• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.147-153
• /
• 2013

Recently the primary water stress corrosion cracking(PWSCC) has occurred in the dissimilar metal weld region between pressurizer nozzle and safe-end in nuclear power plants(NPPs). As material of the pressurizer nozzle, SA508 Gr. 3 low alloy steel was used. F316L stainless steel and Alloy 82/182 were used as safe-end and weld metal, respectively. Although mechanical properties are needed for evaluation of the structural integrity against flaw in the material, material specification and standard don't supply those properties. Therefore, the present study conducted tensile and fracture toughness tests on SA508 Gr.3 and F316L stainless steel at ambient temperature and operating temperature of NPPs and reported the tested results.

• Nuclear Engineering and Technology
• /
• v.55 no.5
• /
• pp.1924-1934
• /
• 2023

In this study, the probabilistic fatigue life model for Ni-base alloys was developed based on the Weibull distribution using statistical analysis of fatigue data reported in NUREG/CR-6909 and the new fatigue data of Alloy 52M/152 and 82/182. The developed Weibull model can consider right-censored data (i.e., non-failed data) and quantify the improved safety (or reliability) based on the level of failure probability. The overall margin in the current fatigue design limit model (ASME design curve + NUREG/CR-6909 F_en model) is similar to that of the Weibull model with a cumulative failure probability of approximately 2.5%. The margin in the current fatigue design limit model demonstrated inconsistencies for the Ni-base alloy weld data, whereas the Weibull model showed a consistent margin. Therefore, the Weibull model can systematically mitigate the excessive safety margin.