• Korean Journal of Materials Research
• /
• v.27 no.8
• /
• pp.397-402
• /
• 2017

We used an etching process to control the line-width of screen printed Ag paste patterns. Ag paste was printed on anodized Al substrate to produce a high power LED. In general, Ag paste spreads or diffuses on anodized Al substrate in the process of screen printing; therefore, the line-width of the printed Ag paste pattern increases in contrast with the ideal line-width of the pattern. Smudges of Ag paste on anodized Al substrate were removed by neutral etching process without surface damage of the anodized Al substrate. Accordingly, the line-width of the printed Ag paste pattern was controlled as close as possible to the ideal line-width. When the etched Ag paste pattern was used as a seed layer for electroless Ni plating, the line width of the plated Ni film was similar to the line-width of the etched Ag paste pattern. Finally, in pattern formation by Ag paste screen printing, we found that the accuracy of the line-width of the pattern can be effectively improved by using an etching process before electroless Ni plating.

• Korean Journal of Materials Research
• /
• v.20 no.1
• /
• pp.19-24
• /
• 2010

The current study examined Ag migration from the Ag paste bump in the SABiT technology-applied PCB. A series of experiments were performed to measure the existence/non-existence of Ag in the insulating prepreg region. The average grain size of Ag paste was 30 nm according to X-ray diffraction (XRD) measurement. Conventional XRD showed limitations in finding a small amount of Ag in the prepreg region. The surface morphology and cross section view in the Cu line-Ag paste bump-Cu line structure were observed using a field emission scanning electron microscope (FE-SEM). The amount of Ag as a function of distance from the edge of Ag paste bump was obtained by FE-SEM with energy dispersive spectroscopy (EDS). We used an electron probe micro analyzer (EPMA) to improve the detecting resolution of Ag content and achieved the Ag distribution function as a function of the distance from the edge of the Ag paste bump. The same method with EPMA was applied for Cu filled via instead of Ag paste bump. We compared the distribution function of Ag and Cu, obtained from EPMA, and concluded that there was no considerable Ag migration effect for the SABiT technology-applied printed circuit board (PCB).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.233-234
• /
• 2006

In this paper, Via hole pore were investigated during PLAS (PessureLess Assisted Constrained Sintering) process of LTCC. Ag and Ag-Pd paste mixture were tested for via paste. Ag paste with 10~25% Ag-Pd paste showed no via hole pore, but further increase of Ag-Pd contents in via paste increased via pore. From shrinkage curve, 10~25% Ag-Pd paste showed expansion behaviors before shrink and this phenomena result in the reduction of via hole pore during PLAS process.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.9
• /
• pp.827-832
• /
• 2005

Dual band internal antennas were fabricated with Ag conducting paste of various preparation conditions and different print thickness by silk screen print. We have investigated microwave properties were compared Ag conducting paste antenna with copperplate antenna at 800 MHz and 1,800 MHz. Gain of Ag conducting paste antenna was improved when preparation conditions were the single size Ag particle, using dry type resin and high Ag containing percent. However, it was lower than that of copperplate antenna within $0.1\~2.0dBi$ at 800MHz. In addition, it was improved at 800MHz when thickness of Ag conducting paste was printed more than skin depth but it was held after critical print thickness. On the other hand, it was reached level of copperplate antenna at 1,800MHz.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2002.11a
• /
• pp.169-172
• /
• 2002

Silver pastes for inner conductor in the Low Temperature Co-fired Ceramics (LTCC) are composed of silver powder, binder, solvent and additives. The composition of the chemicals have influence on rheology, printability, shrinkage rate, etc. In this study, commercial Ag pastes and Ag pastes made in KETI were investigated to find the relationship between characteristics of Ag paste and solid contents. Ag pastes with 68~90 wt% Solid Contents were tested. Substrate/paste matching property and conductivity of the conductor lines showed large dependence on solid contents of Ag paste.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.10
• /
• pp.844-849
• /
• 2011

Two kind of Ag-pastes were prepared for integrating the bulk Si solar cell. One is the Ag-paste with Pb-based glass frit and the other is that with Bi-based glass frit. The pastes were the mixture of 84 wt% Ag, 2 wt% glass frit, 11 wt% solvent of buthyl cabitol acetate, and 2 wt% additives. After fabricating the Ag-pastes, they was coated on a $SiN_x$/n+/p- stacks of a commercial mono-Si solar cell. The solar cell efficiency was 17.6% in the case of the Pb-based Ag-paste. However that was 16.2% in the solar cell integrated with the Bi-based Ag-paste. The lower performance in Bi-based Ag-paste was caused by the higher series resistance and the lower shunt resistance in comparison with the Pb-based Ag-paste.

• Journal of the Korean Society of Safety
• /
• v.30 no.1
• /
• pp.21-27
• /
• 2015

In this study, interfacial characteristics between SOFC and Ag paste as current collector was estimated in the high temperature environment. The Ag paste was used to connect the unit cell of SOFC strongly with interconnector and provide the electrical conductivity between them. To confirm electrical conductivity, Ag paste was treated in the furnace at $800^{\circ}C$ for 48 hours. The sheet resistance of Ag paste was measured to compare the resistance values before and after the heat treatment. Also, the four-point bending test was performed to measure the interfacial adhesion. The unit cell of SOFC and $SiO_2$ wafer were diced and then attached by Ag paste. The $SiO_2$ wafer had the center notch to initiate a crack from the tip of the notch. The modified stereomicroscope combined with the CCD camera and system for measuring the length was used to observe the fracture behavior. To compare the characteristics before heat treatment and after heat treatment, the specimen was exposed in the furnace at $800^{\circ}C$ for 48 hours and then the interfacial adhesion was evaluated. Finally, the interfacial adhesion energy quantitatively increases $1.78{\pm}0.07J/m^2$ to $4.9{\pm}0.87J/m^2$ between the cathode and Ag paste and also increase $2.9{\pm}0.47J/m^2$ to $5.12{\pm}1.01J/m^2$ between the anode and Ag paste through the high temperature. Therefore, it is expected that Ag paste as current collector was appropriate for improving the structural stability in the stacked SOFC system if the electrical conductivity was more increased.

• Journal of the Korean Graphic Arts Communication Society
• /
• v.29 no.2
• /
• pp.1-13
• /
• 2011

The recent spotlight on electronic touch-screen display, a rapid breakthrough in the information society is evolving. Touch panel input device such as a keyboard or mouse without the use of, the on-screen character or a specific location or object on the person's hand touches a particular feature to identify the location of a panel is to be handled. The touch screen on the touch panel is used in the Ag paste is used mostly for low-curable paste. The thermal-curing paste according to the drying process of thermal energy consumption and improve the working environment of organic solvents have problems. In this study, Ag paste used in the non-thermal curing friendly and cost-effective UV curable paste was prepared. Current commercially available thermal-curable binder, was used instead of the flow characteristics of UV-curable oligomers and monomers with functional groups to give a single conductive Ag paste with the addition of a pattern could be formed. Ag paste as a result, thermal-curing adhesive, hardness, resistance and excellent reproduction of fine patterns and was available with screen printing environmentally friendly could see its potential as a patterning technology.

• 한국신재생에너지학회:학술대회논문집
• /
• 2010.11a
• /
• pp.45.1-45.1
• /
• 2010

소성 온도에 따른 전면 전극과 태양전지 에미터와의 계면에서 전기적 특성을 평가하였다. Ag 전극 형성 시 특정 온도 이상의 열처리 과정을 통해 에미터와 전극 간 양질의 전기적 접촉을 형성하기 위해 소성 온도에 따라 Ag paste 내의 siver가 결정화되어 에미터 내부로 성장함을 확인 하고 Ag 전극의 전기적 특성을 평가하였다. 소성 온도 $650{\sim}750^{\circ}C$에서 전기적 특성이 가장 좋았으며 silver의 결정 생성에 의해 Ag paste와 에미터 간 전기적 접촉이 잘 형성됨을 확인 하였다.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.2
• /
• pp.85-90
• /
• 2014

Ag paste has been used in the front electrode of the Si-solar cell. It is composed by Ag powder, glass frit, binder, solvent and dispersant. The role of the binder and the solvent is to make a flow and a printing property. However, it was not enough to report the printing properties with the variation of binder in the controled viscosity. In this study, we selected 3 kinds of typical binder which were used as binder for the paste in the industry, such as Ethyl cellulose, Hydroxypropyl cellulose and Acrylic. Ag pastes using these were prepared, controled viscosity and printed on the SiNx coated Si wafer. In the 'A paste' used Acrylic binder, printed hight was highest and 'H paste' used Hydroxypropyl cellulose binder was lowest. Because 'H paste' was high viscosity due to the molecular weight, the solvent was added in the paste to control the viscosity. Therefore, the content of solid was lower in 'H paste'. The relative pattern width which is related to the spreading of paste was the best in the case of 'H paste' and 'EH paste' at $30^{\circ}C$. It is thought that the optimization of the relative pattern width is possible for a paste by the controling shear thinning phenomenon. In the case of 'A paste', though printing hight was best, the pattern width was dependant on the temperature.