• Proceedings of the Korean Magnestics Society Conference
• /
• 1997.11a
• /
• pp.60-61
• /
• 1997

• Transactions of Materials Processing
• /
• v.5 no.4
• /
• pp.297-304
• /
• 1996

A process model is formulated considering the effect of crystallographic texture developed in forming process. The deformation induced plastic anisotropy can be predicted by capturing the evolution of texture during large deformation in the polycrystalline aggregate. The anisotropic stiffness matrix for the aggregate is derived and implemented in Eulerian finite element code using a Consistent Penalty method. As an application the evolution of texture in rolling drawing and extrusion processes are simulated. The numerical results show good agreements with report-ed experimental textures.

• Journal of the Korea Construction Safety Engineering Association
• /
• s.43
• /
• pp.98-106
• /
• 2007

In this paper, a ground disturbance effects, strength and consolidation characteristics of soft clay through using the large block samples($\theta$:300mm, H:400mm) and the piston samples, f hose which had been gathered in west coast and south coast. Especially, we have assessed the coefficient of horizontal consolidation when penetrating the mandrel considering the variance of ratio between diameter and height in drainage sample through the experiment of the oedometer test and Rowecell and also investigated the disturbance area in smear zone by interior model test, the strength originated by disturbance, the variance in characteristics of the consolidation. As the result, the large block sample has been investigated that ihe uniaxial compression test(qu) was shown bigger than the piston sample by about 11-19%. Under the size of anistropy in consolidation, the coefficient ratio of consolidation(ch/cv,) perfomed by standard consolidation test(SC) was shown bigger than that of (Cro/Cv) by the Rowecell test. And the coefficient ratio of consolidation(Cro/Cv) perfomed by piston sample was evaluated bigger than that Of (Cro/Cv) by the large block sample by about 0.9-1.9. The coefficient ratio of consolidation along with the variance in ratio of between diameter and height when penetrating the mandrel was shown big difference according to the characteristics of soil of the specimen. In addition, ds/dw of smear zone at the marine clay in west-south was ranged from 1.6 to 4.2. The width of variance in rat io[(qud)/(quud)] of strength n the area between disturbance and undisturbance was shown big as about 72-91% but the principle was judged with the similiar range when the decrease of the strength in smear zone become the zone under 25% in unditurbance area.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.119-124
• /
• 1999

Silicon nitride ceramics with highly oriented microstructure were prepared by tape casting a slurry containing 5 wt% of the silicon nitride whiskers. The whiskers were aligned in the casting direction and worked as seeds for the grain growth. The anisotropy was observed from the sintering shrinkage, Vickers indentation crack lengths, and XRD patterns. The cracks were much longer on the surface normal to the aligned grains than on the tape casting surface where the lateral cracks were also observed. The effect of sintering additives and the annealing treatment on the indentation crack length was examined. The sample with higher silica content had longer cracks than the one with lower silica content. The crack length anisotropy increased after annealing at 2123K.

• Journal of the Korean Society for Precision Engineering
• /
• v.10 no.1
• /
• pp.147-152
• /
• 1993

The lapping characteristics of single crystal diamond are studied by considering the crystallographic anisotropy. It is introduced for lapping method to identify crystallographic orientantion by the X-ray diffraction and to measure lapping force ratio, lapping temperature and lapping wear. Diamound bonded wheels are used for lapping under dry condition. On the lapping {110} and {100} planes, it shows remarkable crystallographic anistropy. The lapping force ratio, temperature and wear become gerater with sliding direction along the <100> than along <110>. The results also show that the wear of diamond is influenced by mechanical work(tangential lapping force * lapping distance) as well by lapping speed.

• Journal of the Korean Magnetics Society
• /
• v.3 no.3
• /
• pp.201-207
• /
• 1993

Starting ingot of $Pr_{15}Fe_{77}B_{8}$ were prepared by vacuum induction melting under argon atmosphere. The ingot were induction melted in a quartz crucible and then ejected as a molten alloy throuth a 0.6 mrn orifice onto a rotating cop¬per wheel. An anisotropic magnet was prepared from ribbon by hot deformation techniques. A fully dense precursor magnet first made by pressing ribbons at $680^{\circ}C$ under a pressure of $21.8\;kg/mm^{2}$. A substantially oriented magnets were obtained by die-upset under various conditions. As the compression ratio increases, the $B_{r}$ value increases pronouncedly though $_{i}H_{c}$ decreases. Also, XRD analyses show increased diffraction peak from (006). From these results, it can be known that the magnetic easy axis was formed along the compression axis. As the die-upset speed increases, $_{i}H_{c}$ increases though $B_{r}$ decreases. The $B_{r}$ increases up to $750^{\circ}C$ of die-upset temperature and above this temperature decreases. The value of $4{\pi}M_{s}$ of the $Pr_{15}Fe_{77}B_{8}$ alloy prepared is found to be 11.8 KG. When the alloy was compressed by 0.8 under the die-upset speed of 0.05 m/sec at $750^{\circ}C$, $B_{r}$ was 11.0 KG indicating that the alloy has excellent magnetic anistropy. However, this alloy has some limitation because of low $_{i}H_{c}$.