• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.18-19
• /
• 2017

In this study, hardening characteristics and microstructure of blast furnace slag-cement mortar replaced alpha-calcium sulfate hemihydrate were analyzed. As a result of replacing alpha-calcium sulfate hemihydrate with 0, 10, 20, 30%, it was confirmed that the initial and final setting times are faster than that of blast furnace slag-cement mortar. The compressive strength of the specimens containing alpha-calcium sulfate hemihydrate decreased in the range of 42 ~ 76% at age 28 days compared with blast furnace slag-cement mortar. In the case of replacing the alpha-calcium sulfate hemihydrate, the shrinkage did not occur more rapidly than the cement mortar, but the slope of the strain curve showed a linear behavior. The results of scanning electron microscopy images analysis showed that the formation of ettringite was increased at alpha-calcium sulfate hemihydrate replaced mortar.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.21 no.5
• /
• pp.117-124
• /
• 2017

In this study, to evaluate the setting time, compressive strength and drying shrinkage of ordinary Portland cement and Portland blast-furnace slag cement mortar with 0, 10, 20, 30 wt.% alpha-calcium sulfate hemihydrate. As a results, as the replacement ratio of alpha-calcium sulfate hemihydrate increased, the initial setting time of ordinary Portland cement and Portland blast-furnace slag cement mortar was faster. In addition, the compressive strength decreased with increasing replacement ratio of alpha-calcium sulfate hemihydrate in both ordinary Portland cement mortar and Portland blast-furnace slag cement mortar. The strength development of Portland blast-furnace slag cement mortar with alpha-calcium sulfate hemihydrate was effective than that of ordinary Portland cement mortar. On the other hand, in the case of the mortar with alpha-calcium sulfate hemihydrate, it was confirmed that shrinkage deformation was reduced at the early age by growth pressure of needle-shaped ettringite crystals produced by incorporation of alpha-calcium sulfate hemihydrate. However, the effect of inhibiting shrinkage deformation of mortar with alpha-calcium sulfate hemihydrate was not significant as the age passed. Therefore, it is considered that the alpha-calcium sulfate hemihydrate is useful as a construction material.

• Journal of the Korean Ceramic Society
• /
• v.24 no.4
• /
• pp.343-348
• /
• 1987

The effects of salts such as aluminum sulfate as inorganic salt(2-4%), and sodium salts of citrate, tartrate, succinate, potassium tartrate and gelatin as organic salts(0.1%) on the formation of ${\alpha}$-calcium sulfate hemihydrate from by-product gypsum of phosphoric acid process under hydrothermal condition at 123$^{\circ}C$ and 133$^{\circ}C$ were investigated. Aluminum sulfate solution exhibited the catalystic effected on the crystallization of ${\alpha}$-calcium sulfate hemihydrate of which was assumed in the prismatic form, and organic salts solution exhibited little effect on the catalystic action to the crystallization, than inorganic salts. In the acidic solution with sulfuric acid(pH=2), needle like crystal of calcium sulfate hemihydrate was obtained. Hydrothermal process with aluminum sulfate solution also showed certain amounts of impurity removal such as phosphorus penataoxide from calcium sulfate hemihydrate.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.1
• /
• pp.1-7
• /
• 2019

This study evaluated the mechanical properties of the alpha-calcium sulfate hemihydrate replaced concrete to reduce the cracking in a box culvert power transmission. After setting the replacement ratio of alpha-calcium sulfate hemihydrate at 0, 6, 9, 12, and 15%, the setting time, compressive strength, and drying shrinkage were measured and the microstructure and crystal structure were analyzed. As a result, it was confirmed that as the replacement ratio of alpha-calcium sulfate hemihydrate increased, the setting time decreased and the compressive strength declined. On the other hand, when the alpha-calcium sulfate hemihydrate was set with 15% of replacement ratio, about 60% reduction in the drying shrinkage was shown compared to that of ordinary Portland cement. Therefore, it is thought that when the concrete replacing the alpha-calcium sulfate hemihydrate is applied to a box culvert power transmission, the cracking reduction performance will be improved, and the improvement of compressive strength will be required.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.23 no.7
• /
• pp.72-79
• /
• 2019

Concrete is vulnerable to cracks due to volume changes caused by temperature changes, shrinkage during curing, external forces, or poor construction. In particular, concrete placed in electric power tunnel structures can generate cracks by a variety of factors. As a result, these tunnel structures require continuous maintenance. In this study, we investigated the mechanical properties of electric power tunnel concrete using alpha-calcium sulfate hemihydrate, which is an industrial byproduct that has excellent expansion performance. To compensate for the decrease in compressive strength when substituting alpha-calcium sulfate hemihydrate, based on previous research, we added 9% alpha-calcium sulfate hemihydrate and adjusted the amount of admixture while using the same amount of cement. We then evaluated the mechanical properties of the concrete. The results showed that the compressive strength of the concrete was higher than that of ordinary Portland cement (OPC), and the shrinkage of concrete was reduced by more than 30% compared to that of OPC. Therefore, adding 9% of alpha-calcium sulfate hemihydrate is expected to have a significant effect in reducing concrete cracks.

• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.300-306
• /
• 1988

The catalytic effect of salts on formation of ${\alpha}$-calcium sulfate hemihydrate under water vapor at atmospheric pressure was studied and the formation of q-calcium sulfate hemilydrate from by-product gypsum of phosphoric acid process was investigated. The order of catalytic effect of salts are as follow: Ammonium chloride>Sodium succinate>Calcium chloride>Sodium tartrate>Magnesium chloride The prismatic crystals was formed when ammonium chloride, calcium chloride and magnesium chloride was added, whereas the needle crystals was formed when sodium tartrate was added. Ammonium chlorideis most successful in catalytic effects in formation of ${\alpha}$-calcium sulfate hermihydrate for the by-product gypsum of phosphoric acid process.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.449-454
• /
• 1988

The effects of salts which was used as a catalysis in formation of $\alpha$-calciumusulfate hemihydrate from dicalcium sulfate hydrate were investigated on the hydration of $\alpha$-calciumsulfate hemihydrate. The hydration of $\alpha$-calciumsulfate hemihydrate was studied by the measurements of crystalline water, heat evolution. Also the hydrates were analyzed by XRD, DSC and SEM. The promotive effect each salts on the hydration was as follows: NaCl>NH4Cl>NaNO3>NH4NO3, and the hydration rate was accelerated with concentration of salts. The effect of Al2(SO4)3 and potassium sodium tartrate on the hydration was slmilar to water, whereas sodium succinate and gelatin retarded the hydration in comparision with water. These salts affected the hydration time but total heat evoution was similar.

• Applied Chemistry for Engineering
• /
• v.17 no.6
• /
• pp.619-624
• /
• 2006

This study was performed to investigate the formation process of calcium sulfate ${\alpha}$-hemihydrate from FGD gypsum produced at thermal power plant burning bituminous coal. The experimental results showed that calcium sulfate $\alpha$-hemihydrate with a large aspect ratio was produced in the temperature range of $120^{\circ}C$ and $140^{\circ}C$ in the absence of additives through dissolution-recrystallization mechanism. It was also observed that addition of Na-succinate as a catalyst changed crystal shape from acicular to prismatic, resulting in decreased water/powder ratio down to 33%. Optimum concentration of Na-succinate was 20mM. It was confirmed that the optimum moulding pressure and moisture content of moulded body from FGD gypsum were $30kg_f/cm^2$ and between 10% and 15% respectively, which prevent moulded body from collapsing and maximize the capillary effect by given pore volume while autoclaving.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.04a
• /
• pp.152-153
• /
• 2022

In this study, the mechanical properties of PHC Pile were investigated using α-calcium sulfate hemihydrate, an industrial by-product with excellent expansion performance. As a result, the compressive strength of PHC pile showed a tendency to be higher than that of general Portland cement (OPC).

• Journal of the Korea Institute of Building Construction
• /
• v.16 no.1
• /
• pp.59-65
• /
• 2016

This study examined the compressive strength development and pH values of alpha-calcium sulfate hemihydrate(${\alpha}-CH$)-based binders developed for vegetation concrete with neutral pH between 6~7. Considering cost down and strength enhancement of the prepared binders, the ${\alpha}-CH$ was partially replaced by ground granulated blast furnace slag(GGBS), fly ash(FA), or ordinary Portland cement(OPC) by 25% and 50%. The compressive strength of mortars using 100% ${\alpha}-CH$ was 50% lower than that of 100% OPC mortars. With the increase of the replacement level of GGBS or FA, the compressive strength of ${\alpha}-CH$-based mortars tended to decrease, whereas the pH values were maintained to be 6.5~7.5. The main hydration products of ${\alpha}-CH$-based binders with GGBS or FA were a gypsum($CaSO_4$), whereas portlandite($Ca(OH)_2$) was not observed in such binders. Meanwhile, the pH values of ${\alpha}-CH$-based binders with OPC exceeded 11.5 due to the formation of $Ca(OH)_2$ phase as a hydration product. From the thermogravimetric analysis, the amount of $Ca(OH)_2$ in ${\alpha}-CH$-based binders with OPC was evaluated to be approximately 10% of the cement content.