• International Journal of Highway Engineering
• /
• v.17 no.5
• /
• pp.25-31
• /
• 2015

PURPOSES: The objective of this study is to analyze the relationship between the FWD back-calculated modulus and dynamic modulus of asphalt layers for existing asphalt pavements. METHODS: To evaluate the dynamic modulus of the asphalt mixture in the existing and new asphalt layers, the uniaxial direct tension test was conducted on small asphalt specimens obtained from the existing asphalt-covered pavements. A dynamic modulus master curve was estimated by using the uniaxial direct tension test for each asphalt layer. The falling weight deflectometer (FWD) testing was conducted on the test sections, and the modulus values of pavement layers were back-calculated using the genetic algorithm and the finite element method based back-calculation program. The relationship between measured and back-calculated asphalt layer moduli was examined in this study. The normalized dynamic modulus was adopted to predict the stiffness characteristics of asphalt layers more accurately. RESULTS: From this study, we can conclude that there is no close relationship between dynamic modulus of first layer and back-calculated asphalt modulus. The dynamic moduli of second and third asphalt layers have some relation with asphalt stiffness. Test results also showed that the normalized dynamic modulus of the asphalt mixture is closely related to the FWD back-calculated modulus with 0.73 of R square value. CONCLUSIONS: The back-calculated modulus of asphalt layer can be used as an indicator of the stiffness characteristics of asphalt layers in the asphalt-covered pavements.

• International Journal of Highway Engineering
• /
• v.18 no.1
• /
• pp.57-62
• /
• 2016

PURPOSES : Reflection cracking has been one of the major causes of distress when asphalt pavement is laid on top of concrete pavement. This study evaluated the reflection cracking resistance of asphalt mixtures reinforced with asphalt embedded glass fiber and carbon fiber using a Texas Transportation Institute (TTI) overlay tester. METHODS : Different asphalt mixtures such as polymer-modified mastic asphalt (PSMA) and a dense graded asphalt mixture were reinforced with asphalt-embedded carbon fiber and glass fiber. For comparison purposes, two PSMA asphalt mixtures and one dense graded asphalt mixture were evaluated without fiber reinforcement. Two different overlay test modes, the repeated overlay test (R-OT) and monotonic overlay test (M-OT), were used to evaluate the reflection cracking resistance of asphalt mixtures at $0^{\circ}C$. In the R-OT test, the number of repeated load when the specimen failed was obtained. In the M-OT test, the tensile strength at the peak load and tensile strain were obtained. RESULTS : As expected, the fiber-reinforced asphalt mixture showed a higher reflection cracking resistance than the conventional nonreinforced asphalt mixtures based on the R-OT test and M-OT test. The dense graded asphalt mixture showed the least reflection cracking resistance and less resistance than the PSMA. CONCLUSIONS : The TTI overlay tester could be used to differentiate the reflection cracking resistance values of asphalt mixtures. Based on the R-OT and M-OT results, the carbon-fiber-reinforced asphalt mixture showed the highest reflection cracking resistance among the nonreinforced asphalt mixtures and glass-fiber-reinforced asphalt mixture.

• International Journal of Highway Engineering
• /
• v.15 no.4
• /
• pp.43-51
• /
• 2013

PURPOSES : The main purposes of this study are to examine the influences of polyethylene wax-based WMA additive on the optimum asphalt content of warm-recycled asphalt mixture based on the Marshall mix design and to evaluate performance of warm-recycled asphalt mixture containing 30% RAP with polyethylene wax-based WMA additive. METHODS: Physical and rheological properties of the residual asphalt were evaluated in terms of penetration, softening point, ductility and performance grade (PG) in order to examine the effects of polyethylene wax-based WMA additive on the residual asphalt. Also, To evaluate performance characteristics of the warm-recycled asphalt mixtures using polyethylene wax-based WMA additive along with a control hot-recycled asphalt mixture, indirect tensile strength test, modified Lottman test, dynamic immersion test, wheel tracking test and dynamic modulus test were conduced in the laboratory. RESULTS : Based on the limited laboratory test results, polyethylene wax-based WMA additive is effective to decrease mixing and compacting temperatures without compromising the volumetric characteristics of warm-recycled asphalt mixtures compared to hot-recycled asphalt mixture. Also, it doesn't affect the optimum asphalt content on recycled-asphalt mixture. All performance test results show that the performance of warm-recycled asphalt mixture using polyethylene wax-based WMA additive is similar to that of a control hot-recycled asphalt mixture. CONCLUSIONS: Overall, the performance of warm-recycled asphalt mixture using polyethylene wax-based WMA additive is comparable to hot-recycled asphalt mixture.

• Elastomers and Composites
• /
• v.50 no.3
• /
• pp.167-174
• /
• 2015

Anionic epoxy compound was synthesized and added to asphalt aiming to prepare self-healing asphalt. Epoxy-modified asphalt showed excellent modification effect and healing effect as well. The results revealed that with 5% addition of polymer the tensile strength, impact strength and complex shear modulus of the polymer-modified asphalt increased by 65%. 64% and 35%, respectively. It seems that high interaction occurs between polymer and asphalt matrix. Self-healing efficiency of the polymer-modified asphalt based on tensile strength showed 100%, comparing to 79% of straight asphalt. In impact experiment the polymer-modified asphalt showed 99% of healing efficiency, comparing to 77% of straight asphalt. In rheological experiment the polymer-modified asphalt showed 103% of healing efficiency, comparing to 72% of straight asphalt. It appears that the ionic bonding existing in epoxy polymers contributed to high values of self-healing efficiency. The polymer which has high intermolecular force fills the crack of the asphalt, pulling the opponent side each other, and so the original properties were restored.

• International Journal of Highway Engineering
• /
• v.17 no.6
• /
• pp.1-9
• /
• 2015

PURPOSES : The objective of this study is to propose a quality control and quality assurance method for use during asphalt pavement construction using non-destructive methods, such as ground penetrating radar (GPR) and an infrared (IR) camera. METHODS : A 1.0 GHz air-coupled GPR system was used to measure the thickness and in situ density of asphalt concrete overlay during the placement and compaction of the asphalt layer in two test construction sections. The in situ density of the asphalt layer was estimated based on the dielectric constant of the asphalt concrete, which was measured as the ratio of the amplitude of the surface reflection of the asphalt mat to that of a metal plate. In addition, an IR camera was used to monitor the surface temperature of the asphalt mat to ensure its uniformity, for both conventional asphalt concrete and fiber-reinforced asphalt (FRA) concrete. RESULTS : From the GPR test, the measured in situ air void of the asphalt concrete overlay gradually decreased from 12.6% at placement to 8.1% after five roller passes for conventional asphalt concrete, and from 10.7% to 5.9% for the FRA concrete. The thickness of the asphalt concrete overlay was reduced from 7.0 cm to 6.0 cm for the conventional material, and from 9.2 cm to 6.4 cm for the FRA concrete. From the IR camera measurements, the temperature differences in the asphalt mat ranged from $10^{\circ}C$ to $30^{\circ}C$ in the two test sections. CONCLUSIONS : During asphalt concrete construction, GPR and IR tests can be applicable for monitoring the changes in in situ density, thickness, and temperature differences of the overlay, which are the most important factors for quality control. For easier and more reliable quality control of asphalt overlay construction, it is better to use the thickness measurement from the GPR.

• Journal of Environmental Science International
• /
• v.10 no.4
• /
• pp.311-314
• /
• 2001

The asphalt mixture with CRM(Crumb Rubber Modifier) is known to show a better performance in resisting thermal cracking, fatigue cracking and rutting compared with the conventional mixture. The laboratory tests on the physical characteristics of indirect tensile strength, density, flow and Marshall value of the CRM asphalt were conducted. The test results show that CRM asphalt has better physical characteristics than that of conventional asphalts. And the analysis on the noise reduction effect, penetration capacity from the field test on the national road in Haksan of Chungbuk, and recycling of tire waste were conducted. From this study, the results show that 1% CRM asphalt has higher the noise reduction effect and penetration capacity that those of conventional asphalts. And, optimal contents of crumb rubber modifier in the asphalt binder is one percent. In this case, crumb rubber modifier were used 10 kg to make the asphalt binder of one cubic meter. So it was named as Eco-asphalt.

• Land and Housing Review
• /
• v.10 no.4
• /
• pp.51-59
• /
• 2019

The government is encouraging the notice of obligatory reclaimed asphalt as a result of the economic and social positioning of green growth to reduce the amount of waste resources and to solve natural resource problems by recycling continuously generated waste resources. However, it is necessary to develop application guideline for each application to apply reclaimed asphalt to the site because quality control of the reclaimed asphalt is difficult and the specifications are ambiguous as well. Therefore, in this study, the mix design, quality test, performance test, and finite element analysis about reclaimed Asphalt Pavement were conducted to develop application guideline for reclaimed hot asphalt. The mix design was carried out for the comparative general hot mix asphalt mixture, the reclaimed hot mix asphalt mixture using the additive, and the reclaimed hot mix asphalt mixture without the additive. Indirect tensile strength and tensile strength ratio tests were used to characterize the reclaimed hot mix asphalt mixture. Using the results of dynamic modulus test and FWD test for KPRP analysis and finite element analysis, the performance life was evaluated for general pavement and pavement using recycled aggregate. Finally, the life cycle cost analysis was used to compare and analyze the economics of reclaimed asphalt concrete pavement.

• International Journal of Highway Engineering
• /
• v.11 no.4
• /
• pp.153-160
• /
• 2009

Falling Weight Deflectometer (FWD) tests were performed to evaluate the structural capacity of glass fiber reinforced (GFR), polymer modified (PM), and unmodified asphalt pavement in Korea-LTPP (Long Term Pavement Performance) section. FWD tests showed that the tensile strains of GFR and PM asphalt pavements at the bottom of asphalt layer were 29% and 21% less than that of unmodified asphalt pavement. The structural capacity was then used as a performance criterion for calculating the cost effect of GFR and PM asphalt pavements. From the results, 5cm of asphalt layer thickness was reduced by applying GFR asphalt, and 3cm by applying PM asphalt. However, construction cost of PM and GFR asphalt pavement were increased due to the higher GFR and PM asphalt price. Life cycle cost analysis showed that the initial construction cost of GFR and PM asphalt pavement were higher but the management and user cost were less than those of unmodified asphalt pavement.

• Proceedings of the Korean Geotechical Society Conference
• /
• 2008.03a
• /
• pp.932-937
• /
• 2008

The asphalt waste has been collected more than ten thousands' ton from repairing works on the road and excavation repair works, most of them are disposed on land of reclamation. Only a few percentage of wasted asphalt recycled to new one. Therefore, In this study, usage of wasted asphalt and has been done engineered characteristic test for recycling materials of sub-grade and structure. To know the characteristic of asphalt waste, tamping test, bearing-ratio test, permeability test and direct shear test was done using asphalt-sand mixture. The test results shows that, mixed asphalt materials with sand can be used for materials of subgrade-soil and structure.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.05a
• /
• pp.216-217
• /
• 2018

The three kinds of tests are used to further study the effect of the amount of mineral powder in this mixture design. Firstly, comparing the relationship of the content of mineral powder and asphalt bitumen membrane thickness at different asphalt content, through film thickness to determine the range of gradation and asphalt content in laboratory tests, Grade A and Grade D, asphalt content 2.6%, 3.4% and 3.8% are set for the benchmark, then fatigue properties of the test are carried out in the established range, the result show that asphalt film thickness decreases with the addition of mineral powder. The result also show that fatigue properties of asphalt rubber mixture will reduced, when mineral powder added in, especially when the asphalt content is high.