• Journal of the Korean Chemical Society
• /
• v.62 no.2
• /
• pp.93-98
• /
• 2018

Bis-GMA, TEGDMA, and camphorquinone were used as the main material, cross-linking agent, and photoinitiator, respectively. In addition, 2-isocyanatoethyl methacrylate was used as an additive for high strength, while the 3-hydroxypyridine was used as an additive for antibacterial activity. Photopolymerization was also carried out at a 440-480 nm wavelength and at about $1000mW/cm^2$ intensity for about 40 seconds. The breaking strength measurement of the samples showed that the breaking strength increased along with increasing the addition ratio of IEM, while it took less time until the polymerization was complete, thereby suggesting that the degree of polymerization has the tendency to increase. And also, compared to the size of the clear zone formed by ampicillin, the 3-hydroxypyridine group exhibited antimicrobial activity induced by ampicillin. The results of this study suggest that the use of 2-isocyanatoethyl methacrylate as an additive for high strength and 3-hydroxypyridine as an additive for improved antibacterial activity would improve the usability of the fabricated polymer as a dental resin cement material with high functionality.

• Journal of Adhesion and Interface
• /
• v.11 no.2
• /
• pp.63-69
• /
• 2010

In this study, acryl resin PSA containing hydroxyl group based on 2-EHA (2-ethyl hexyl acrylate), 2-EHMA (2-ethyl hexyl methacrylate), 2-HEA (2-Hydroxy ethyl acrylate), acrylic acid was synthesized and then, isocyanate modified acryl resin PSA prepared with adduct reaction according to the amount of MOI (Methacryloyloxyethyl isocyanate) or 2-isocyanatoethyl methacrylate that can improve the curing property. This research shows that the initial PSA and peel adhesion are decreased according to the increase of the amount of the MOI and isocyanate curing agent. After UV irradiating, the peel adhesion is decreased with increasing the amount of the MOI (Methacryloyloxyethyl isocyanate) and isocyanate curing agent, because of the high curing property.