• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2011.10a
• /
• pp.886-887
• /
• 2011

To obtain a transparent electrode, AZO thin film was deposited on SiOC film with various flow rates by rf magnetron sputtering system. SiOC film was deposited with various DMDMOS/O2 flow rate ratio by CVD, The optical electrical properties of the SiOC film and SiOC/AZO were analyzed by the uv visible spectrometer and 4 point prove system. The reflectance of SiOC/AZO film was changed in compared with that of SiOC film. The resistance was decreased with low RF power because of increasing the concentration of carriers.

• Journal of information and communication convergence engineering
• /
• v.9 no.4
• /
• pp.461-465
• /
• 2011

An aluminum doped zinc oxide (AZO) film for front contacts of thin film solar cells, in this work, were deposited by r.f. magnetron sputtering, and then etched in diluted hydrochloric acid solution for different times. Effects of surface texturing on the electro-optical properties of AZO films were investigated. Also, to clarify the light trapping of textured AZO film, amorphous silicon thin film solar cells were fabricated on the textured AZO/glass substrate and the performance of solar cells were studied. After texturing, the spectral haze at the visible range of 400 ~750 nm increased substantially with the etching time, without a change in the resistivity. The conversion efficiency of amorphous Si solar cells with textured AZO film as a front electrode was improved by the increase of short-circuit current density ($J_{sc}$), compared to cell with flat AZO films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.1
• /
• pp.37-43
• /
• 2012

We were studied that AZO conductive thin film can substitute for FTO electrode in dye sensitized solar cell. Three types of AZO films were deposited on soda-lime glass(AZO/glass, AZO/AZO/glass, textured AZO/AZO/glass) using RF magnetron sputtering process and investigated their properties of electrical, optical, and photoelectric conversion rate. The textured AZO/AZO/glass has the lowest resistivity of $3.079{\times}10^{-4}\;{\Omega}cm$ among other films. And the optical transmittance rate was better than both non textured AZO/AZO/glass and FTO/glass in the visible region. After manufacturing dye solar cells using the three types of AZO films, the textured AZO/AZO/glass showed the highest photoelectric conversion rate of 3.68% among AZO samples. But the transformation rate was slightly lower than FTO cells (4.52%). However, the conductive film of textured AZO/AZO/glass can be applicable to use an electrode in solar cells as cost-effective products.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.281-282
• /
• 2005

The AZO thin film was prepared on flexible substrate by Facing Targets Sputtering method. The substrate used the Polycarbonate(PC), thickness 200$\mu$m. In particular, the AZO thin film was prepared at room temperature because the substrate is weak in heat. The structural, electrical, optical properties of the AZO thin film were investigated and the surface was observed by microscope.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.9
• /
• pp.979-982
• /
• 2004

The ZnO thin films were prepared by the FTS (facing target sputtering) system, which enables to provide high density plasma and a high deposition rate at a low working gas pressure. We introduced the AZO thin film in order to improve the crystallographic properties of ZnO thin film because of the AZO(ZnO:Al) thin film has an equal crystal structure to the ZnO thin film. ZnO/AZO thin films were deposited at a different oxygen gas flow ratio, R.T. 2mTorr working pressure and a 0.8A sputtering current. The film thickness and c-axis preferred orientation of ZnO/AZO/glass thin films were measured by ${\alpha}$-step and an x-ray diffraction (XRD) instrument. In the results, we could prepare the ZnO thin film with c-axis preferred orientation of about 6$^{\circ}$ on substrate temperature R.T. at O$_2$ gas flo rate 0.5.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.4
• /
• pp.422-425
• /
• 2004

In this study, the AZO thin films were prepared as a function of oxygen gas flow ratio at room temperature by FTS(Facing Targets Sputtering) apparatus using Zn:Al(metal)-Zn:Al(metal) or Zn(metal)-ZnO:Al(ceramic). The film thickness, crystalline and electric properties of AZO thin film was evaluated by $\alpha$-step, XRD and 4-point probe. In the results, the resistivity of AZO thin film was shown the lowest value about 8${\times}$10$^{-2}$ $\Omega$-cm(Zn:Al-Zn:Al), 3${\times}$10$^{-1}$ $\Omega$-cm(Zn-ZnO:Al) at the oxygen gas flow ratio 0.3. And the AZO thin film has good crystalline at oxygen gas flow ration 0.4, using Zn:Al-Zn:Al targets.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07a
• /
• pp.165-168
• /
• 2004

In this study, AZO(ZnO:Al) thin film were prepared by FTS(Facing Target Sputtering) system. The electrical, optical and crystallographic properties of AZO thin film with $O_2$ gas flow ratio have been investigated. The thickness, transmittance, crystal structure and resistivity of AZO thin film were measured by a-step, UV-VIS spectrometer, XRD and four-point probe, respectively. As a result AZO thin film deposited with the transmittance over 80% and the resistivity about $10^{-1}\Omega-cm$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.11a
• /
• pp.586-589
• /
• 2004

In this study, AZO(ZnO:Al) thin film were prepared by FTS(Facing Target Sputtering) system. The electrical, optical properties and crystalline of AZO thin film with thickness have been investigated. The thickness, transmittance, crystalline and electrical properties of AZO thin film were measured by a-step, UV-VIS spectrometer, hall effect measurement system, XRD and four-point probe, respectively. As a result, AZO thin film deposited with the transmittance over 80% and the resistivity about $10^{-4}\;\Omega-cm$.

• Transactions on Electrical and Electronic Materials
• /
• v.15 no.4
• /
• pp.207-212
• /
• 2014

Aluminum-doped zinc oxide (AZO) films were deposited on SiOC/Si wafer by an RF-magnetron sputtering system, by varying the deposition parameters of radio frequency power from 50 to 200 W. To assess the correlation of the optical properties between the substrate and AZO thin film, photoluminescence was measured, and the origin of deep level emission of AZO thin films grown on SiOC/Si wafer was studied. AZO formed on SiOC/Si substrates exhibited ultraviolet emission due to exciton recombination, and the visible emission was associated with intrinsic and extrinsic defects. For the AZO thin film deposited on SiOC at low RF-power, the deep level emission near the UV region is attributed to an increase of the variations of defects related to the AZO and SiOC layers. The applied RF-power influenced an energy gap of localized trap state produced from the defects, and the gap increased at low RF power due to the formation of new defects across the AZO layer caused by lattice mismatch of the AZO and SiOC films. The optical properties of AZO films on amorphous SiOC compared with those of AZO film on Si were considerably improved by reducing the roughness of the surface with low surface ionization energy, and by solving the problem of structural mismatch with the AZO film and Si wafer.

• Korean Journal of Materials Research
• /
• v.21 no.6
• /
• pp.341-346
• /
• 2011

In this study, we inserted a Zn buffer layer into a AZO/p-type a-si:H layer interface in order to lower the contact resistance of the interface. For the Zn layer, the deposition was conducted at 5 nm, 7 nm and 10 nm using the rf-magnetron sputtering method. The results were compared to that of the AZO film to discuss the possibility of the Zn layer being used as a transparent conductive oxide thin film for application in the silicon heterojunction solar cell. We used the rf-magnetron sputtering method to fabricate Al 2 wt.% of Al-doped ZnO (AZO) film as a transparent conductive oxide (TCO). We analyzed the electro-optical properties of the ZnO as well as the interface properties of the AZO/p-type a-Si:H layer. After inserting a buffer layer into the AZO/p-type a-Si:H layers to enhance the interface properties, we measured the contact resistance of the layers using a CTLM (circular transmission line model) pattern, the depth profile of the layers using AES (auger electron spectroscopy), and the changes in the properties of the AZO thin film through heat treatment. We investigated the effects of the interface properties of the AZO/p-type a-Si:H layer on the characteristics of silicon heterojunction solar cells and the way to improve the interface properties. When depositing AZO thin film on a-Si layer, oxygen atoms are diffused from the AZO thin film towards the a-Si layer. Thus, the characteristics of the solar cells deteriorate due to the created oxide film. While a diffusion of Zn occurs toward the a-Si in the case of AZO used as TCO, the diffusion of In occurs toward a-Si in the case of ITO used as TCO.