• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2001.11a
• /
• pp.24-24
• /
• 2001

• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.296-300
• /
• 1999

Cross-shape structures of spin tunneling junctions were fabricated using DC magnetron sputtering and metal masks. The film structures were $substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al_2O_3/CoFe/NiFe$ and $substrate/Ta/NiFe/CoFe/ Al_2O_3/CoFe/NiFe/FeMn/NiFe$. Fabrication conditions of insulating layer ($Al_2O_3$) and thickness and sputtering power of each film layer were varied, and maximum magnetoresistance ratio of 24.3 % was obtained. Magnetic characteristic variations in the above mentioned two structures and two types of substrates (Corning glass 7059 and Si(111)) were compared. Annealing of the junctions was performed to find out magnetic characteristic variations expected from the device fabrication. Magneoresistance Ratio were observed to maintain as-deposited value up to 150 $^{\circ}C$ annealing and then to drop rapidly after 180 $^{\circ}C$ annealing.

• Journal of Powder Materials
• /
• v.24 no.3
• /
• pp.242-247
• /
• 2017

In this study, the electroless nickel plating method has been investigated for the coating of Ni nanoparticles onto fine Al powder as promising energetic materials. The adsorption of nickel nanoparticles onto the surface of Al powders has been studied by varying various process parameters, namely, the amounts of reducing agent, complexing agent, and pH-controller. The size of nickel nanoparticles synthesized in the process has been optimized to approximately 200 nm and they have been adsorbed on the Al powder. TGA results clearly show that the temperature at which oxidation of Al mainly occurs is lowered as the amount of Ni nanoparticles on the Al surface increases. Furthermore, the Ni-plated Al powders prepared for all conditions show improved exothermic reaction due to the self-propagating high-temperature synthesis (SHS) between Ni and Al. Therefore, Al powders fully coated by Ni nanoparticles show the highest exothermic reactivity: this demonstrates the efficiency of Ni coating in improving the energetic properties of Al powders.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.593-602
• /
• 1991

Al2O3 and NiO-doped Al2O3 powders were prepared from the ethanol solution of Al (NO3)3$.$9H2O and Ni(NO3)2$.$6H2O by spray pylolysis method using two-fluid nozzle. As a result of spraying test with 0.3 mol/{{{{ iota }} concentration starting solution, mean droplet sizes varied with 8.99∼9.69$\mu\textrm{m}$ and those standard deviation were 4.57∼5.12. As-prepared powders which were synthesized at 1000$^{\circ}C$ have spherical shape, sizes of 0.1∼3.0$\mu\textrm{m}$ and specific surface area of 22.34∼24.20㎡/g. Most powders consisted of {{{{ gamma }}-Al2O3 phase and transforned into ${\alpha}$-A;2O3 phase by calcination at 1100$^{\circ}C$ for 1 hr. NiO-doped Al2O3 sintered bodies had better sinterability than those of pure Al2O3 and 0.3 wt% NiO-doped Al2O3 had near theoretical density and dense microstructure.

• Korean Journal of Materials Research
• /
• v.13 no.1
• /
• pp.24-30
• /
• 2003

The Raney Ni catalyst was fabricated by mechanochemically process(MC process) in the Al-Ni system. Intermetallic compound obtained by mechanical alloying was leached in an alkaline solution. The characteristics of the mechanically alloyed powder and Raney Ni catalyst were analyzed by XRD, ICP-AES and EXAFS. In Al-50wt.%Ni, the metastable intermetallic compound phase close to AlNi phase was obtained by mechanical alloying unlike Al-Ni equilibrium phase diagram. The metastable intermetallic compound was transformed into $Al_3$$Ni_2$phase via the annealing at $750^{\circ}C$. The microstructure of Raney Ni fabricated by MC process was mainly bcc Ni including fcc Ni.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.5 s.176
• /
• pp.1146-1154
• /
• 2000

Fatigue strength of NiAl and Ni$_3$Al particulate reinforced aluminum alloy composites fabricated by the diecasting method was examined at room and elevated temperatures. The results were compared wit h that of SiC particulate reinforced one. The particulate reinforced composites showed some improvement in the static and fatigue strength at elevated temperatures when compared with that of Al alloy. The composites reinforced by intermetallic compound particles showed good fatigue strengths at elevated temperatures especially $Ni_3AI_{p}/Al$ alloy composite showed good fatigue limit up to high temperature of 30$0^{\circ}C$. Adopting intermetallic compound particle as a reinforcement phase, it will be possible to develop MMC representing better fatigue property at elevated temperature.

• Clean Technology
• /
• v.9 no.3
• /
• pp.125-132
• /
• 2003

Activity improvement of Ni metal catalysts for carbon dioxide reforming was studied using HY-zeolite as the main supporter. As the reaction temperature increased, $CH_4$ and $CO_2$ conversions increased, and conversions higher than 80% was obtained above $700^{\circ}C$. As the Ni loading increased, the catalyst activity increased, and the highest activity was shown for the Ni loading of 13wt%. The HY-zeolite support showed the highest intial conversions of $CH_4$ and $CO_2$, but it showed faster deactivation than a ${\gamma}-Al_2O_3$ support. Nevertheless, it maintained the $CH_4$conversion higher than 80% after 24 hr reaction. The effect of promoters such as Mg, Mn, K, and Ca was also studied. It was observed that the Mg promotor exhibited the highest catalyst activity and less deactivation compared with Mn, K and Ca. After 24hr reaction, The optimum Mg content was found to be 5wt%.

• Journal of the Korean Society for Heat Treatment
• /
• v.23 no.2
• /
• pp.96-103
• /
• 2010

$Ni_3Al$ is known as a good high temperature structural material because of high yield strength at ambient temperature. However, it is too brittle to use as a structural material because of their weak grain boundary. In this work, orientation measurement and related mechanical properties of directionally solidified NiAl/$Ni_3Al$ two-phase alloys with various compositions (Ni-23~27 at.%Al) were investigated for developing multi-phase DS-processed alloys with the growth rates of 10, 50 and 100 ${\mu}m/s$ in a modified Bridgeman type furnace. It was found that the multi-phase microstructures such as the $\gamma$ dendrite +${\gamma}'$ matrix duplex microstructure was formed in the hypoeutectic composition of 23 at.%Al, $\beta$ dendrite +${\gamma}'$ matrix duplex microstructure in the hypereutectic composition of 26 and 27 at.%Al. And ${\gamma}'$ single phase was formed in the composition of 24.5 and 25 at.%Al. The hypoeutectic alloy including $\gamma$ dendrites with ${\gamma}'$ matrix showed a large elongation of over 70% at room temperature. However, the room-temperature tensile elongation decreased with increasing Al contents because the volume fraction of brittle $\beta$ dendrites in the ductile ${\gamma}'$ matrix increased.

• Advances in Energy Research
• /
• v.8 no.4
• /
• pp.223-231
• /
• 2022

An ex-situ gravitational fixed bed pyrolysis reactor was used over Al₂O₃ supported Ni₂P based catalyst with various Ni/P molar ratios (0.5-2.0) and constant nickel loading of 5.37 mmol/g Al₂O₃ to determine the hydrodeoxygenation of rubberwood sawdust (RWS) at atmospheric pressure. The 3D catalysts formed were characterized structurally as well as acidic properties were determined by hydrogen-temperature programmed reduction (TPR). The Ni₂P phase formed completely on Al₂O₃ for 1.5 Ni/P ratio, although lesser crystallite sizes of Ni₂P were seen at Ni/P ratios less than 1.5. Additionally, it was shown that when nickel loading level increased, acidity increased and specific surface area dropped, probably because nickel phosphate is not easily converted to Ni₂P. When Ni/P ratio was 1.5, Ni₂P phase fully formed on Al₂O₃. The catalytic activity was explained in terms of impacts of reaction temperature and Ni/P molar ratio. At relatively high temperature of 450℃, the high-value deoxygenated produce was predominantly composed of n-alkanes. Based on the findings, it was suggested that hydrogenolysis, hydrodeoxygenation, dehydration, decarbonylation, and hydrogenation are all part of mechanism underlying hydrotreatment of RWS. In conclusion, the synthesized Ni₂P/ Al₂O₃ catalyst was capable of deoxygenating RWS with ease at atmospheric pressure, primarily resulting in long chained (C₉-C₂₄) hydrocarbons and acetic acid.

• Proceedings of the Korea Air Pollution Research Association Conference
• /
• 1988.12a
• /
• pp.24-24
• /
• 1988