• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.23 no.4
• /
• pp.189-194
• /
• 2013

Single phase crystalline powders of $Mg_3Sb_2$ and $Mg_3Bi_2$ were prepared by mechanical alloying Mg, Sb and Bi metals with planetary ball milling for 24~48 h. The compositions of starting raw materials for single phase $Mg_3Sb_2$ and $Mg_3Bi_2$ were 3Mg : 1.8Sb and 3Mg : 1.6Bi, respectively. Two types of mechanically alloyed powders obtained were mixed at some ratios for the fabrication of $Mg_3Sb_2-Mg_3Bi_2$ composites and then hot pressed under uniaxial pressure of 70 MPa at 723 K for 1 h. The main phase of composites was a stable phase similar to $Mg_3Bi_2$ phase with a small amount of Bi phase. The distributions of Sb and Bi elements on EDS mapping images were discontinuous and their compositional contours were clear, which means that the hot pressed specimens were composites composed of two compounds of $Mg_3Sb_2$ and $Mg_3Bi_2$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.22 no.4
• /
• pp.207-212
• /
• 2012

A single phase $Mg_3Sb_2$ alloy was synthesized by melting the mixture of Mg and Sb metal powders at 1173 K. The figure of merit of the $Mg_3Sb_2$ prepared by melting method increased with temperature and showed a value of $2.39{\times}10^{-2}$ at 593 K. When the $Mg_3Sb_2$ powders were milled at high speed in a planetary ball mill for 12~48 h, Zintle phase ($Mg_3Sb_2$) was maintained as a main phase, but its crystallinity became deteriorated and elemental Sb phase appeared. Sb phase free $Mg_3Sb_2$ could be obtained by the mechanical alloying of high speed ball milling for 24 h using elemental Mg and Sb powder mixtures.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.24 no.4
• /
• pp.176-182
• /
• 2014

We intended to prepare $Mg_3Sb_2$ compound bodies through solid state reactive sintering after cold-pressing mixtures of elementary Mg and Sb powders and investigated the crystal phases of the sintered bodies according to Mg/Sb mole ratios and reaction temperatures. The $Mg_3Sb_2$ bodies sintered at the temperatures of 773~843 K showed typical crystalline phases of $Mg_3Sb_2$ compounds, but their diffraction angles in XRD patterns were slightly different along with the vertical axis of the bodies obtained. All the bottom parts of the sintered $Mg_3Sb_2$ bodies were composed of the typical crystalline phases of $Mg_3Sb_2$ compounds and their diffraction angles were completely in accord with those of the ${\alpha}-Mg_3Sb_2$ phase, when Mg : Sb = 3.15 : 1.85 at 823 K, or when the Mg moles were greater than or equal to 3.10 at 843 K. It was considered that the slightly remaining Mg phases were formed by precipitation from ${\alpha}-Mg_3Sb_2$ phases during the solidification process of liquid phase.

• Korean Journal of Materials Research
• /
• v.23 no.2
• /
• pp.98-103
• /
• 2013

$Mg_{3-x}Zn_xSb_2$ powders with x = 0-1.2 were fabricated by mechanical alloying in a planetary ball mill with a speed of 350 rpm for 24 hrs and then hot pressed under a pressure of 70 MPa at 773 K for 2 hrs. It was found that there were systematic shifts in the X-ray diffraction peaks of $Mg_3Sb_2$ (x = 0) toward a higher angle with increasing Zn for both the powder and the bulk sample and finally the phase of $Mg_{1.86}Zn_{1.14}Sb_2$ was formed at the Zn content of x = 1.2. The $Mg_{3-x}Zn_xSb_2$ compounds had nano-sized grains of 21-30 nm for the powder and 28-66 nm for the hot pressed specimens. The electrical conductivity of hot pressed $Mg_{3-x}Zn_xSb_2$ increased with increasing Zn content and temperature from 33 $Sm^{-1}$ for x = 0 to 13,026 $Sm^{-1}$ for x = 1.2 at 323 K. The samples for all the compositions from x = 0 to x = 1.2 had positive Seebeck coefficients, which decreased with increasing Zn content and temperature, which resulted from the increased charge carrier concentration. Most of the samples had relatively low thermal conductivities comparable to the high performance thermoelectric materials. The dimensionless figure of merit of $Mg_{3-x}Zn_xSb_2$ was directly proportional to the Zn content except for the compound with Zn = 1.2 at high temperature. The $Mg_{3-x}Zn_xSb_2$ compound with Zn = 0.8 had the largest value of ZT, 0.33 at 723 K.

• Food Science and Preservation
• /
• v.24 no.5
• /
• pp.565-575
• /
• 2017

This study was carried out to investigate shelf-life and quality of fresh-cut Dungkunma (Dioscorea bulbifera) in order to elevate utilization of Dungkunma a fresh food. Before vacuum-packaging (in polyethylene/polypropylene film ($100{\mu}m$, $15{\times}20cm$, $75{\pm}2cmHg$) and storaging at $2^{\circ}C$, Dungkunma was peeled out and cut to dice type ($2.0{\pm}0.5cm^3$), and then washed and blanched using hot water (at $90{\pm}2^{\circ}C$ with 2% NaCl solution for 30 sec). Blanched Dungkunma was pre-dried at room temperature, $40^{\circ}C$ and $50^{\circ}C$ for removing surface water. Each peeled dice Dungkunma was packed 50 g in polyethylene/polypropylene film ($100{\mu}m$, $15{\times}20cm$) with vacuum treatment ($75{\pm}2cmHg$) and stored at $2^{\circ}C$ for 90 days. Hardness and adhesiveness of Dungkunma blanched by 2% NaCl and pre-dried at $50^{\circ}C$ (SB50) were the highest, but changes were the least during storage. Lightness and yellowness of stored Dungkunma in all treatments decreased slightly while redness increased during storage. Changes of color of SB50 was the least. Total concentration of aerobic bacteria in SB50 was $1.88{\pm}0.18log\;CFU/g$ during 90 days and E. coli was detected in all treatments during whole storage periods. Dioscin and allantoin contents of SB50 were virtually unchanged during the storage. Consequently, the results of this study suggest that vacuum packaged Dungkunma after blanching using 2% NaCl solution could be effective to prolong the quality of fresh-cut Dungkunma.

• Journal of Physiology & Pathology in Korean Medicine
• /
• v.24 no.3
• /
• pp.476-483
• /
• 2010

The present study was performed to investigate the putative anxiolytic-like effects of the aqueous extract of the roots of Scrophularia buergeriana (SB-W) using elevated plus-maze (EPM) and hole-board apparatus in mice. SB-W was orally administered at doses of 50, 100, 200 or 400 mg/kg to ICR mice, 1 h before the behavioral evaluation. Control group were administered with an equal volume of saline, and positive control group with buspirone (2 mg/kg, i.p.). The administration of SB-W significantly increased the percentage of time spent in open arms and entries into the open arms of the EPM compared with saline-treated control group (P < 0.05). Futhermore, those anxiolytic-like activities of SB-W were antagonized by flumazenil (a $GABA_A$ antagonist, 10 mg/kg), but not by WAY-100635 (a 5-$HT_{1A}$ antagonist, 0.3 mg/kg). Moreover, there were no changes in the locomotor activity and myorelaxant effects in any group compared with saline-treated control group. In the hole-board test, the administration of SB-W (200 and 400 mg/kg) significantly increased the number of head-dipping compared with saline-treated control group (P < 0.05). Therefore, these findings suggest that Scrophularia buergeriana promotes the anxiolytic-like activity mediated by GABAergic nervous system in mice.

• Journal of the Korean earth science society
• /
• v.22 no.3
• /
• pp.208-222
• /
• 2001

Geochemical investigations on suspended amorphous iron oxide material from the Kwangyang gold mine and its surrounding area, Cheonnam, Korea have been carried out. The sediments samples were collected from 11 location along Kwangyang mine area and were air dried and sieved to -80 mesh. These samples consist mainly of iron, silicon and alumina. The Fe$_2$O$_3$ contents ranges from 17.9 wt.% to 72.3 wt.%. The content of Fe$_2$O$_3$ increase with decreasing Si, Al, Mg, Na, K, Mn, and Ti, whereas the contents of Te, Au, Ga, Bi, Cd, Hg, Sb, and Se increase in the amorphous stream sediments. Amorphous stream sediments have been severely enriched for As (up to 54.9 ppm), Bi (up to 3.77 ppm), Cd (up to 3.65 ppm), Hg (up to 64 ppm), Sb (up to 10.1 ppm), Cu (up to 37.1 ppm), Mo (up to 8.86 ppm), Pb (up to 9.45 ppm) and Zn (up to 29.7 ppm). At the upstream site, the Au content (up to 4.4 ppm) in the amorphous stream sediments are relatively high but those contents decrease with distance of mine location. The content of Ag (up to 0.24 ppm) were low in upstream site but those contents increase significantly in the downstream sites. The X-ray diffraction patterns of the samples have virtually no sharp and discrete peaks, indicating that some samples are amorphous or poorly-ordered. The quartz, goethite, kaolinite and illite were associated in amorphous stream sediments. The infrared spectra for amorphous stream sediments show major absorption bands due to OH stretching, adsorbed molecular water, sulfate and Fe-O stretching, respectively.

• Korean Journal of Medicinal Crop Science
• /
• v.24 no.5
• /
• pp.386-392
• /
• 2016

Background: Sorghum is a major cereal food crop used in many parts of the world. It has been grown on a subsistence level by farmers, under various conditions of environmental stresses in the semi-arid tropics of Africa and Asia. This plant has received significant attention because of its ability to reduce cholesterol in the blood, and its anti-dementia, antioxidant, and antimicrobial properties. It is possible to develop a functional and commercially viable sorghum variety by using superior cultivars of sorghum. The objective of this study was to build a database of superior sorghum accession. Methods and Results: We used 250 sorghum accessions collected from different geographical bioregions in Korea. We determined various agronomic characters including germination rate and ear length of these accessions. To determine the antioxidant capacity, we measured the 1,1-diphenyl-2-picrylhydrazyl radical scavenging activity, 2,2'-azino-bis (3-ethylbenzothiazoline-6-sulfonic acid)-diammonium salt radical scavenging activity, total phenolic contents, and total flavonoid contents. Accession 189 showed higher germination (> 80%) than the other accessions. Higher 1,1-diphenyl-2-picrylhydrazyl radical scavenging activity was observed in 11-SB-078 ($RC_{50}$; $1.89{\pm}2.88{\mu}g/m{\ell}$), and higher 2,2'-azino-bis (3-ethylbenzothiazoline-6-sulfonic acid)-diammonium salt radical scavenging activity was recorded in 11-SB-116 ($RC_{50}$; $35.48{\pm}2.42{\mu}g/m{\ell}$) than in the other accessions. The ear length ranged from 15 cm to 48 cm, the total phenolic contents ranged from $3mg{\cdot}GAE/g$ to $77mg{\cdot}GAE/g$, and total flavonoid contents ranged from $0.09mg{\cdot}QE/g$ to $1.07mg{\cdot}QE/g$. Conclusions: Among 250 sorghum accessions, we selected 10 with both superior agronomic characters and highly functional food quality.

• The Journal of Pediatrics of Korean Medicine
• /
• v.21 no.1
• /
• pp.253-270
• /
• 2007

Objectives : This study has been carried out to understand the effect of Cimicifugae Rhizoma and Seungmagalgeuntang on the hyperglycemic mice induced with Streptozotocin(STZ). Methods : The 60mg/kg of STZ was fed into mice twice by 24 h interval and then 120mg/kg STZ was fed again 3 days after the earlier feeding, Control group was administered mice with 0.9% saline(2mL/kg/day), and experimental groups were administered Cimicifugae Rhizoma extract(CA group, 10mg/kg/day; CB group, 30mg/kg/day) or Seungmagalgeuntang(SA group, 10mg/kg/day; SB group, 30mg/kg/day) after hyperglycemic induction for 6 weeks. Results : The body weight of experimental groups higher than control. The blood glucose concentration of the control group increased continuously reaching to 298.9 mg/dL after 6 weeks, however, significantly(p<0.01 or p<0.05) decreased in the SA and SB groups compared with control group. Blood insulin level significantly(p<0.01) increased in the experimental groups. The activities of SOD and catalase were more decreased in the experimental group than control group compared with normal group. In the point of pancreatic immunohistochemical change, the experimental group's pancreatic islets have increased and enlarged and the concentration of insulin-positive beta cells has also increased, comparing with the control group. Meanwhile forms of nucleus and mitochondria in the experimental group's hepatic cells were almost similar to the normal group. Conclusion : The result from the six weeks of observation demonstrates that the extracts from Cimicifugae Rhizoma and Seungmagalgeuntang have positive effects on lowering blood sugar level and elevating insulin concentration. The extract had also effects on recovering and regenerating pancreatic tissue of the hyperglycemic mice induced with STZ. At the same time, it had a protective effect against hepatotoxicity as well.

• Journal of the Korean Society of Food Science and Nutrition
• /
• v.24 no.4
• /
• pp.570-577
• /
• 1995

Aspergillus sp. SB-2704 was selected for its strong polygalacturonase activity among various strain of mold found in soil. It was found that production of polygalacturonase reached to maximum when the wheat bran medium containing 1% polypepton, 1% glucose, and 0.2% FeSO4 were cultured for 3 days at 35$^{\circ}C$. Polygalacturonase was purified 20.90 fold from Aspergillus SB-2704. The purification procedures include ammonium sulfate treatment, gel filtration on Sephdex G-150 and DEAE-cellulose ion exchange chromatography. Yield of the enzyme purification was 4.34%. Purified enzyme was confirmed as a single band by the polyacrylamide gel electrophoresis. When the purified enzyme was applied to SDS-polyacrylamide gel electrophoresis, the molecular weight was estimated to be 36,000. The optimum pH for the enzyme activity was 5.5 and optimum temperature was 5$0^{\circ}C$. The enzyme is stable in acidic condition. The activity of purified enzyme was inhibited by Pb2+, Hg2+ and Ba2+, whereas activated by Cu2+, Mn2+, Mg2+ and Fe2+. The activity of polygalacturonase was inhibited by the treament wit maleic anhydride, iodine, and EDTA. The result indicate the possible involvement of histidine and metal ion at active site.