Activated carbons from rice-straw can be used as an adsorbents for the purification of water were prepared and evaluated. The adsorptive capacities of activated carbons were measured by iodine, potassium permangante, phenol and metals. It was observed by electron microscope (SEM) and IR spectrum that organic components in the rice-straw and its carbonization product were disappeared. Slit-shaped and porousstructures were formed by activation. There was no relationship between temperature and adsorption of iodine but adsorption of potassium permanganate increased as temperature rose. The adsorption of the phenol was greater than 99%. The adsorption data of phenol at $25^\circ{C}$ obeyed the Freundlich's isotherm. Various metals except sodium were not removed by activated carbon.

• Proceedings of the Korean Fiber Society Conference
• /
• 1996.10a
• /
• pp.117-123
• /
• 1996

Cabon fiber of general purpose was prepared from coal tar pitch modified with 10% benzoquinine(BQ) at 380C for 3 hours. Such a modified pitch raised the softening of the pitch from 85C to 271C at the yield of 40%. The modified pitch was spun smoothly at a rate of 480m/min into a fiber of 20um diameter. The fiber was stabilized stepwise at 236C (5C/min) and 312C (1C/min) for 3 hours each. Both carbonized and graphitized fibers exhibited tensile strength of 570MPa which appears large enough as a precursor for active carbon fiber. The activated carbon fiber prepared exhibited relatively high surface area of 2062m2/g at 76% burn-off and rather narrow distribution pore size of 20A.

• Proceedings of the Korean Society For Composite Materials Conference
• /
• 2005.04a
• /
• pp.226-230
• /
• 2005

This paper presents the actuation performance of a conducting shape memory polyurethane (CSMPU) actuator. We introduced a concept of shape memory polyurethane activated by electric power while conventional shape memory polyurethanes are activated by external heat source. A conducting shape memory polyurethane actuator was manufactured by adding cabon nano-tube to conventional shape memory polyurethane. The main problem of the previous CSMPU was bad dispersion of carbon nano-tubes in polyurethane. In this paper, we have tried to find manufacturing method to solve the dispersion problem. With a lot of elaborative works, we have developed conducting shape memory polyurethane actuator with good electrical performance. The actuation performance of the developed conducting shape memory polyurethane actuator was measured and assessed.

• Korean Chemical Engineering Research
• /
• v.56 no.5
• /
• pp.641-646
• /
• 2018

Sodium borohydride, $NaBH_4$, shows a number of advantages as hydrogen source for portable proton exchange membrane fuel cells (PEMFCs). Properties of $NaBH_4$ hydrolysis reaction using activated carbon supported Co-B/C, Co-P-B/C catalyst were studied. BET surface area of catalyst, yield of hydrogen, effect of $NaBH_4$ concentration and durability of catalyst were measured. The BET surface area of carbon supported catalyst was over $500m^2/g$ and this value was 2~3 times higher than that of unsupported catalyst. Hydrogen generation of activated carbon supported catalyst was more stable than that of unsupported catalyst. The activation energy of Co-P-B/C catalyst was 59.4 kJ/mol in 20 wt% $NaBH_4$ and 14% lower than that of Co-P-B/FeCrAlloy catalyst. Catalyst loss on activated carbon supported catalyst was reduced to about 1/3~1/2 compared with unsupported catalyst, therefore durability was improved by supporting catalyst on activated carbon.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.48-53
• /
• 2002

$Al_2O_3-SiC$ and $Al_2O_3-SiC$-TiC composite powders were prepared by SHS process using $SiO_2,\;TiO_2$, Al and C as raw materials. Aluminum powder was used as reducing agent of $SiO_2,\;TiO_2$ and activated charcoal was used as carbon source. In the preparations of $Al_2O_3-SiC$, the effect of the molar ratio in raw materials, compaction pressure, preheating temperature and atmosphere were investigated. The most important variable affecting the synthesis of $Al_2O_3-SiC$ was the molar ratio of carbon. Unreactants remained in the product among all conditions without compaction. The optimum condition in this reaction was $SiO_2$: Al: C=3: 5: 5.5, 80MPa compaction pressure under Preheating of $400^{\circ}C$ with Ar atmosphere. However there remains cabon in the optimum condition. The effect of $TiO_2$ as additive was investigated in the preparations of $Al_2O_3-SiC$. As a result of $TiO_2$ addition, $Al_2O_3-SiC$-TiC composite powder was prepared. The $Al_2O_3$ powder showed an angular type with 8 to $15{\mu}m$, and the particle size of SiC powder were 5~$10{\mu}m$ and TiC powder were 2 to $5{\mu}m$.

• Korean Chemical Engineering Research
• /
• v.43 no.6
• /
• pp.668-674
• /
• 2005

It is reported that a method for the hydrogen production from the propane decomposition using carbon black as a catalyst is more effective than from the methane decomposition. Since the by-products like CO and $CO_2$ are not produced by the direct decomposition of propane, it is considered as an environmentally sustainable process. In this study, hydrogen was produced by the direct decomposition of propane using either commercial activated carbon or carbon black at atmospheric pressure in the temperature range of $500-1,000^{\circ}C$. Resulting products in our experiment were not only hydrogen but also several by-products such as methane, ethylene, ethane, and propylene. Hydrogen yield increased as temperature increased because the amount of those by-products produced in the experiment was inversely proportional to temperature. The achieved hydrogen yield at $750^{\circ}C$ with commercial DCC N330 catalyst was 22.47％ in this study.