(Ba,Sr)$TiO_3$ thin films have attracted great interest as new dielectric materials of capacitors for ultra-large-scale integrated dynamic random access memories (ULSI-DRAMs) such as 1 Gbit or 4 Gbit. In this study, inductively coupled $BCl_3/Cl_2/Ar$ plasmas was used to etch (Ba,Sr)$TiO_3$ thin films. RF power/dc bias voltage=600 W/-250 V and chamber pressure was 10 mTorr. The $Cl_2/(Cl_2+Ar)$ was fixed at 0.2 the (Ba,Sr)$TiO_3$ thin films were etched adding $BCl_3$. The highest (Ba,Sr)$TiO_3$ etch rate is $480{\AA}/min$ at 10 % $BCl_3$ to $Cl_2/Ar$. The change of Cl, B radical density measured by optical emission spectroscopy(OES) as a function of $BCl_3$ percentage in $Cl_2/Ar$. The highest Cl radical density was shown at the addition of 10% $BCl_3$ to $Cl_2/Ar$. To study on the surface reaction of (Ba, Sr)$TiO_3$ thin films was investigated by XPS analysis. Ion bombardment etching is necessary to break Ba-O bond and to remove $BaCl_2$. There is a little chemical reaction between Sr and Cl, but Sr is removed by physical sputtering. There is a chemical reaction between Ti and Cl, and $TiCl_4$ is removed with ease. The cross-sectional of (Ba,Sr)$TiO_3$ thin film was investigated by scanning electron microscopy (SEM), the etch slope is about 65~70$^{\circ}$.

• Journal of the Korean Ceramic Society
• /
• v.35 no.7
• /
• pp.679-684
• /
• 1998

Dielectricand pyroelectric properties of {{{{ { { {Ba }_{0.67 }Sr }_{0.33 } }`TiO_{3 } ^{ } }} (BST) thin plates and films were investigated. For BST thin plates maximum dielectric constant and pyrolelectric coefficient were observed at around 24$^{\circ}C$ and pyroelectric characteristics were improved as applied bias field was increased. When the electric field of 4kV/cm was applied to the thin plates sintered at 140$0^{\circ}C$ the pyroelectric coefficients over 4$\times$10-7C/{{{{ { cm}^{2 }K }} were obtained in the range of 0-4$0^{\circ}C$ BST thin films deposited using rf magnetron sputtering showed [001] preferred orientation at substrate temperatures above 50$0^{\circ}C$ On the contrary to the thin plates the dielectric constants of the thin films gradually increased above 15$^{\circ}C$ and decreased as applied bias field in-creased. The pyroelectric coefficients of thin films were lower than 1/10 those of thin plates.