• Journal of the Korean Ceramic Society
• /
• v.52 no.5
• /
• pp.338-343
• /
• 2015

To prevent an interfacial reaction between the anode and the electrolyte layer during the conventional high-temperature co-firing process, an anode-supported type cell with a thin-film electrolyte was fabricated by low-temperature ceramic thick film coating process. Ni-GDC cermet composite was used as the anode material and YSZ was used as the electrolyte material. Open circuit voltage and maximum power density were found to strongly depend on the surface uniformity of the anode functional layer. By optimizing the microstructure of the anode functional layer, the open circuit voltage and maximum powder density of the cell increased to 1.11 V and $1.35W/cm^2$, respectively, at $750^{\circ}C$. When a GDC barrier layer was applied between the YSZ electrolyte and the LSCF cathode, the cell showed good stability, with almost no degradation up to 100 h. Anode-supported type SOFCs with high performance and good stability were fabricated using a coating process.

• Transactions of the Korean hydrogen and new energy society
• /
• v.20 no.6
• /
• pp.485-491
• /
• 2009

In present work, NiO/YSZ anode functional layer was prepared by nano NiO powder and 8YSZ powder. The nano NiO powders were made by Pulsed wire evaporation (PWE) method. Nano NiO- YSZ functional layer was sintered at the temperature of $900-1400^{\circ}C$. The prepared functional layer was characterized by scanning electron microscopy (SEM) and electrochemical impedance spectroscopy. The nano NiO- YSZ anode functional layer sintered at $1300^{\circ}C$ shows the lowest polarization resistance. Nano NiO- YSZ anode functional layer shows about two times smaller polarization resistance than the anode functional layer made by commercial NiO-YSZ powders. Based on these experimental results, it is concluded that the nano NiO-YSZ cermet is suitable as a anode functional layer operated at $800^{\circ}C$.

• New & Renewable Energy
• /
• v.5 no.1
• /
• pp.11-17
• /
• 2009

To improve the performance of the anode-supported Solid Oxide Fuel Cell (SOFC) which can be operated at an intermediate temperature, the functional layer (FL) is introduced on a anode substrate. And the scandia-stabilized zirconia (ScSZ) and samaria-doped ceria (SDC) which have higher ionic conductivity and better chemical stability than yttria-stabilized zirconia (YSZ) are used as material for the anode FL with the Ni, The fabrication process of anode-supported single cell with the anode FL was established and the power density of those was evaluated. As a result, the sample with anode FL (Ni-YSZ) has higher power density than normal cell. The single cell which was composed of the FL (Ni-YSZ) and electrolyte (YSZ) showed about $550mW/cm^2$ of the maximum power density at $650^{\circ}C$ and $1430mW/cm^2$ at $750^{\circ}C$ respectively, In case of the single cell using the ScSZ and SDC as anode FL, the performance of samples decreased rapidly and those showed unstable voltage during long-term test. In case of using methane as a fuel, the cell performance with each FL decreased comparing with $H_2$ fuel. In the region of a high current density, there are large concentration polarizations.

• Korean Journal of Materials Research
• /
• v.22 no.11
• /
• pp.626-630
• /
• 2012

The properties of SOFC unit cells manufactured using the decalcomania method were investigated. SOFC unit cell manufacturing using the decalcomania method is a very simple process. In order to minimize the ohmic loss of flattened tube type anode supports of solid oxide fuel cells(SOFC), the cells were fabricated by producing an anode function layer, YSZ electrolyte, LSM electrode, etc., on the supports and laminating them. The influence of these materials on the power output characteristics was studied when laminating the components and laminating the anode function layer between the anode and the electrolyte to improve the output characteristics. Regarding the performance of the SOFC unit cell, the output was 246 $mW/cm^2$ at a temperature of $800^{\circ}C$ in the case of not laminating the anode function layer; however, this value was improved by a factor of two to 574 $mW/cm^2$ due to the decrease of the ohmic resistance and polarization resistance of the cell in the case of laminating the anode function layer. The outputs appeared to be as high as 574 and 246 $mW/cm^2$ at a temperature of $800^{\circ}C$ in the case of using decalcomania paper when laminating the electrolyte layer using the in dip-coating method; however, the reason for this is that interfacial adhesion was improved due to the dense structure, which leads to a thin thickness of the electrolyte layer.

• Journal of Electrochemical Science and Technology
• /
• v.11 no.4
• /
• pp.336-345
• /
• 2020

Nickel-doped lanthanum cobalt oxide (LaCo_1-xNi_xO_3-δ, LCN) was investigated as an alternative anode material for solid oxide fuel cells. To improve its catalytic activity for steam methane reforming (SMR) reaction, Ni²⁺ was substituted into Co³⁺ lattice in LaCoO₃. LCN anode, synthesized using the Pechini method, reacts with yttria-stabilized zirconia (YSZ) electrolyte at high temperatures to form an electrochemically inactive phase such as La₂Zr₂O₇. To minimize the interlayer by-products, the LCN was coated via a double-tape casting method on the Ni/YSZ anode as a catalytic functional layer. By increasing the Ni doping amount, oxygen vacancies in the LCN increased and the cell performance improved. CH₄ fuel decomposed to H₂ and CO via SMR reaction in the LCN functional layer. Hence, the LCN-coated Ni/YSZ anode exhibited better cell performance than the Ni/YSZ anode under H₂ and CH₄ fuels. LCN with 12 mol% of Ni (LCN12)-modified Ni/YSZ anode showed excellent long-term stability under H₂ and CH₄ conditions.

• ETRI Journal
• /
• v.26 no.4
• /
• pp.285-291
• /
• 2004

We prepared a novel multi-functional dual-layer polymer electrolyte by impregnating the interconnected pores with an ethylene carbonate (EC)/dimethyl carbonate (DMC)/lithium hexafluorophosphate $(LiPF_6)$ solution. The first layer, based on a microporous polyethylene, is incompatible with a liquid electrolyte, and the second layer, based on poly (vinylidenefluoride-co-hexafluoropropylene), is submicroporous and compatible with an electrolyte solution. The maximum ionic conductivity is $7{\times}10^{-3}S/cm$ at ambient temperature. A unit cell using the optimum polymer electrolyte showed a reversible capacity of 198 mAh/g at the 500th cycle, which was about 87% of the initial value.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.520-524
• /
• 2011

The properties of manufactured SOFC unit cell using decalcomania method were investigated. The decalcomania method that used in ceramics, dish, vessel and etc. was the very simple process. The SOFC unit cell manufacturer using decalcomania method is very simple process. Especially, the decalcomania method was the most suitable manufacturing method for the segmented type SOFC. The cathode, prevent diffusion layer (PDL), anode functional layer (AFL) and electrolyte were manufactured using decalcomania method on porous anode support. The sintered electrolyte at 1450$^{\circ}C$ for 2 h using decalcomania method was very dense, and the thickness was about 10 ${\mu}m$. The cathode, the PDL and the AFL were manufactured using decalcomania method and was sintered at 1250$^{\circ}C$ for 2 h, and the sintered electrodes were the porous. As a result, with humidified hydrogen used as fuel, the cell with an 15 ${\mu}m$-thick AFL exhibited maximum power densities of 0.246, 0.364, 0.504W/$cm^2$ at 700, 750, 800$^{\circ}C$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.52 no.5
• /
• pp.315-319
• /
• 2015

Yttria-stabilized zirconia (YSZ)-based micro tubular SOFC single cells were fabricated by electrophoretic deposition (EPD) process. Stable slurries for the EPD process were prepared by adding phosphate ester (PE) as a dispersant in order to control the pH, conductivity, and zeta-potential. NiO-YSZ anode support, NiO-YSZ anode functional layer (AFL), and YSZ electrolyte were consecutively deposited on a graphite rod using the EPD process; materials were then co-sintered at $1400^{\circ}C$ for 4 h. The thickness of the deposited layer increased with increasing of the applied voltage and the deposition time. A YSZ-based micro tubular single cell fabricated by the EPD process exhibited a maximum power density of $0.3W/cm^2$ at $750^{\circ}C$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.90-90
• /
• 2012

The electron/hole injections in organic electronic devices have long been an issue due to the large energy level mismatches between electrode and organic layer. To utilize the organic materials in electronic devices, functional thin layers have been used, which reduce the electron/hole injection barrier from electrode to organic material. Typically, inorganic compounds and organic molecules are used as an electron and hole injection layer, respectively. Recently, CsN3 and 1,4,5,8,- naphthalene-tetracarboxylic-dianhydride (NTCDA) are reported as a potential electron and hole injection layers. CsN3 shows unique properties that it breaks into Cs and N and thus Cs can dope organic layer into n-type. On the other side, hole injection anode, NTCDA forms gap states with anode material. In this presentation, we show the electronic structure changes upon the insertion of CsN3 and NTCDA at proper interfaces to reduce the charge injection barriers. These barrier reductions are correlated with device characteristics.

• Journal of the Korean Ceramic Society
• /
• v.52 no.5
• /
• pp.320-324
• /
• 2015

Optimization of the fabrication process of NiO-yttrium doped barium zirconate (BZY) composite anode substrates using tape-casting for high performance thin-film protonic ceramic fuel cells (PCFCs) is investigated. The anode substrate is composed of a tens of microns-thick anode functional layer laminated over a porous anode substrate. The macro-pore structure of the anode support is induced by micron-scale polymethyl methacrylate (PMMA) pore formers. Thermal gravity analysis (TGA) and a dilatometer are used to determine the polymeric additive burn-out and sintering temperatures. Crystallinity and microstructure of the tape-cast NiO-BZY anode are analyzed after the sintering.