• E2M - 전기 전자와 첨단 소재
• /
• 제7권4호
• /
• pp.317-324
• /
• 1994

In this study, new preparation method of LiCoO$_{2}$ was applied to develop cathode active material for Li rechargeable cell, and followed by X-ray diffraction analysis, electrochemical properties and initial charge/discharge characteristics as function of current density. HC8A72- and CC9A24-LiCoO$_{2}$ were prepared by heating treatment of the mixture of LiOH H$_{2}$O/CoCO$_{3}$(1:1 mole ratio) and the mixture of Li$_{2}$CO$_{3}$/CoCO$_{3}$(1:2 mole ratio) at 850 and 900.deg. C, respectively. Two prepared LiCoO$_{2}$s were identified as same structure by X-ray diffraction analysis. a and c lattice constant were 2.816.angs. and 14.046.angs., respectively. The electrochemical potential of CFM-LiCoO$_{2}$(Cyprus Foote Mineral Co.'s product), HC8A72-LiCoO$_{2}$ and CC9A24 LiCoO$_{2}$ electrode were approximately between 3.32V and 3.42V vs. Li/Li reference electrode. Stable cycling behavior was obtained during the cyclic voltammetry of LiCoO$_{2}$ electrode. According as scan rate increases, cathodic capacity decreases, but redox coulombic efficiency was about 100% at potential range between 3.6V and 4.2V vs. Li/Li reference electrode. Cathodic capacity of HC8A72-LiCoO$_{2}$ was 32% higher than that of CFM-LiCoO$_{2}$ and that of CC9A24-LiCoO$_{2}$ was 47% lower than that of CFM-LiCoO$_{2}$ at 130th cycle in the condition of lmV/sec scan rate. Constant cur-rent charge/discharge characteristics of LiCoO$_{2}$/Li cell showed increasing Ah efficiency with initial charge/discharge cycle. Specific discharge capacities of CFM and HC8A72-LiCoO$_{2}$ cathode active materials were about 93mAh/g correspondent to 34% of theretical value, 110mAh/g correspondent to 40% of theretical value, respectively. In the view of reversibility, HC8A72-LiCoO$_{2}$ was also more excellent than CFM- and CC9A24-LiCoO$_{2}$.

• 전기화학회지
• /
• 제24권4호
• /
• pp.120-132
• /
• 2021

기존 LiCoO₂의 고전압 사용의 제약에 따른 용량적 한계와 코발트 원료의 높은 가격을 해결하기 위하여 high-Nickel에 대한 개발이 활발히 진행되고 있지만 Ni 함량의 증가에 따른 구조적 안정성의 저하에 의한 전지 특성의 저하는 상용화를 지연시키는 중요한 원인이 되고 있다. 이에 Ni-rich 삼성분계 양극소재 LiNi_0.6Co_0.2Mn_0.2O₂의 고안정성을 높이고자 전구체에 균일한 이종원소 Ti를 치환을 위해서 나노크기의 TiO₂ 서스펜젼 형태 소스를 사용하여 전구체 Ni_0.6Co_0.2Mn_0.2-x(OH)₂/xTiO₂를 제조하였다. Li₂CO₃와 혼합하고, 열처리 후 양극활물질 LiNi_0.6Co_0.2Mn_0.2-xTi_xO₂ 합성하여 Ti 함량에 따른 물리적 특성을 비교하였다. Field Emission Scanning electron Microscope(FE-SEM) 및 Energy Dispersive Spectroscopy (EDS) mapping 분석을 통해 Ti 치환된 구형의 전구체와 입자 크기 측정을 통해 균일한 입자크기를 가지는 양극 활물질 제조를 확인하였고, 내부치밀도와 강도가 증가함을 확인 하고, X-ray Diffractometry (XRD) 구조 분석과 Inductively Coupled Plasma Mass Spectrometry (ICP-MS) 정량분석을 통해 Ti 치환된 양극활물질 제조 및 고온, 고전압에서 충·방전을 지속하더라도 효과적으로 용량이 유지됨을 확인하였다.