• Transactions of the Korean Society of Mechanical Engineers
• /
• v.18 no.5
• /
• pp.1144-1149
• /
• 1994

Damage caused in CFRP laminates by low energy impact of steel ball are investigated ultrasonically. Two types of laminated specimens having different stacking sequence are used as a target material. The effects of pre-bending on the behaviors of impact damage are specifically discussed. The initiation and progagation behaviors of delamination were largely dependent upon the bending rigidity of each specimen. Specimen C having higher bending rigidity produced larger delamination damage than the Specimen D having relatively low bending rigidity, however it was little for the Specimen C. Application of pre-bending increased the apparent bending rigidity of target during impacting, it produced delamination at lower impact energy level compared to the case of no preload.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.577-577
• /
• 1989

In this paper, a detail evaluation of ultimate strength of offshore unstiffened tubular members with bending and local denting damage which are subjected to combined axial force and bending moment and to component load is presented through theoretical and experimental approaches. Based upon the results obtained here, the damage effect on the ultimate strength of tubular member under combined loads and component load is investigated.

• Journal of Ocean Engineering and Technology
• /
• v.3 no.2
• /
• pp.77-86
• /
• 1989

In this paper, a detail evaluation of ultimate strength of offshore unstiffened tubular members with bending and local denting damage which are subjected to combined axial force and bending moment and to component load is presented through theoretical and experimental approaches. Based upon the results obtained here, the damage effect on the ultimate strength of tubular member under combined loads and component load is investigated.

• Journal of the Korean Society of Safety
• /
• v.30 no.3
• /
• pp.7-12
• /
• 2015

CFRP composites are used as primary structural members in various industrial fields because their specific strength and specific stiffness are excellent in comparison to conventional metals. Their usage is expanding to high added-value industrial fields because they are more than 50% lighter than metals, and have excellent heat resistance and wear resistance. However, when CFRP composites suffer impact damage, destruction of fiber and interface delamination occur. This causes an unexpected deterioration of strength, and for this reason it is very difficult to ensure the reliability of the excellent mechanical properties. Therefore, for the destruction mechanism in bending with impact damage, this study investigated the reinforcement data regarding various external loads by identifying the consequential strength deterioration. Specimens were damaged by impact with a steel ball propelled by air pressure. Decrease in bending strength caused by the tension and compression of the impact side, and depending on the lamination direction of fiber and interface inside the specimen. From the bending test it was found that the bending strength reduced when the impact energy increased. Especially in the case of compression on the impact side, as tensile stress occurred at the damage starting point, causing rapid failure and a substantially reduced failure strength.

• Journal of the Korean Society for Precision Engineering
• /
• v.10 no.4
• /
• pp.152-162
• /
• 1993

The purpose of this study is to investigate problems of residual bending strength and the impact damage experimentally when CFRP composite laminates are subjected to Foreign object damage. The specimens composed of four types of CR/EPOXY and a CF/PEEK composite laminates which involved difference of fiber stracking orientation and matrics. The result were summariged as follows : 1) It is found that both orthotropic and guasi-isotropic composite laminates are increasimg lineally between impact energy and damage delamination area. 2) Delamination devel- opment energy(mm$^{2}$J) OF cf/epoxy composite aminates is less than that of CF/PEEK. 3) When impact energy is applied to specimens within 3J, the residual strength of orthotropic is greater than guasi-isotropic composite laminates. On the other hand, it is predicted that residual bending strength of orthotropic composite laminates is less than that of quasi-isotropic when impact energy is more thaen 3J. 4) It is found in CF/PEEK that for the impact side compression, residual of bending strength versus impact energy is almost constant, while in case of impact side tension, residual bending strength is decreased rapidly near 1.2J. of impact energy due to the effect of delamination buckling.

• Journal of Aerospace System Engineering
• /
• v.4 no.1
• /
• pp.23-26
• /
• 2010

In this study, it was performed damage assesment of small scale composite aircraft developing. This aircraft adopted the sandwich structure to skin of wing. This study aims to investigate the residual strength of sandwich composites with Nomex honeycomb core and carbon fiber face sheets after the open hole damage by the experimental investigation. The 4-point bending tests were used to find the bending strength, and the open hole was applied to introduce the simulated damage on the specimen. The bending strength test results after open hole was compared with the results of no damaged specimen test. The FEM analysis is assessed via an experimental 4-point bending test.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.31 no.8
• /
• pp.870-879
• /
• 2007

In this study, various damage modes in bending unimorph piezoelectric composite actuators with a thin sandwiched PZT plate during bending fracture tests have been evaluated by monitoring acoustic emission (AE) signals in terms of waveform and peak frequency as well as AE parameters. Three kinds of actuator specimens consisting of woven fabric fiber skin layers and a PZT ceramic core layer are loaded with a roller and an AE activity from the specimen is monitored during the entire loading using an AE transducer mounted on the specimen. AE characteristics from a monolithic PZT ceramic with a thickness of $250{\mu}m$ are examined first in order to distinguish different AE signals from various possible damage modes in piezoelectric composite actuators. Post-failure observations and stress analyses in the respective layers of the specimens are conducted to identify particular features in the acoustic emission signal that correspond to specific types of damage modes. As a result, the signal classification based on waveform and peak frequency analyses successfully describes the failure process of the bending piezoelectric composite actuator exhibiting diverse failure mechanisms. Furthermore, it is elucidated that when the PZT ceramic embedded actuators are loaded mechanical bending loads, the failure process of actuator specimens with different lay-up configurations is almost same irrespective of their lay-up configurations.

• Journal of the Korean Society of Safety
• /
• v.18 no.2
• /
• pp.34-39
• /
• 2003

In this paper, when CF/PEEK laminates for high efficiency space structure are subjected to FOD(Foreign Object Damage), the effects of temperature change on the impact damages(interlaminar separation and transverse crack) of CF/PEEK laminates and the relationship between residual lift and impact damages are experimentally investigated. Composite laminates used in this experiment are CF/PEEK orthotropic laminated plates, which have two-interlaces [$0^{\circ}_4/90^{\circ}_8/0^{\circ}_4$]. A steel ball launched by the air gun collides against CF/PEEK laminates to generate impact damages. And then CF/PEEK specimens with impact damages are observed by a scanning acoustic microscope under room and high temperatures. In this experimental results, various relations are experimentally observed including the delamination area vs. temperature change, the bending strength vs. impact energy and the residual bending strength vs. impact damage of CF/PEEK laminates.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.11
• /
• pp.2752-2761
• /
• 1993

The purpose of this study is to confirm the decreasing problems of residual bending strength, and the fracture machanism experimentally when CFRP composite laminates are subjected to Foreign Object Damage. Composite laminates used for this experiment are CFRP orthotropy laminated plates, which have two-interfaces [O/sub 6//sup o//90/sub 6//sup o/]sub sym/ and four-interfaces [O/sub 3//sup o//90/sub 6//sup o//O/sub 3//sup o]/sub sym/. When the specimen is subjected to transverse impact by a steel ball, the delamination area generated by impact damage is observed by using SAM(Scanning Acoustic Microscope). also, Thefracture surfaces obtained by three-point bending test were observed by using SEM (Scanning Electron Microscope). Then, fracture mechanism was investigated based on the observed delamination area and fracture surface. The results were summarized as follows; (1) It is found that for the specimen with more interface, the critical delamination energy is increased while delamination-development energy is decreased. (2) Residual bending strength of specimen A is greater than that of Specimen B within the impact range of impact energy 1. 65J (impacted-side compression) and 1. 45J (impacted-side tension). On the other hand, when the impact energy is beyond the above ranges, residual bending strength of specimen A is smaller than that of specimen B. (3) In specimen A and B, residual strength of CFRP plates subjected to impact damage is lower in the impacted-side compression than in the impacted-side tension. (4) In the case of impacted-side compression, fracture is propagated from the transverse crack generat-ed near impact point. On the other hand, fracture is developed toward the impact point from the edge of interface-B delamination in the case of impacted-side tension.

• Structural Engineering and Mechanics
• /
• v.32 no.2
• /
• pp.301-320
• /
• 2009

Damage assessment for buried structures against an internal blast is conducted by considering the soil-structure interaction. The structural element under analysis is assumed to be rigid-plastic and simply-supported at both ends. Shear failure, bending failure and combined failure modes are included based on five possible transverse velocity profiles. The maximum deflections with respect to shear and bending failure are derived respectively by employing proper failure criteria of the structural element. Pressure-Impulse diagrams to assess damage of the buried structures are subsequently developed. Comparisons have been done to evaluate the influences of the soil-structure interaction and the shear-to-bending strength ratio of the structural element. A case study for a buried reinforced concrete structure has been conducted to show the applicability of the proposed damage assessment method.