The accelerated thermal aging of CSPE(Chloro Sulfonate Polyethylene) was carried out for 40.41, 121.22, 202.04 days, 16.82, 50.45, 84.09 days and 7.32, 21.96, 36.59 days at 100, 110, and $120^{\circ}C$, respectively, which are equivalent to 20, 60, 100 years of aging at $50^{\circ}C$. The permittivities and the apparent densities of the accelerated thermally aged CSPE samples are increased with accelerated thermal aging year but EAB(Elongation at Break) is decreased with that. The dielectric strength and the electric breakdown of the non-accelerated and accelerated thermally aged CSPE samples do not depend on accelerated thermal aging year and applied voltage rising time. density and EAB measures.

• Proceedings of the KIEE Conference
• /
• 2011.07a
• /
• pp.1447-1448
• /
• 2011

The CSPE cables are used for three years in nuclear power plant. The accelerated thermal aging of chloro sulfonate polyethylene(CSPE) jacket of test cables were carried out for the period equal to 10, 20 and 30 years in air at 90 and $100^{\circ}C$, respectively. The electrical volume resistivity, density, XPS, FE-SEM, EDS and XRF of the accelerated thermal aging of CSPE were measured. The validation of condition monitering method of accelerated thermal aging CSPE was estimated by them. The best validation of condition monitoring method of accelerated aging CSPE is electrical volume resistivity because change thermal of the specimen showed distinction.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.59 no.10
• /
• pp.1832-1838
• /
• 2010

Aging of transformer insulating material in natural ester insulating oil is compared to that in conventional transformer oil. Aging of insulating paper and insulating oil have been studied by performing accelerated thermal aging test. Sealed aging test vessels containing cooper, laminated core, Kraft paper and insulating oil(natural oil or mineral oil) were aged at $140^{\circ}C$ for 500, 1000, 1500 and 2000 hours. Insulating oils after aging are investigated with total acid number, breakdown voltage and viscosity. Also, degradation of insulating paper after aging is determined using breakdown voltage and mechanical strength. Accelerated aging studies demonstrate a slower aging rate for natural ester insulating oil compared to the rate for conventional mineral oil.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.60 no.11
• /
• pp.2088-2092
• /
• 2011

The accelerated thermal aging of CSPE(chloro sulfonate polyethylene) of test cables were carried out for the period equal to 10, 20 and 30 years in air at $100^{\circ}C$, respectively. The CSPE cables(TAIHAN electric wire Co. Ltd) which installed in nuclear power plant for three years were used as starting materials. Condition monitering methods of the accelerated thermal aging of CSPE cables were estimated through indenter modulus and OIT(oxidation induction time) of IEC 62582, and those were newly estimated through volume electrical resistivity, ultrasound reflection time, density, FE-SEM(field emission scanning electron microscopy), XPS(x-ray photoelectron spectroscopy), EDS(energy dispersive spectroscopy), and WD-XRF(wavelength dispersive x-ray fluorescence). A new condition monitoring methods of the accelerated thermal aging of CSPE cables were generally coincident with trend of indenter modulus expect EDS, XPS and XRF. A volume electrical resistivity among new condition monitoring methods of the accelerated thermal aging of CSPE cables is excellent. It is considered that life-time of CSPE cable can be predicted through volume electrical resistivity, if CSPE jacket was aged for period such as more than 20 years.

• Proceedings of the KSR Conference
• /
• 2003.10c
• /
• pp.606-610
• /
• 2003

The 200 class insulation system which adopted to traction motor have excellent dielectric strength but weaken to thermal stress therefore deterioration phenomena analysis according to thermal stress is necessary. Accelerated thermal aging tests have been used to determine thermal reliability of stator coils used as traction motor in electric multiple unit. The conventional aging test is carried on according to IEC 60034-18-31 and IEEE Std. 275-1992. Variation in insulation resistance, P.I, capacitance, dielectric loss($tan{\delta}$) and partial discharge are measured during the aging cycle. Sample coils for traction motor were tested by accelerated aging test which composed of heat, vibration and moisture. Reliability and expected life were evaluated on the insulation system for traction motor.

• Journal of Ocean Engineering and Technology
• /
• v.8 no.2
• /
• pp.157-165
• /
• 1994

Effect of an accelerated iso-thermal aging (375 degree C x 66days, 375 degree C x 200days) on elastic-plastic fracture resistance curve were examined in SA533B low alloy steel. Fracture toughness test are conducted by unloading compliance method at room temperature. But the apparent negative crack growth phenomenon, usually arise in partial unloading compliance test. The phenomenon of negative crack growth may be eliminated by the offset technique. There is no effect of aging on J sub(IC) and dJ/da in iso-thermal aged (375 degree C x 66 days) specimen, but there is very little effect in iso-thermal aged (375 degree C x 200 days) specimen.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.2
• /
• pp.24-30
• /
• 2011

The accelerated aging characteristics of electroconductive papers manufactured with a mixture of carbon fiber were investigated by heating in dry oven. By accelerated aging time, the tensile strength, tensile stretch of the papers were decreased more slowly with increase of carbon fiber content, but the electrical conductivity was more rapidly decreased in case of high carbon fiber content. The weight loss of papers by thermal analysis were reduced as increasing the carbon fiber content. These results were indicated that the electrical conductivity of carbon fiber was diminished easily by heat aging, but thermal characteristic of carbon fiber was much better than that of wood pulp.

• Journal of the Korean Solar Energy Society
• /
• v.40 no.2
• /
• pp.11-23
• /
• 2020

The application of the high-performance insulation materials for buildings seems to be an essential measure for reducing energy use in buildings. Phenolic foam is a readily available insulation material with thermal conductivity of about 0.018 to 0.020 W/(mK). It has the advantage of higher thermal resistance and better fire resistance compared to other conventional building insulation materials. Insulation material used for building envelope is regarded as one of the decisive factors for building's energy load. Furthermore, the degradation of its thermal performance over time increasingly affects the building's energy use demand. Generally, the life span of conventionally built buildings is expected to be more than 50 years, so the long-term performance of insulation materials is critical. This paper aims to evaluate the long-term performance of phenolic form boards through an accelerated aging test. The tests were conducted according to BS EN 13166 and KS M ISO 11561. Based on the results of the accelerated aging test, the thermal performance variation of the material was analyzed, and then its aged value after 25 years was computed. Also, the characteristics of the phenolic foam board's long-term performance were also examined based on the standard testing methods adopted.

• Journal of the Korean Society for Railway
• /
• v.8 no.2
• /
• pp.188-194
• /
• 2005

Aging characteristics of glass fabric/phenolic composites for tilting train subjected to combined environmental aging factors were investigated. A 2.5KW accelerated aging tester with a xenon-arc lamp was used to provide environmental aging factors such as temperature, moisture, and ultraviolet. A series of aging tests were conducted up to 3000 hours and several types of specimens were prepared along the warp direction and the fill direction. Mechanical degradations for tensile, flexural, and shear properties were evaluated as a function of exposure times through a material testing system. Thermal analysis properties such as storage shear modulus, loss shear modulus, and tan 3 were measured through a dynamic mechanical analyzer. Finally exposed surfaces of the composites were examined using a scanning electron microscope. According to the experimental results, mechanical properties and thermal analysis properties of glass fabric/phenolic composites were found to be slightly degraded as a function of exposure times due to combined environmental effects.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.2
• /
• pp.119-126
• /
• 2002

The mica/epoxy composite used in generator(rated 22 kV and 500 MW) stator windings was aged at 180$\^{C}$ for up to 1000 hours in air and hydrogen. The degradation mechanism was investigated through the defect of evolution and microstructural analysis by performing SEM(Scanning Electron Microscope). As the thermal aging time increases, the number of voids per unit volume increases at the mica/epoxy interface of generator stator windings. The aged specimens in hydrogen showed retarded generation and growth of voids. Accelerated aging tests were conducted using the combination of thermal and electrical aging in air and hydrogen. The aging was carried out at a combined stress such as thermal aging at 110$\^{C}$, electrical aging at 5.5 kV/mm and frequencies 420 Hz in air, and electrical aging at 5.5 kV/mm and frequencies 420 Hz in hydrogen (pressure 4 kg/㎠). Thermal and electrical aging generates large voids at the mica/epoxy interface in air. Electrical aging in hydrogen also generates small voids, delaminations and cracks in mica tapes.