• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.5
• /
• pp.197-202
• /
• 2021

Synthesis of Z-type hexaferrite Ba₃Co₂Fe₂₄O₄₁ (Ba₃Z) and Ba_1.5La_1.5Co₂Fe₂₄O₄₁ (Ba_1.5La_1.5Z) powders were tried using molten salt synthesis after primary calcination. Ba₃Z calcined at 1000℃ was formed with both M-type and Y-type hexaferrite, and then Z-type was obtained when sintered with molten salt at 1150℃ and 1200℃. In the case of Ba_1.5La_1.5Z calcined at 1000℃, however, M-type hexaferrite, CoFe₂O₄ (Spinel phase), and LaFeO₃ were synthesized. As a result, Z-type hexaferrite was not synthesized after sintering with molten salt. In addition, the aspect ratio of the particles decreased as the sintering temperature increased with molten salt synthesis. To obtain a single-phase Ba_1.5La_1.5Z with a high aspect ratio, it is expected the raw materials have to calcine below the temperature of a spinel phase formation before sintering with molten salt.

• Proceedings of the KIEE Conference
• /
• 1991.07a
• /
• pp.194-197
• /
• 1991

In this study, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, added $MnO_2$ (0-0.30[mol%]) ceramics were fabricated by the mixed oxide method. The sintering temperature and time were $1250[^{\circ}C]$, 2[hr], respectively. In the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens, relative dielectric constant and dielectric loss were minimum values 3.52, 0.003, respectively, and Curie temperature were highest values $256[^{\circ}C]$. Pyroelectric coefficient and voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$, and added $MnO_2$ (0.24[mol%]) specimen were good values, $6.73{\times}10^{-8}[C/cm^2K],\;125[v/W]$, respectively. Figure of merit of pyroelectric current, voltage and detectivity of the specimen, $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) were good values $2.714{\times}10^{-8}[Ccm/J],\;7.706{\times}10^{-11}[Ccm/J],\;2.640{\times}10^{-8}[Ccm/J]$, respectively. Voltage responsivity of the $(Pb_{0.99}La_{0.01})[(Sb_{1/2}Sn_{1/2})_{0.10}Ti_{0.25}Zr_{0.65}]O_3$ added $MnO_2$ (0.24[mol%]) specimens were decreased with increasing the chopper frequency.

• Journal of the Korean Chemical Society
• /
• v.38 no.4
• /
• pp.276-282
• /
• 1994

Perovskite-type mixed oxides LaBO$_3$(B = Mn, Fe, Co) were prepared by citrate sol-gel method in $air(850^{\circ}C$, 24h). The oxygen stoichiometries and structures of these oxides were determined by XRD and TPR results as followings; LaMnO$_{3.16}$(a = 5.507, c = 13.329 $\AA$, hexagonal), LaFeO$_{3.17}$(a = 5.554, b = 5.555, c = 7.863 $\AA$, orthorhomibic), LaCoO$_{3.0}$(a = 5.436, c = 13.095 $\AA$, hexagonal). The temperature programmed reduction(TPR) experiments in static 300 torr H$_2$ atmosphere shows that the reduction reaction of LaBO$_3$(B = Mn, Fe, Co) proceeds into two stages, and thermal stabilities of these oxides decreased in the order of LaMnO$_3$ > LaFeO$_3$ > LaCoO$_3$. According to the kinetic analysis the lowest activation energy was obtained for LaCoO$_3$.

• The Journal of Natural Sciences
• /
• v.15 no.1
• /
• pp.35-46
• /
• 2005

$LaFeO_3$ and substituted $LaFeO_3$ mixed oxides were prepared by Citrate and Cyanide method in air $850^{\circ}C$/24h. These oxides of orthorhombic perovskite were characterized by XRD and IR, but substituted $LaFeO_3$ with 0.5mol Cu at B site was not obtained single phase. Also, reduction reaction of un-substituted $LaFeO_3.17$ were two steps but each site substituted oxides were three steps reactions. These means that new reduction step of each site substituted oxides were atributed tot dopant.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.2
• /
• pp.63-67
• /
• 2003

Synthesis of $PbLaTiO_{3}$ : Mn powders containing La and Mn was carried out using $PbO,\;TiO_{2},\;La_{2}O_{3}\;and\;MnO_{2}$ as starting materials by hydrothermal method. In the synthesis of single phase $PbLaTiO_{3}$ : Mn powder containing La and Mn, the optimal x value corresponding to La substitution was 0.01 which corresponds to $0.99(Pb_{1-x}La_{2x/3}TiO_{3})+0.01MnO_{2}$. The optimal conditions for the preparation of the powder synthesis were 8 M-KOH solvent of hydrothermal solvent, $270^{\circ}C$ of reaction temperature and 24 hrs of run time. It was found that the synthesized powders had spherical morphology with average particle size of 70 nm and specific surface area of $5.5\;m^{2}/g$.

• Journal of the Korean Ceramic Society
• /
• v.34 no.3
• /
• pp.330-336
• /
• 1997

1:1 복합 페로스카이트 물질인 La(Mg1/2Ti1/2)O3 and La(Mg1/2Zr1/2)O3의 양이온 규칙 존재와 고주파 유전특성을 x선 회절과 회로망분석기를 사용하여 조사하였다. 기존의 연구에서는 두 물질 모두 양이온 규칙이 없으며 입방정 구조를 갖는다고 보고되었지만, 본 연구에서의 x선 분석에서는 양이온 규칙을 나타내는 초격자회절선과 비입방정 구조를 의미하는 기본회절선의 split이 발견되었다. 고주파 영역에서의 유전율은 La(Mg1/2Ti1/2)O3의 경우 29,La(Mg1/2Zr1/2)O3는 24, 품질계수(Q*f)는 각각 73000, 49000이다. 공진주파수 온도계수는 La(Mg1/2Ti1/2)O3의 경우 - 65ppm/$^{\circ}$C,La(Mg1/2Zr1/2)O3는 -80ppm/$^{\circ}$C로 음의 값을 가진다.

• Journal of the Korean Ceramic Society
• /
• v.52 no.1
• /
• pp.19-22
• /
• 2015

The joining behavior of YSZ ceramics to the glasses used in the $9Al_2O_3-24ZrO_2-51SiO_2-16R_2O$ and $9Al_2O_3-24ZrO_2-51SiO_2-7La_2O_3-9R_2O$ (wt%) glass systems was investigated. The glass transition and softening temperatures were determined to be $430^{\circ}C$ and $760^{\circ}C$, respectively. The behavior of the contact angle was inversely proportional to an increase in the temperature. The Zr element in YSZ acted as a nucleation agent and contributed to the bonding behavior at the interface.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.415-418
• /
• 2001

The I-V characteristics and its stability of ZPCCL-based ceramic varistors doped with La$_2$O$_3$in the range of 0.0~4.0 mol% were investigated. The density of ceramics was increased in the range of 4.7~5.8 g/cm$^3$ with increasing La$_2$O$_3$content. As La$_2$O$_3$content is increased, the varistor voltage was decreased in the range of 503.49-9.42 V/mm up to 2.0 mol%, whereas increasing La$_2$O$_3$content further caused it to increase. The ZPCCL-based varistors were characterized by nonlinearity, in which the nonlinear exponent is in the range of 3.05~82.43 and leakage current is in the range of 0.24-100.22 $\mu$A. Among ZPCCL-based varistors, 0.5 mol% added-varistors exhibited an excellent nonlinearity, in which the nonlinear exponent is 82.43 and the leakage current is 0.24 $\mu$A. Furthermore, they exhibited a high stability, in which the variation rate of the varistor voltage and the nonlinear exponent was -1.11% and -6.72%, respectively, under DC stress, such as (0.80 V$_{1mA}$9$0^{\circ}C$/12h)+(0.85 V$_{1mA}$115$^{\circ}C$//12h) +(0.90 V$_{1mA}$12$0^{\circ}C$//12h)+(0.95 V$_{1mA}$1$25^{\circ}C$//12h)+(0.95 V$_{1mA}$15$0^{\circ}C$//12h). Consequently, it was estimated that ZPCCL-based ceramics will be applied to development of Pr$_{6}$O$_{11}$ based ZnO varistors having a high performance.e.rformance.e.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.4
• /
• pp.189-195
• /
• 2006

The microstructure, electrical and dielectric properties, and stability against DC accelerated aging stress of the varistors, which are composed of quaternary system $ZnO-Pr_6O_{11}CoO-Cr_2O_3-based$ ceramics, were investigated for different $La_2O_3$ contents. The increase of $La_2O_3$ content led to more densified ceramics, whereas abruptly decreased the nonlinear properties by incorporating beyond 1.0mol%. The highest nonlinearity was obtained from 0.5mol% $La_2O_3$, with the nonlinear coefficient of 81.6 and the leakage current of $0.1{\mu}A$. The varistors doped with 0.5mol% $La_2O_3$ exhibited high stability, in which the variation rates of breakdown voltage, nonlinear coefficient, leakage current, dielectric constant, and dissipation factor were -1.1%, -3.7%, +100%, +1.4%, and +8.2%, respectively, for stressing state of $0.95V_{1mA}/150^{\circ}C/24h$.

• Korean Journal of Materials Research
• /
• v.7 no.10
• /
• pp.871-871
• /
• 1997

(1-x)CaTiO/sub 3/-xLa(Zn/sub 1/2/Ti/sub 1/2/)O/sub 3/의 마이크로 유전특성을 조사하였다. x가 증가함에 따라 비유전율과 공진주파수의 온도계수는 감소하였으며, Qㆍf/sub 0/는 증가하였다. 그 결과 x=0.5인 (Ca/sub 0.5/La/sub 0.5/)(Ti/sub 0.75/Zn/sub 0.25/)O/sub 3/의 조성에서 ε/sub r/=51, Qㆍf/sub 0/=38,000 (at 7 GHz), τ/sub f/=+5ppm/℃의 유전특성이 나타났다. (Ca/sub 0.5/La/sub 0.5/)(Ti/sub 0.75/Zn/sub 0.25/) O/sub 3/조성의 소결온도를 저하시키기 위하여 Bi/sub 2/O/sub 3/를 주조성으로한 소결체를 첨가하여 소결 및 유전특성을 조사하였다. 1wt% 0.76Bi/sub 2/O/sub 3/-0.24NiO가 첨가된 경우 소결온도는 150℃ 낮아졌으며, 비유전율 (ε/sub r/), 공진주파수의 온도계수(τ/sub f), Qㆍf/sub 0/가 각각 50+5ppm/℃, 35,000인 마이크로파 유전특성이 얻어졌다. 또한 3wt%의 0.76Bi/sub 2/O/sub 3/-0.24NiO가 첨가된 경우 소결온도는 200℃ 저하되었고, 비유전율 (ε/sub r/)과 공진주파수의 온도계수 (τ/sub f)는 변하기 않았으나, Qㆍf/sub 0/값이 38,000에서 25,000으로 저하되었다.