• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.33 no.4
• /
• pp.440-446
• /
• 2009

This paper was designed to fabricate the miniature spur gear with pitch circle of 2.25mm using extrusion process of a mechanically alloyed Al-78wt%Zn powder. The mechanical alloying of the powder particles were performed for ball milled times of 4h, 8h, 16 and 32h by the planetary ball milling. The mechanical properties of these alloyed powders, which were compacted and sintered-cylindrical preforms, were estimated using compression test. The results showed that the alloyed powder with average particle size of $10{\mu}m$ milled for 32h has the highest compressive(fractured) strength(288MPa). Extrusions of the miniature spur gear using the alloyed powder were carried out at different extrusion temperatures. Extrusion temperature of $300^{\circ}C$ provided the spur gear with the highest relative density and Vickers hardness and without any surface defects.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.387-390
• /
• 2009

This study was designed to fabricate the micro-electro-mechanical systems (MEMS) parts such as micro spur gears using hot extrusion of gas atomized Al-78Zn powders. For this purpose, it is important to develop new methods to fabricate micro-dies and choose suitable extrusion conditions for a micro-forming. Micro-dies with Ni were fabricated by LIGA technology. LIGA technology was capable to produce micro-extrusion dies with close tolerances, thick bearing length and adequate surface quality. Superplastic Al-78Zn powders have the great advantage in achieving deformation under low stresses and exhibiting good micro formability with average strain rates ranging from $10^{-3}$ to $10^{-2}\;s^{-1}$ and constant temperatures ranging from 503 to 563K. Al-78Zn powders were compacted into a cylindrical shape (${\Phi}3{\times}h10$) under compressive force of 10kN and, subsequently, the compacted powders were extruded at 563k in a hot furnace. Micro-extrusion has succeeded in forming micro-gear shafts.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2009.06a
• /
• pp.785-786
• /
• 2009

• Transactions of Materials Processing
• /
• v.19 no.6
• /
• pp.352-356
• /
• 2010

This paper was designed to fabricate the micro-spur gear by the LIGA and hybrid powder extrusion process. It is important to manufacture a micro-die with a high aspect ratio and determine appropriate extrusion conditions for a microforming. Ni has been used to fabricate micro-dies. LIGA process was capable to produce micro-extrusion dies with close tolerance, longer bearing length and adequate surface quality. Superplastic Al-78Zn powders have the great advantage in achieving deformation under low stresses and exhibiting good micro-formability with average strain rate raging from $10^{-3}$ to $10^{-2} s^{-1}$ and constant temperature ranging from 503 to 563K. Al-78Zn powders were compacted into a cylindrical shape ($\Phi3\times$h10mm) under compressive force of 10kN and, subsequently, the compacted powders were extruded by the hybrid powder extrusion process controlling of the temperature holing time for a improvement on formability of Al-22Zn powder. Micro-extrusion has succeeded in forming micro-gear shafts.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.4
• /
• pp.172-177
• /
• 2002

The CuZnAl alloys have some advantages against other shape memory alloys, such as the widely variable transformation temperature, the low cost and easy fabrication. The alloys have been produced mostly by metallurgical methods. Thereby a tendency to large grain sizes is observed, which causes brittle properties of the materials. In order to avoid these deficiencies a special powder metallurgical process, SPS(spark plasma sintering), is applied in the present investigation. The starting materials were the pure (99.9 %) Cu, Zn and Al element powders with different particle size. The relatively fine grained and homogeneous Cu-24.78Zn-9.11Al (at.%) and Cu-13.22Zn-17.24Al (at.%) shape memory alloys were obtained using the powders with size of 75-150 $\mu$m. The average grain size is about 70 $\mu$m and the phases at room temperature are the austenitic and martensitic phase respectively.