• Journal of Electrical Engineering and Technology
• /
• v.9 no.1
• /
• pp.273-279
• /
• 2014

Hexagonal Ba-ferrites are widely suggested as materials for small antennas. In this paper, the sintering behavior and magneto-electric properties of $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ ($0.1{\leq}x{\leq}0.5$) ceramics were investigated for small antenna application. All samples of $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ ceramics were prepared by the solid-state reaction method and sintered at $1250^{\circ}C$. From the XRD patterns of the sintered $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ceramics, the Z-type phases were found to be the main phases. The real part of permittivity and permeability of the $Ba_3Co_{2-2x}Mn_{2x}Fe_{24}O_{41}$ceramics decreased with frequency. On the other hand, loss tangents of permittivity and permeability tended to behave opposite to real part of permittivity and permeability. The real part of permeability was affected by Mn additions. The real part of permittivity, the loss tangent of permittivity and the real part of permeability, the loss tangent of permeability of $Ba_3Co_{0.2}Mn_{0.8}Fe_{24}O_{41}$ ceramics were 19.774, 0.176 and 15.183, 0.073, respectively, at 510 MHz. In order to investigate the effect of magneto-dielectric ceramics on antenna, PIFA (Planar Inverted F Antenna) was simulated with CST (Computer Simulation Technology). The operating frequency of antenna was decreased without considerable change of bandwidth by using the $Ba_3Co_{0.2}Mn_{0.8}Fe_{24}O_{41}$ ceramics as the carrier.

• Journal of the Korean Magnetics Society
• /
• v.18 no.2
• /
• pp.67-70
• /
• 2008

$Tb_2Bi_1Ga_xFe_{5-x}O_{12}$(x=0, 1) fabricated by sol-gel and vacuum sealed annealing process. $Tb_2Bi_1Ga_xFe_{5-x}O_{12}$(x=0, 1) have been studied by x-ray diffraction(XRD), vibrating sample magnetometer, and $M\ddot{o}ssbauer$ spectroscopy. The crystal structures were found to be a cubic garnet structure with space group Ia3d. The determined lattice constants $a_0$ of x = 0, and 1 are $12.497\AA$, and $12.465\AA$, respectively. The distribution of gallium and iron in $Tb_2Bi_1Ga_xFe_{5-x}O_{12}$ is studied by Rietveld refinement. Based on Rietveld refinement results, the terbium and bismuth ions occupy the 24c site, iron ions occupy the 24d, l6a site, and nonmagmetic gallium ions occupy the 16a site. In order to verify the magnetic site occupancy of iron and gallium, we have taken $M\ddot{o}ssbauer$ spectra for $Tb_2Bi_1Ga_xFe_{5-x}O_{12}$(x=0, 1) at room temperature. From the results of $M\ddot{o}ssbauer$ spectra analysis, the absorption area ratios of Fe ions for $Tb_2Bi_1Fe_5O_{12}$ on 24d and 16a sites are 60.8 % and 39.2 %, respectively, and the absorption area ratios of Fe ions for $Tb_2Bi_1Fe_5O_{12}$ on 24d and 16a sites are 74.7 % and 25.3 %, respectively. It is noticeable that all of the nonmagnetic Ga atoms occupy the 16a site by vacuum annealing process.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.5
• /
• pp.197-202
• /
• 2021

Synthesis of Z-type hexaferrite Ba₃Co₂Fe₂₄O₄₁ (Ba₃Z) and Ba_1.5La_1.5Co₂Fe₂₄O₄₁ (Ba_1.5La_1.5Z) powders were tried using molten salt synthesis after primary calcination. Ba₃Z calcined at 1000℃ was formed with both M-type and Y-type hexaferrite, and then Z-type was obtained when sintered with molten salt at 1150℃ and 1200℃. In the case of Ba_1.5La_1.5Z calcined at 1000℃, however, M-type hexaferrite, CoFe₂O₄ (Spinel phase), and LaFeO₃ were synthesized. As a result, Z-type hexaferrite was not synthesized after sintering with molten salt. In addition, the aspect ratio of the particles decreased as the sintering temperature increased with molten salt synthesis. To obtain a single-phase Ba_1.5La_1.5Z with a high aspect ratio, it is expected the raw materials have to calcine below the temperature of a spinel phase formation before sintering with molten salt.

• Journal of the Korean Magnetics Society
• /
• v.19 no.1
• /
• pp.12-16
• /
• 2009

Z-type barium ferrite [($Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$, $Ba_{3+{\delta}}Co_{0.8}Zn_{1.2}Fe_{24}O_{41}$ ${\delta}$ = 3, 5, 7, 13 wt%. $Ba_{3}Co_{0.8}Zn_{1.2}Fe_{24+{\delta}}O_{41}$ ${\delta}$ = 5, 7, 10 wt% )] were synthesized using co-precipitation method. The microstructure and magnetic properties of synthesized particles were investigated. In all prepared particles M-type Ba ferrite is identified with Z-type Ba ferrite together. It is found that particles having 7 wt% for Ba and 5 wt% for Fe excess addition revealed high saturation magnetization, respectively. All synthesized particles showed relatively high coercivity for device application. This result may be attributed to the contribution of M-type Ba ferrite. Ba and Fe excess addition was not affected to the structural change of CoZnZ Ba ferrite. The certain amount of excess additions of Ba and Fe and the 2 step heat-treatment may be beneficial to the improvement of soft magnetic properties of Z-type barium hexa-ferrite

• Korean Journal of Materials Research
• /
• v.24 no.8
• /
• pp.423-428
• /
• 2014

We synthesized Fe-doped $TiO_2/{\alpha}-Fe_2O_3$ core-shell nanowires(NWs) by means of a co-electrospinning method and demonstrated their magnetic properties. To investigate the structural, morphological, chemical, and magnetic properties of the samples, X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy were used, as was a vibrating sample magnetometer. The morphology of the nanostructures obtained after calcination at $500^{\circ}C$ exhibited core/shell NWs consisting of $TiO_2$ in the core region and ${\alpha}-Fe_2O_3$ in the shell region. In addition, the XPS results confirmed the formation of Fe-doped $TiO_2$ by the doping effect of $Fe^{3+}$ ions into the $TiO_2$ lattice, which can affect the ferromagnetic properties in the core region. For comparison, pure ${\alpha}-Fe_2O_3$ NWs were also fabricated using an electrospinning method. With regard to the magnetic properties, the Fe-doped $TiO_2/{\alpha}-Fe_2O_3$ core-shell NWs exhibited improved saturation magnetization(Ms) of approximately ~2.96 emu/g, which is approximately 6.1 times larger than that of pure ${\alpha}-Fe_2O_3$ NWs. The performance enhancement can be explained by three main mechanisms: the doping effect of Fe ions into the $TiO_2$ lattice, the size effect of the $Fe_2O3_$ nanoparticles, and the structural effect of the core-shell nanostructures.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.5
• /
• pp.365-372
• /
• 2000

Pure $Fe_3$Al alloys with three different compositions of Fe-21.8%Al, Fe-24.1%Al and Fe-27.2%Al were prepared by vacuum induction melting followed by homogenization and hot forging. The long-time oxidation behavior of the prepared alloys was studied at 1073, 1273 and 1473k in air. The oxidation resistance greatly increased with an increase in Al contents. Thin and uniform oxide scales were always formed on Fe-27.2%Al, while thick and fragile oxide scales were formed on Fe-(21.8, 24.1%)Al. Internal oxidation was observed in Fe-(21.8, 24.1%)Al, when oxidized above 1273K. The major oxidation product of all the oxidized alloys was always $\alpha$-$Al_2$$O_3$.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.12
• /
• pp.2270-2275
• /
• 2011

The sintering behavior and microwave properties of ferrite ($Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics) were investigated for microwave applications. Also PIFA type antenna with ferrite was simulated. All samples were prepared by the solid state reaction method and sintered at $1350^{\circ}C$. All ceramics had relatively density above of 92% compare with theoretical density of $Ba_3Co_2Fe_{24}O_{41}$ ceramics. From the XRD pattens, the Z-type phase was existed as main phase in $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics. The permittivity and permeability of $Ba_3Co_{2-2x}Zn_{2x}Fe_{24}O_{41}$ ceramics were increased with Zn additions and decreased rapidly over frequency of 200~600 MHz. Several PIFA type antennas with ferrite and FR4 were simulated. All antenna structure had return loss of less than -10 dB at each resonant frequency. Simulated antenna using both ferrite and FR4 showed size reduction of 25% without a significant decrement of efficiency.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2003.11a
• /
• pp.373-378
• /
• 2003

As a part of assessment of the structural material for the molten salt handling system, corrosion behavior of austenitic alloys, Fe-base and Ni-base in the molten salt of $LiCl-Li_2O_2$ was investigated in the range of temperature; 650~$725^{\circ}C$, time; 24- 168h, $Li_2O$; 3wt%, mixed gas; Ar-10%$O_2$. In the molten salt of $LiCl-Li_2O_2$, Ni-base alloys showed higher corrosion resistance than Fe-base alloys. Fe-base alloy with low Fe and high Ni contents exhibited better corrosion resistance. The scales of $Cr_2O_3$, $FeCr_2O_4$ on Fe-base alloys were showed, and $Cr_2O_3$, $NiFe_2O_4$ on Ni-base alloys were also showed.

• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.296-300
• /
• 1999

Cross-shape structures of spin tunneling junctions were fabricated using DC magnetron sputtering and metal masks. The film structures were $substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al_2O_3/CoFe/NiFe$ and $substrate/Ta/NiFe/CoFe/ Al_2O_3/CoFe/NiFe/FeMn/NiFe$. Fabrication conditions of insulating layer ($Al_2O_3$) and thickness and sputtering power of each film layer were varied, and maximum magnetoresistance ratio of 24.3 % was obtained. Magnetic characteristic variations in the above mentioned two structures and two types of substrates (Corning glass 7059 and Si(111)) were compared. Annealing of the junctions was performed to find out magnetic characteristic variations expected from the device fabrication. Magneoresistance Ratio were observed to maintain as-deposited value up to 150 $^{\circ}C$ annealing and then to drop rapidly after 180 $^{\circ}C$ annealing.

• Proceedings of the KIEE Conference
• /
• 2009.07a
• /
• pp.1293_1294
• /
• 2009

The sintering and high frequency electro-magnetic properties of Ba-hexagonal ferrite were investigated. All samples of the Ba-hexagonal ferrite were prepared by the conventional mixed oxide method and sintered at $1150^{\circ}C$~$1400^{\circ}C$. From the X-ray diffraction patterns of sintered Ba-hexagonal ferrite, the $Ba_3Co_2Fe_{24}O_{41}$ phase was represented as main phase in the almost sintering conditions. The bulk densities with sintering temperature and decreased at $1400^{\circ}C$. The permittivity ($\varepsilon$') and loss tangent of permittivity ($\varepsilon$"/$\varepsilon$') of $Ba_3Co_2Fe_{24}O_{41}$ ceramics increased and decreased with sintering temperature, respectively. The permeability of $Ba_3Co_2Fe_{24}O_{41}$ ceramics decreased with sinteirng temperature. The loss tangent of permeability was not changed compared each other with sintering temperature. The bulk density of $Ba_3Co_2Fe_{24}O_{41}$ ceramics sintered at $1300^{\circ}C$ was 4.79 g/$cm^3$. The permittivity, loss tangent of permittivity and permeability, loss tangent of permeability were 19.896, 0.1718 and 14.218, 0.2046 at 210 MHz, respectively.