hot-press sintered and pressureless-annealed by adding 16, 20, 24 wt% ${\beta}-SiC-TiB_2$(6:4 wt%) powder as a liquid forming additives at low temperature(1800 $^{\circ}C$) for 4 h. Phase analysis of composites by XRD revealed mostly of ${\alpha}$-SiC(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$). The relative density was over 95-88 % of the theoretical density, and the porosity increased with increasing $Al_2O_3+Y_2O_3$ contents because of the increasing tendency of pore formation. The fracture toughness showed the highest value of 5.88 MPa${\cdot}m^{1/2}$ for composites added with 20 wt% $Al_2O_3+Y_2O_3$ additives at room temperature. The electrical resistivity showed the lowest value of $5.22{\times}10^{-4}\;{\Omega}\;{\cdot}\;cm$ for composite added with 20 wt% $Al_2O_3+Y_2O_3$ additives at room temperature, and was all positive temperature coefficeint resistance(PTCR) against temperature up to 900 $^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.5
• /
• pp.406-414
• /
• 1991

The composition of base glass was selected as MgO 8, Al2O3 24, SiO2 68 in weight percent. TiO2 and ZrO2 were added to the base glass to investigate their effects as nucleating agents. In the case of ZrO2 addition, the optimum temperature for nucleation, which was related to the precipitation of tetragonal ZrO2, was 80$0^{\circ}C$. The optimum growth condition for the crystal was 87$0^{\circ}C$ for 8 hrs, and the major crystal phases precipitated in the samples were $\beta$-quartz ss. and mullite. The light transmissivity turned out to be around 80 per cent. On the other hand, when the TiO2 was added, it was difficult to determine the nucleating temperature, because the samples turned easily into translucency during the heat treatment. Therefore, it was almost impossible to retain transparency in the samples. The light transmissivity was below 30 per cent.